• The Journal of Korean Academy of Prosthodontics
• /
• v.52 no.3
• /
• pp.195-201
• /
• 2014

Purpose: This study was designed to compare the amount of polymerization shrinkage of dual-cure resin cements according to different polymerization modes and to determine the effect of light activation on the degree of polymerization. Materials and methods: Four kinds of dual-cure resin cements were investigated: Smartcem 2, Panavia F 2.0, Clearfil SA Luting and Zirconite. Each material was tested in three different polymerization modes: self-polymerization only, immediate light polymerization and 5 minutes-delayed light polymerization. The time-dependent polymerization shrinkage-strain was evaluated for 30 minutes by Bonded-disk method at $37^{\circ}C$. Five recordings of each material with three different modes were taken. Data were analyzed using one-way ANOVA and multiple comparison Scheffe′test (${\alpha}$=.05). Results: All materials, except Panavia F 2.0, exhibited the highest polymerization shrinkage-strain through delayed light-activated polymerization. No significant difference between light activation modes was found with Panavia F 2.0. All materials exhibited more than 90% of polymerization rate in the immediate or delayed light activated group within 10 minutes. Conclusion: As a clinical implication of this study, the application of delayed light activation mode to dual-cure resin cements is advantageous in terms of degree of polymerization.

• The Journal of Korean Academy of Prosthodontics
• /
• v.48 no.1
• /
• pp.55-60
• /
• 2010

Purpose: The shrinkage of dental resin cement may cause several clinical problems such as distortion that may jeopardize the accurate fit to the prepared tooth and internal stress within the restorations. It is important to know the polymerization shrinkage-strain of dental resin cement to reduce clinical complications. The purpose of this study was to investigate the polymerization shrinkage-strain kinetics of six commercially available dental resin cements. Material and methods: Three self-cure resin cements (Fujicem, Superbond, M-bond) and three dual-cure resin cements (Maxcem, Panavia-F, Variolink II) were investigated. Time dependent polymerization shrinkage-strain kinetics of the materials were measured by the Bonded-disk method as a function of time at $23^{\circ}C$, with values particularly noted at 1, 5, 10, 30, 60, 120 min after mixing. Five recordings were taken for each materials. The data were analyzed with one-way ANOVA and Scheffe post hoc test at the significance level of 0.05. Results: Polymerization shrinkage-strain values were 3.72%, 4.19%, 4.13%, 2.44%, 7.57%, 2.90% for Fujicem, Maxcem, M bond, Panavia F, Superbond, Variolink II, respectively at 120 minutes after the start of mixing. Panavia F exhibited maximum polymerization shrinkage-strain values, but Superbond showed minimum polymerization shrinkage-strain values among the investigated materials (P < .05). There was no significant differences of shrinkage-strain value between Maxcem and M bond at 120 minutes after the start of mixing (P > .05). Most shrinkage of the resin cement materials investigated occurred in the first 30 minutes after the start of mixing. Conclusion: The onset of polymerization shrinkage of self-cure resin cements was slower than that of dual-cure resin cements after mixing, but the net shrinkage strain values of self-cure resin cements was higher than that of dual-cure resin cements at 120 minutes after mixing. Most shrinkage of the dental resin cements occurred in the first 30 minutes after mixing.

• Restorative Dentistry and Endodontics
• /
• v.34 no.2
• /
• pp.103-112
• /
• 2009

The purpose of this study was to compare the effect of curing methods of adhesive resins and resin cements in the root canal. Crown portions of 32 single-rooted mandibular premolars were removed. Routine endodontic treatment was done, and 9 mm deep post spaces were prepared within root canals. No.3 FRC Postec posts (Ivoclar-Vivadent AG, Liechtensteih) were cemented in the post spaces by self-(SC) or light-curing (LC) using two dual-cured adhesives (Adper Scotchbond multi-purpose plus and Exite DSC )and resin cements (RelyX ARC and Variolink II). They were assigned to 4 groups (n=8): R-SC, R-LC, V-SC, V-LC group. After stored in distilled water for 24 hours, each root was transversally sectioned with 1.5 mm thick and made three slices. The specimens were subjected to push-out test in a universal testing machine (EZ Test, Shimadzu Co., Japan) with a crosshead speed of 1 mm/min. The data were analyzed with repeated ANOVA and one-way ANOVA. Also the interface of post-resin cement and resin cement-canal wall of each group was observed under FE-SEM. When fiber posts were cemented into the root canal using total-etch adhesives, the bond strength and adaptation between post and root canal dentin was affected by curing method. Self-cure of adhesives and resin cements showed higher bond strength and closer adaptation than light-cure of them.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.26 no.3
• /
• pp.311-322
• /
• 2010

The purpose of this study was to evaluate the bond strengths between IPS e.max Press and four different types of resin cements that often used for esthetic restoration. Disc shaped IPS e.max Press blocks(N=40, diameter: 12mm, thickness: 3mm) were fabricated according to the manufacture's instruction and cleaned with ultrasonic cleaner. They were embedded into an autopolymerizing acrylic resin. Fourty cylinder shaped resin block(Filtek Z350, diameter: 4.5mm, thickness: 3mm) were fabricated using a plastic tube. Each specimens were randomly divided into 4 experimental group and bonded each other using 4 different resin cements(Variolink II(light-cure), Variolink II(dual-cure), Calibra, Super-Bond C&B) according to the manufactures' recommendations. All the specimens were stored in normal saline at $37^{\circ}C$ for 24 hours before test. Universal testing machine at a crosshead speed of 1mm/min was used to evaluate the shear bond strength. The data were statistically analyzed using one-way ANOVA(P<.01). Multiple comparison was done by the Tukey HSD test. The shear bond strength of Super-Bond C&B to e.max was significantly lower than those of Calibra, Variolink II(light-cure), Variolink II(dual-cure) (P<.01). The shear bond strength of Calibra, Variolink II(light-cure), Variolink II(dual-cure) to e.max were not significantly different. The shear bond strengths of light-cure/dual-cure cement were higher than that of self-cure cement.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.30 no.2
• /
• pp.138-144
• /
• 2014

Purpose: This study examined the water sorption of commonly used dual-cure resin cements and compared the change in the micro-hardness among the cements. Materials and Methods: Five types of dual-cure resin cements (Maxcem, Duo-link, Panavia F, Variolink II, Rely X Unicem) were selected. Fifty specimens were classified into five groups containing ten specimens in each group. The water sorption of the five specimens in each group was evaluated after being immersed in distilled water (DDW) for seven days. The following results were obtained by comparing the specimens immersed in DDW with those not immersed in DDW. Results: 1. The water sorption of Maxcem showed the highest score, followed by Panavia F. These two cements were followed by Duo-link and Rely X Unicem. The water sorption of Variolink II showed the lowest score among the cements used in this study. 2. Among the specimens not immersed in DDW, the micro-hardness of Rely X Unicem showed the highest score followed by Panavia F and Variolink II. These cements were followed in order by Duo-link and Maxcem. 3. Among the specimens immersed in DDW, the microhardness of Rely X Unicem showed the highest score followed by Maxcem, Panavia F and Variolink II. Duo-link shoed the lowest score among the cements used in this study. 4. Maxcem, Duo-link, Panavia F and Rely X Unicem showed significant differences in micro-hardness due to water resorption but Variolink II was unaffected by immersion in water. Conclusion: Using the resin cement which has lower water sorption and higher micro-hardness is recommended.

• Restorative Dentistry and Endodontics
• /
• v.33 no.5
• /
• pp.419-427
• /
• 2008

This study analyzed the influence of dental adhesive/primer on the bond strength between indirect resin composite and the resin cement. Seventy disc specimens of indirect resin composite (Tescera Dentin, Bisco) were fabricated. And bonding area of all specimens were sandblasted and silane treated for one minute. The resin cements were used with or without application of adhesive/primer to bonding area of indirect resin restoration, Variolink-II (Ivoclar-Vivadent) : Exite DSC, Panavia-F (Kuraray) : ED-Primer, RelyX Unicorn (3M ESPE) Single- Bond, Duolink (Risco) : One-step, Mulitlink (Ivoclar-Vivadent) : Multilinh Primer. Shear bond strength was measured by Instron universal testing machine. Adhesive application improved shear bond strength (p<0.05) But Variolink II and Panavia-F showed no statistically significant difference according to the adhesive application. With the above results, when resin inlay is luted by resin cement it seems that application of dental adhesive/primer is necessary in order to improve the bond strength.

• Korean Journal of Dental Materials
• /
• v.44 no.2
• /
• pp.151-161
• /
• 2017

The purpose of this study was to examine the effect of shade and thickness of resin-nanoceramic CAD-CAM block (RNB) on the microhardness of dual-cured resin cement, as well as to measure the number of photons transmitted through RNBs of different thicknesses and colors. One dual-cured resin cement was used to prepare resin cement specimens. Resin cement specimens were light-cured for 40 seconds through 3 shades (A1, A2, A3 in HT (high translucency) and LT (low translucency) respectively) and four thicknesses (1, 2, 3, 4 mm) of RNB specimens. Vickers microhardness measurements of resin cement specimens were performed using a Vickers hardness tester. The light transmission of RNB specimens was measured using a spectrometer (SpectroPro-500, Acton Research, Acton, MA, U.S.A.), and the translucency parameter was calculated using the CIEL*a*b* system. Data were statistically analyzed by ANOVA and Tukey's test. There was a significant decrease of microhardness of resin cement specimen with an overlay of 4 mm of RNB thickness and A3 shade in comparison to A1 and 1 mm, respectively (p<0.05). The translucency parameter values and light transmission of RNBs tested differed significantly, according to the thicknesses of the specimen (p<0.05). Light transmission is decreased with increase in the thicknesses of RNBs. Shade A1 transmitted more light than darker blocks. A decrease in microhardness of resin cement specimens was observed with increasing thickness and shade (A1 to A3) of RNBs.

• Korean Journal of Dental Materials
• /
• v.45 no.4
• /
• pp.301-310
• /
• 2018

The purpose of this study is to evaluate the compatibility of universal adhesives with two dual-cured resin cements. Eighty human molars were divided into eight groups. Tooth was embedded in self-curing acrylic resin and sectioned horizontally to exposure dentine surface. After polishing with 600-grit SiC paper, adhesives were applied. All-Bond Universal (Bisco), G-premio bond (GC), Scotch-bond universal (3M ESPE), Scotch-bond Multipurpose (3M ESPE) were used in this study. Calibra (Dentsply) as a conventional dual-curing resin cement and RelyX Ultimate (3M ESPE) as an amine free resin cement were used. The adhesives and the cements were applied according to the manufacturer's instructions. Final specimens were cylinder (diameter 2mm, height 3mm) shape. After storing in distilled water at $37^{\circ}C$ for 7 days the shear bond strength (SBS) test was performed. There was no significant difference in shear bond strength between the adhesives when RelyX Ultimate was used (p>0.05). However, when Calibra used with Scotch-bond Multipurpose and All-Bond Universal were used, statistically higher SBS was observed, as compared to the groups which Calibra cements with G-premio bond and Scotch-bond universal adhesive (p<0.05) were used. Within the limitations of this study, RelyX Ultimate resin cement was compatible with universal adhesives of various pH. All-Bond Universal adhesive was compatible with a resin cement containing the tertiary amine.

• Restorative Dentistry and Endodontics
• /
• v.33 no.4
• /
• pp.389-396
• /
• 2008

The purpose of this study was to evaluate the color stability of resin cements with accelerated test. Four dual curing resin cements: Panavia-F (KURARAY). Duolink (BISCO), Variolink-II (Ivoclar Vivadent), and RelyX Unicem (3M ESPE) and 1 self curing resin cement: Resiment CE (j. l. Blosser) were used in this study. In control group, Gradia Anterior (GC) composite resin and Tescera Dentin (Bisco) indirect composite were used. Ten disk shape specimens were made from each resin cement. The specimens were subjected to an accelerated aging process in a refrigerated bath circulator at 60$^{\circ}C$ for 15 and 30 days. Spectrophotometric analyses were made before and after 15 days and 30 days of accelerated aging time. The color characteristics ($L^*,\;a^*,\;b^*$) and the color difference (${\Delta}E^*$) of the specimens before and after immersion were measured and computed. Regardless of type of the resin cements, $L^*$ value was decreased and $a^*$ value was increased, but there were no significant difference. But $b^*$ value was increased significantly (p < 0.05). Tescera inlay showed least color change (p < 0.05), but Gradia showed notable color change after 15 days. After 30 days on accelerated aging, ${\Delta}E^*$ value was increased (Panavia-F < Variolink-II < Resiment CE < Duolink < Unicem) (p < 0.05). but there were no significant difference among Panavia-F, Variolink-II, and Resiment CE groups. After 30 days of accelerated aging, ${\Delta}E^*$ value of all resin cements were greater than 3.0 and could be perceived by the human eye.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.38 no.4
• /
• pp.189-195
• /
• 2022

Purpose: For orthodontic bracket bonding, light curing resin cement is widely used because the process is convenient, and it can be polymerized at the desired time. This study compared the difference of bonding strength of orthodontic resin cement according to storage condition. Materials and Methods: After acid etching the bovine enamel surface with 37% phosphoric acid, 15 orthodontic brackets for mandible incisors were bonded with Ortho Connect and Orthomite LC according to following three conditions; 1) Immediate after 4℃ refrigeration for 3 months (IR), 2) One day room temperature after 4℃ refrigeration for 3 months (OR), 3) Room temperature for 3 months (RT). The shear bond strength was measured with a universal material tester and failure pattern of the specimen was observed. Two-way ANOVA and One-way ANOVA were used at the 95% significance level. Results: Ortho Connect that was applied immediately after refrigeration showed the maximum shear bond strength. Orthomite that was applied immediately after refrigeration showed the lowest shear bond strength, and the group stored at room temperature for three months showed the highest shear bond strength, and the difference between the two groups was significant. Conclusion: Ortho Connect can be used without worrying about bond strength even if it is used immediately after refrigeration, but Orthomite should be kept at room temperature sufficiently after refrigeration.