• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.6
• /
• pp.655-662
• /
• 2014

This study conducted tensile tests on an Alloy 690TT tube at room temperature (RT) and at $343^{\circ}C$ using tube- and ring-type specimens to investigate the stress-strain behavior and tensile properties of a steam generator (SG) tube in the axial and circumferential directions at RT and at the design temperature of a nuclear power plant (NPP). The results of the axial tensile test showed that yield point phenomena appeared at both RT and $343^{\circ}C$, and serrated flow in the stress-strain curve appeared at $343^{\circ}C$. Yield and tensile strengths for both directions were clearly lower at $343^{\circ}C$ compared to RT; however, the elongations were approximately the same at both test temperatures. Regardless of the test temperature, the strengths in the circumferential direction were lower by approximately 5~10 % than those in the axial direction. In addition, the test data revealed that the reduction in the yield and tensile strengths of the Alloy 690TT SG tube with the test temperature was more significant than that estimated by the temperature correction factor of ASME Sec.II.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.19-19
• /
• 2010

Mo 변화에 따른 Cr-Mo 강의 미세조직 및 물성병화를 알아보기 위해 새로 디자인된 용접봉을 사용하여 Flux cored arc welding(FCAW) 공정으로 용접하였다. 또한 고온에서의 용접부 물성을 알아보기 위하여 각각의 시편을 $400^{\circ}C$, $500^{\circ}C$, $600^{\circ}C$, $700^{\circ}C$에서 24시간 동안 열처리 하였다. 용접부의 미세조직은 미세한 베이나이트 및 침상 페라이트로 구성되었으며 Mo의 함량이 높아질수록 베이나이트 조직이 증가하여 경도 및 강도가 증가하였다. 높은 항복강도와 인장강도를 가지며 연신율이 매우 낮음을 관찰하였다. 열처리후의 미세조직은 $400^{\circ}C$, $500^{\circ}C$는 템퍼드 베이나이트 조직이 나왔으나 $600^{\circ}C$에서 베이나이트 조직이 성장하였다. $700^{\circ}C$ 로 갈수록 베이나이트가 감소하고 페라이트로 미세조직이 변태 하였으며 탄화물의 석출 및 성장이 관찰되었다. 이로 인하여 경도값이 $400^{\circ}C$, $;500^{\circ}C$ 에서 증가하였고 $600^{\circ}C$는 소폭 감소하였으며 $700^{\circ}C$의 경우 완전 페라이트 조직의 형성으로 경도가 크게 감소하고 Mo 함량에 따른 경도 차이 또한 보이지 않았다.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1994.06a
• /
• pp.79-86
• /
• 1994

스템핑용 냉연강판의 기계적 성질은 온도에 따라 변하므로 금형재의 열적 특성은 성형의 성공여부에 영향을 미칠 수 있으며 재질선정에 있어 중요한 인자의 하나이다. 금형재질이 성형에 미치는 영향을 조사하기 위하여 차체의 패널용으로 사용되는 강판에 대하여 상온 및 고온에서의 인장시험을 하였으며 구상흑연주철과 회주철을 중심으로 열특성을 조사하였다. 연신율과 인장 강도의 온도 의존성에 대한 검토와 함께 금형재료에 따른 열전달 특성을 분석하여 열특성 측면에서는 회주철이 구상흑연 주철보다 더 적합 하며 열전도율이나 비열 등의 열특성치도 금형재 선정에 중요한 인자중 하나라는 결론을 얻었다.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2004.11a
• /
• pp.228-233
• /
• 2004

The characteristics of the probability distribution for mechanical properties, e.g. tensile strength, reduction of area ana elongation, for STS304 stainless steel in elevated temperature were investigated from tensile test performed by constant cross head speea controls with 1mm/min, Recently, in order to clarify the strengthening mechanisms at high temperature, a new scheme to improve high temperature mechanical properties is desired. Therefore, the test ,technique development of high temperature creep behaviors for this material is very important. In this paper, the creep praperties and creep life prediction by Larson-Miller parameter method for STS304 stainless steel to be used for other high temperature components were presented at the elevated temperatures of 600, 650 and $700^{\circ}C$.

• Journal of Ocean Engineering and Technology
• /
• v.18 no.2
• /
• pp.64-69
• /
• 2004

The characteristics of the probability distribution for mechanical properties, e.g. tensile strength, reduction of area, and elongation, for STS304 stainless steel in elevated temperature are investigated. Tensile test is performed by constant crosshead speed controls with 1mm/min. The probability distribution function of measured mechanical properties seems to follow $\alpha$ 3-parameter Weibull, and shows a slight dependence on the temperature. When the temperature is raised, the shape parameter a is increased, but both the scale parameter $\beta$ and location parameter v are decreased.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.153-154
• /
• 2009

원자력발전소 증기발생기 전열관 보수 기술의 하나로 니켈 합금 전기 도금이 연구되고 있다. 여러 도금 공정변수 중 peak current density를 달리하여 Ni-P-Fe 전기도금층을 제조한 뒤, 열처리 온도 $325^{\circ}C$에서 10, 30일간 열처리를 한 후, 인장강도와 연신율을 측정하고, 그 파단면을 관찰하였다. 50mA/$cm^2$로 제조된 도금층은 100mA/$cm^2$로 제조된 도금층에 비해 우수한 열적안정성을 가짐을 알 수 있었다.

• Journal of the Korean Chemical Society
• /
• v.21 no.5
• /
• pp.379-383
• /
• 1977

Since the organophilic bentonite disperses well in polymer matrix, a composite material of polymer and bentonite was studied for its mechanical properties. To increase the degree of dispersion and the bond in forces to the polymer matrix, bentonite, encapsulated by imidazoline, was used as a filler. Polyethylene powder of particle size of 100 mesh was used, and organophilic bentonite, so-called bentone, whose particle size was 250 mesh was also used in this experiment. V-type mixer was used for mixing and Banbury mixer was used for melt-blending. The sample specimen were made by heating the mixture in the plate press, and the specimen were formed as a sheet, exactly the same as the mold on the plate. Tensile strength, bending strength and compressive strength were studied specially. Tensile strength, elongation rate, bending strength and bending rate at constant pressure were decreased as the filler content increased. Compressive strength was increased as the filler content increased.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.105-105
• /
• 2010

자동차 차체부품에 적용되는 플라스틱 소재는 강도와 내마모성, 내충격성의 충분한 물성확보가 필요하며, 이에 플라스틱 소재의 기계적 특성 향상을 위해 유리 섬유가 다량 함유된 복합소재적용이 증가하고 있다. 반면 플라스틱이 고강도화함에 따라 제품 성형을 위한 사출 금형을 손상시키는 사례가 빈번하게 발생하고, 소재의 유동성 저하에 따른 사출 불량이 증가하고 있어 고강성 플라스틱 복합소재에 대응하는 고경도, 고내마모 특성이 부여된 사출 금형의 개발이 시급한 실정이다. 특히 사출 금형에 사용되는 소재는 기존 소재에 비해 우수한 내마모성과 함께 고광택을 유지하는 것이 더욱 중요해졌으며, 이에 따라 유럽, 일본과 국내 연구진에 의해 다양한 연구가 진행되고 있다. 그 중에서도 일본에서 개발되어 국내에도 소개된 래디칼 질화는 기존 질화법에 표면의 화합물 층만을 제어하는 것으로 다소의 표면 광택 효과는 있으나, 플라스틱 사출에 그대로 적용하기에는 무리가 따르므로 그 용도가 극히 제한적이다. 본 연구에서 적용한 나노 질화기술은 0.1torr 이하의 고진공에서 고밀도의 플라즈마 에너지를 발생시키는 방법으로 화합물층이 없는 나노 크기의 질화층을 소재 표면에 형성시키는 기술로서, 처리 후에도 표면의 색상 및 광택의 변화가 없는 것을 특징으로 한다. 또한 표면 경도 및 피로 특성을 향상시킴으로써 금형의 내구 수명을 향상시킬 것으로 기대된다. 본 연구에서는 KP4 금형 소재를 사용하여 플라즈마 이온 질화 시험 조건에 따른 소재의 경도 및 내마모 특성을 파악하고, 미세 조직 분석 및 XRD 분석 등을 통해 내마모 특성 향상에 대한 기본 특성을 평가하였다. 또한 인장시험을 통해 인장강도, 항복강도 및 연신율을 파악하고, 이를 토대로 고주기 피로시험을 실시함으로써 S-N curve를 얻고, 이를 통해 피로 강도 및 피로 수명에 미치는 나노 질화 처리의 영향을 파악하고자 하였다. 플라즈마 이온 질화 시험은 질소와 수소 비율($N_2:H_2$), 진공도, Screen bias voltage, Bias voltage를 변화시켰으며, 챔버 온도는 $400^{\circ}C$로 고정하였으며, 처리시간도 3시간으로 고정하였다. 질소와 수소의 비율은 3:1일 때 최고의 내마모 특성을 보였으며, 진공도는 내마모 특성에 큰 영향을 미치지 않는 것으로 관찰되었다. KP4의 초기 경도값은 약 302 Hv인 반면 최적의 나노 질화처리를 거친 시편에서는 800Hv 이상의 Vickers 경도값을 보였다. SEM 미세조직 분석과 EPMA를 통한 성분 분석을 시행한 결과 표층으로부터 약 $1.5{\mu}m$의 나노질화층을 확인할 수 있었다.

• Korean Journal of Materials Research
• /
• v.8 no.9
• /
• pp.807-812
• /
• 1998

Interfacial reaction and mechanical properties between Sn-Bi-X ternary alloys(X : 2Cu. 2Sb 5In) and Cu-substrate were studied. Cu/solder joints were subjected to aging treatments for up to 60days to see interfacial reaction at $100^{\circ}C$ and then were examined changes of microstructure and interfacial compound by optical microscopy, SEM and EDS. Cu/solder joints were aged to 30days and then loaded to failure at cross head speed of 0.3mm $\textrm{min}^{-1}$ to measure strength and elongation. According to the result of EDS, it is supposed that the soldered interfacial zone was composed of $\textrm{Cu}_{3}\textrm{Sn}$ and $\textrm{Cu}_{6}\textrm{Sn}_{5}$. According to the tensile test of Cu/solder joint, joint strength was decreased by aging treatment. Fractographs of Cu/Sn-Bi solder detailed the effect of aging on fracture behavior. When intermetallic was thin, the fracture occurred through the solder. But as the interfacial intermetallic is thickened, the fracture propagated along the intermetallic/solder interface.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1995.05b
• /
• pp.597-602
• /
• 1995

원자력 발전소 증기발생기 전열관 재료인 합금 600의 대체재료로써 설계된 합금 690의 내식성의 향상을 위해서 염소 이온이 다량 포함된 환경에서의 부식 저항성을 크게 향상시킨다고 보고된 Mo을 첨가하여 부식 및 기계적 특성에 미치는 영향을 알아보았다. 미세조직상 Mo를 첨가함에 따라 기지에 미세한 석출물이 석출되어 입자의 미세화를 얻을 수 있었으며 연신율의 감소없이 항복 강도, 인장 강도 및 경도의 향상을 얻을 수 있었다. 공식 저항성은 Mo의 첨가량이 증가함에 따라 부식 속도가 감소하였다. 양극 분극 시험에서도 5$0^{\circ}C$, 3.5wt% NaCl 용액과 0.5N HCl 용액 모두에서 Mo의 함량이 증가할수록 부동태화 전류 밀도 및 임계 부동태화 전류 밀도가 감소하여 전반적으로 현저한 내식성의 향상을 관찰할 수 있었다.