• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.8
• /
• pp.35-41
• /
• 2010

White Etching Layer(WEL) is a phenomenon that occurs on the surface of rail due to wheel/rail interactions such as excessive braking and acceleration. Rolling Contact Fatigue(RCF) cracks on the surface of rail have been found to be associated with WEL. In this study, we have investigated RCF damages of white etching layer using twin disc testing and fatigue analysis. These tests consist of wheel flat tests and rolling contact fatigue tests. WEL has been simulated by wheel flat test. It has been founded that the WEL with a bright featureless contrast is formed on the surface of specimen by etching. Rolling contact fatigue test was conducted by using flat specimens with the WEL generated by the wheel flat test. It has been observed that two types of cracks occur within the specimen. The contact fatigue test was simulated in 2D elastic-plastic FE simulations. Based on loading cycles obtained from the finite element analysis, the fatigue life analysis according to the thickness variation of WEL was carried out. The longest fatigue life was observed from the thickness of 20um.

• Journal of the Korean Society for Precision Engineering
• /
• v.29 no.6
• /
• pp.613-620
• /
• 2012

Rails are subjected to damage from rolling contact fatigue, which leads to defects such as cracks. Rolling contact fatigue damages on the surface of rail such as head check, squats are one of growing problems. Another form of rail surface damage, known as "Ballast imprint" has become apparent. This form of damage is associated with ballast particles becoming trapped between the wheel and the surface of rail. These defects are still one of the key reasons for rail maintenance and replacement. In this study, we have investigated whether the ballast imprint is an initiator of head check type cracks and effect of defect size using Finite element analysis. The FE analysis were used to investigate stresses and strains in subsurface of defects according to variation of defect size. Based on loading cycles obtained from FE analysis, fatigue analysis for each point was carried out.

• Journal of the Society of Naval Architects of Korea
• /
• v.28 no.2
• /
• pp.275-284
• /
• 1991

Fatigure crack growth from surface defects is one of the most important subjects for the evaluation and the assurance of safety in pressure vessels, piping systems, ship hulls and other various structures. This paper attempts to analysis some practical or general problems such as the estimation of crack growth life to penetrate the plate thickness, based on fatigure crack growth from a single surface flaw and the interaction of multiple flaws. An experiment on the coalescence of multiple undercuts was carried out under cyclic tension condition as a attempt to the analysis of multiple crack problems. It is noted that the fracture strength is characterized by the analogy to that in a single crack growth.

• Journal of Ocean Engineering and Technology
• /
• v.8 no.2
• /
• pp.141-150
• /
• 1994

In designing, the strength of tubular joint has been an important problem for integrity of steel structures in which many tubular members are used. This paper presents the results of FEM analysis on stress concentration and fatigue crack initiation life for two types of tubular joints. One is circular and rectangular T type joints which consist of circular brace and rectangular chord. Another is circular and circular T type joints which consist of circular brace and circular chord. FEM analyses were performed under the axial load and in-plane bending moment. The fatigue crack initiation life can be estimated by using $\varepsilon$-N curve and by applying the Palmgren-Miner linear damage rule. According to the results, the stress concentration factor(SCF) of circular and rectangular joints is higher than that of circular and circular joints. The fatigue crack initiation lives of circular-circular joints and circular-rectangular joints were calculated.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.23 no.4
• /
• pp.319-327
• /
• 2020

In this study a methodology to evaluate fatigue life of the electronic parts for the fighter radar unit under random vibration loading is presented. To do this, one parameter for the 3-σ RMS quation of Steinberg fatigue model is modified to come up with a printed circuit board(PCB) with multiple electronic parts, while fundamental frequency and dynamic deflection of the PCB are calculated from a MATLAB based finite element computer code. For the RIFA structure selected in this study, the 3-σ RMS fatigue limit displacement is reduced to 0.741 times as much as the Steinberg model. This investigation allows to assess the life of multiple electronic parts mounted on the PCB with reinforced metal cover/body showing non-sinusoidal deflection patterns.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.41 no.5
• /
• pp.375-380
• /
• 2017

This paper reports the results of an acceleration test to predict the contact-induced failure that could occur at the cylinder-to-hole joint for the fuel rod of a sodium-cooled fast reactor (SFR). To incorporate the fuel life of the SFR currently under development at KAERI (around 35,000 h), the acceleration test method of reliability engineering was adopted in this work. A finite element method was used to evaluate the flow-induced vibration frequency and amplitude for the test parameter values. Five specimens were tested. The failure criterion during the life of the SFR fuel was applied. The S-N curve of the HT-9, the material of concern, was used to obtain the acceleration factor. As a result, a test time of 16.5 h was obtained for each specimen. It was concluded that the $B_{0.004}$ life would be guaranteed for the SFR fuel rods with 99％ confidence if no failure was observed at any of the contact surfaces of the five specimens.

• Journal of the Microelectronics and Packaging Society
• /
• v.13 no.1 s.38
• /
• pp.63-72
• /
• 2006

Mobile products, such as cellular phones, PDA and notebook, are subjected to many different mechanical loads, which include bending, twisting, impact shock and vibration. In this study, a cyclic bending test of the BGA package was performed to evaluate the fatigue life. Special bending tester, which was suitable for electronic package, was developed using an electromagnetic actuator. A nonlinear finite element model was used to simulate the mechanical bending deformation of solder joint in BGA packages. The fatigue life of lead-free (95.5Sn4.0Ag0.5Cu) solder joints was compared with that of lead-contained (63Sn37Pb). When the applied load to the specimen is small, the lead-free solder has longer fatigue life than lead-contained solder. The fatigue crack is initialized at the exterior solder joints and is propagated into the inner solder joints.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.22 no.2
• /
• pp.141-147
• /
• 2014

This study aims to investigate the influence of bevel angles on the fatigue life of V-groove butt-welded joints with back-plates made by SM490A steel material, generally used for excavators, because changes in the geometry, material and surface properties of welded regions affect the fatigue life of welded structures. Butt type test specimens were prepared by the $CO_2$ welding of rolled steel plates (SM50A steel) with a thickness of 13.5 mm at a welding speed of 30 cm/min and these Butt type test specimens had two different groove angles, which are $40^{\circ}$ (A type) and $30^{\circ}$ (B type). In order to investigate differences in fatigue life between two types, 4-point bending fatigue tests were conducted with a stress ratio of R=0.1 under the cyclic loading environment at a frequency of 5 Hz at room temperature. The fatigue life of A type specimens was approximately 7% higher than that of B type specimens. The stress concentration factors calculated by finite element analysis were 2.16 for A type and 2.25 for B type, whose difference was caused by the influence of the back-plates of butt-welded structures. The current results could provide important guidelines to determine the V-groove angle of butt-welded joints with a satisfactory fatigue life, although under severe operating conditions.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.13 no.2
• /
• pp.1-9
• /
• 2005

An end beam is one of the most important structural members supporting uncovered freight under in-service loading. In general, it needs to endure over 25 years. However fatigue fracture has occurred at dynamic stress concentration location of the end beam because user's specifications demanded high speed and vehicle manufacturer made the uncovered freight car with comparatively low strength and stiffness. For durability analysis, finite element analysis is performed to evaluate the problem of uncovered freight structure and local strain. The uncovered freight car was operated on actual problematic railroad line to measure dynamic stress versus time history on the critical part from which a crack is initiated often. Rainflow cycle counting method was used to estimate fatigue damage at dangerous area under operating condition. Therefore, this study shows that analytical fatigue life at the end beam can be predicted on the basis of S-N curve and structure analysis and has a fairly good correlation with experimental fatigue life.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.39 no.8
• /
• pp.758-765
• /
• 2011

Recently, the wind energy has been widely used as a renewable energy resource due to lack and environmental issues of the mostly used fossil fuel. This work is to develop a 500W class blade design of vertical axis wind turbine system which will be applicable to relatively low speed region like Korea and for the domestic use. For this wind turbine a high efficiency and low noise turbine blade was designed with the proposing aerodynamic design procedure, and a light composite structure blade. Structural analyses were performed using the Finite Element Method and fatigue life of the designed blade is estimated. Finally, in order to check its performance, the manufactured blade was tested by using truck and the results of test was good with respect to its analysis result.