• Journal of the Korea Concrete Institute
• /
• v.14 no.1
• /
• pp.58-66
• /
• 2002

The objective of this study is to examine the fracture characteristics of concrete at early ages such as critical stress intensity factor, critical crack-tip opening displacement, fracture energy, and bilinear softening curve based on the concepts of the effective-elastic crack model and the cohesive crack model. A wedge splitting test for Mode I was performed on cubic wedge specimens with a notch at the edge. By taking various strengths and ages, load-crack mouth opening displacement curves were obtained, and the results were analyzed by linear elastic fracture mechanics and the finite element method. The results from the test and analysis showed that critical stress intensity factor and fracture energy increased, and critical crack-tip opening displacement decreased with concrete ages from 1 day to 28 days. By numerical analysis four parameters of bilinear softening curve from 1 day to 28 days were obtained. The obtained fracture parameters and bilinear softening curves at early ages may be used as a fracture criterion and an input data for finite element analysis of concrete at early ages.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.3
• /
• pp.179-187
• /
• 1997

콘크리트는 여러 구성 성분들이 불규칙적인 배열을 이루어 형성된 복합재료이지만, 과거에는 이 재료를 하나의 단종재료로 간주하여 해석하였기 때문에, LEFM에서 사용되는 파괴인성계수만으로는 콘크리트의 파괴역학적 접근이 어렵다는 것 이외에는 파괴인성계수들의 크기의존성에 대한 이유라든가, 실험을 통해서 관측된 구조물 두께 방향으로의 서로 다른 깊이의 균열 진행 현상에 대해서는 설명하기가 어려웠다. 따라서 본 연구는 콘크리트를 하나의 복합재료로써 각각의 구성요소들이 차지하고 있는 체적비 및 배열상의 효과를 고려하여 복합재료의 파괴거동을 해석하고, 구성재료의 수와 파괴인성계수와의 상관관계를 분석하였다. 각각의 구성요소들을 연립변형모드( SD mode)로 배열시킨 조건에서 복합재료역학개념에 입각하여 해석한 결과, 일반적으로 실험이나 비선형파괴역학 해석과 같이 하중-변위곡선 상단부에서 비선형 거동이 관측되었다. 또한 임계응력확대계수( $K_IC$)나 파괴에너지($G_r$)는 구성원의 수나 보의 크기에 대해서 거의 무관한 값을 나타내지만, 임계군열선단개구변위 ($CTOD_c$)는 크기에 영향을 받음을 보여 주었다. 균열의 진행속도는 균열이 진행될수록 감소하며, 파괴인성이 작은 구성원에서부터 균열이 발생되어 결과적으로 보의 두께 방향으로 서로 다른 크기의 균열길이가 생성됨이 관측되었다.