• Journal of Welding and Joining
• /
• v.16 no.2
• /
• pp.64-72
• /
• 1998

This study aims a investigating the effect of volume fraction of chromium carbide phase(VFC) of hardfaced iron/chromium alloys on fracture toughness. The alloys were deposited twice on a mild steel plate using self-shielding flux cored arc welding process. In order to examine VFC effect, different VFC (0.28∼0.62) were employed by changing the Cr and C content, while the ratio of Cr/C was fixed in the range of 5.7∼6.6. Fracture toughness was constant as increasing VFC because fracture surface was developed in the eutectic phase which was growing parallel with introduced sharp notch in the hypoeutectic alloys, but fracture toughness did not decreased in spite of increasing volume fraction of coarse primary chromium carbide phase which was easily craced at the low stress because the growth direction of chromium carbide phase were more irregular as increasing VFC in the hypereutectic alloys.

• Proceedings of the KWS Conference
• /
• 1998.05a
• /
• pp.251-252
• /
• 1998

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.9 no.1
• /
• pp.70-76
• /
• 2013

Several finite element models for the leak-before-break (LBB) assessment of overlay dissimilar metal weldment were constructed and analyzed to develop a simple finite element modeling method. The J-integral, crack opening displacement (COD) and J-integral distribution along the crack front in thickness direction due to the applied moment were obtained from the analysis results of the constructed finite element models, and studied compared to the previous literatures. It is concluded that the modeling with base material only is simple and produces a slightly conservative results compared to the complex modeling composed with weld metal and base metal in the calculation of J-integrals and COD values which are used for the calculation of fracture toughness and postulated leakage crack length respectively.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.495-496
• /
• 2013

• Journal of Welding and Joining
• /
• v.16 no.1
• /
• pp.114-124
• /
• 1998

The effect of matrix phase (austenite, pearlite, martensite) on the low stress abrasion resistance in the chromium-carbide-type high Cr white iorn hardfacing weld deposites has been investigated. In order to examine matrix phase, a series of alloys with different matrix phase by changing the ratio of Cr/C system by heat treatment were employed. The alloys were deposited twice on a mild steel plate using self-shielding flux cored arc welding process. The low stress abrasion resistance of the alloys against sands was measured by the Dry Sand/Rubber Wheel Abrasion Test(RWAT). Even though formation of pearlite phase in the matrix showed higher hardness than that of austenite, there was no observable difference in wear resistance between the pearlite and austenite phase for the same amount of chromium-carbide in the matrix. On the other hand, the formation of martensitic phase,, from heat treated austenitic alloys (high content of Cr), enhanced wear resistance due to its fine secondary precipitates.

• Journal of Welding and Joining
• /
• v.16 no.1
• /
• pp.125-133
• /
• 1998

The effect of volume fraction of Cr carbide phase (Cr CVF) on the low stress abrasion resistance in the chromium-carbide-type high Cr white iron hardfacing weld deposits has been investigated. In order to examine Cr CVF, a series of alloys with varying Cr CVF by changing chromium and carbon contents and the ratio of Cr/C were employed. The alloys were deposited once or twice on a mild steel plate using the self-shielding flux cored arc welding process. The low stress abrasion resistance of the alloys against sands was measured by the Dry Sand/Rubber Wheel Abrasion Test (RWAT). It was shown that hardness and abrasion resistance increased with increasing Cr CVF within the whole test range (Cr CVF : 0.23-0.64). Both primary Cr carbide and eutectic Cr carbide were particularly effective in resisting wear due to their high hardness.

• Journal of Welding and Joining
• /
• v.14 no.4
• /
• pp.53-61
• /
• 1996

It was attempted to improve the wear resistance of Al alloy under the load condition by making a formation of the thicker surface hardening alloy layers. The thicker surface hardening alloy layers were formed on 6061 Al alloys overlayed by MIG and TIG welding process with Cu powders feeding. The characteristics of hardening and wear resistance have been investigated in relation to the microstructures of alloyed layers, with a selection of optimum alloying conditions for formation of overlaying layer. The results obtained were summarized as follows With increasing feeding rate of Cu powders by MIG welding, the hardness and specific wear of the overlay weld alloys were increased. It is considered that these high hardness and specific wear of overlay weld alloys were due to the formation of Θ($Al_2Cu$) phases. With increasing feeding rate of Cu powders by TIG welding, the hardness and specific wear of the overlay weld alloys were increased in feeding rates 12 and 18g/min. However, the hardness and specific wear were decreased in the powder feeding rate 38g/min. It is considered that considered that decrease of hardness and specific wear in the powder feeding rate 38g/min due to formation of ${\gamma}$($Al_4Cu_9$) phases.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.05a
• /
• pp.1219-1220
• /
• 2012

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2011.06a
• /
• pp.505-506
• /
• 2011

• Journal of Welding and Joining
• /
• v.28 no.3
• /
• pp.31-35
• /
• 2010