• Journal of Welding and Joining
• /
• v.14 no.5
• /
• pp.106-112
• /
• 1996

The effects of Ti addition in welding wire on the spatter generation and the droplet transfer phenomena were investigated. With increasing Ti content the spattering rate was decreased but the ratio of large size spatter (D $\geq$ 1. 0mm) was increased in both short circuit and globular transfer mode of $CO_2$welding. In short circuit transfer region, the arcing time was increased and the droplet transfer frequency was decreased with increasing Ti content In globular transfer region, the transition current and voltage to globular transfer was lowered and the welding condition region for stable globular transfer was widened with increasing Ti content.

• Journal of Welding and Joining
• /
• v.17 no.1
• /
• pp.55-61
• /
• 1999

The effect of S content in welding wires on the arc stability was investigated, in the region of short circuit transfer and spray transfer. In the region of short circuit transfer, with increasing S content, average arcing time and average short circuit time were decreased. Therefore, droplet transfer frequency was increased, due to the reduction of arcing time and peak current at the moment of arc-reiginition was decreased, due to the decrease of short circuit time. In the region of spray transfer, the fluctuation degree of arc current and arc voltage became more stable, with increasing S content.

• Journal of Welding and Joining
• /
• v.16 no.6
• /
• pp.52-58
• /
• 1998

The effect of Si content in welding wires on th arc stability was investigate, in the region of short circuit transfer and spray transfer. In the region of short circuit transfer, with increasing Si content, average arcing time and average short circuit time were increased. Therefore, droplet transfer frequency was decreased, due to the increase of arcing time and peak current at the moment of arc-reiginition was increased, due to the increase of short circuit time. In the region of spray transfer, the fluctuations of arc current and arc voltage was the most stable in wire with Si content of about 00.60 wt.%.