• Transactions of the Korean hydrogen and new energy society
• /
• v.7 no.1
• /
• pp.81-92
• /
• 1996

The Ar/Ar-$H_2$ plasma method was applied to reduce oxides and refine metals of V, Ta and B. In addition, the high temperature chemical reaction in Ar plasma and of the refining reaction in the Ar-(20%)$H_2$ plasma were analyzed. The crude V of 96wt% purity was obtained at the ratio of $C/V_{2}O_{5}=4.50$ by the Ar plasma reduction grade and the maximum reduction was obtained at $C/V_{2}O_{5}=4.50$ due to the $O_{2}$ loss from the thermal decomposition of vanadium oxide. In the Ar-(20%)$H_2$ plasma refining, the metallic V of 99.2wt% was produced at the ratio of $C/V_{2}O_{5}=4.40$. It was considered that a main refining reaction resulted from the chemical reaction between the residual carbon and residual oxygen. The metallic Ta of 99.8wt% was obtained at the ratio of $C/Ta_{2}O_{5}=5.10$ in a Ar plasma reduction and the Oz loss from the thermal decomposition of tantalum pentoxide did not take place. The deoxidation reaction was more significant than the decarburization reaction in the Ar-(20%)$H_2$ plasma refining and the metallic Ta of 99.9wt% was produced within the range of $C/Ta_{2}O_{5}$ ratio of 4.50 to 5.10. The Vickers hardness of Ta in the above mentioned range was about 220Hv due to the decrease in a residual oxygen by the deoxidation reaction. On the other hand, C is no suitable agent for the reduction of $B_{2}O_{3}$ by the Ar and Ar-$H_2$ plasma. But Fe-B-Si alloy was produced with the reduction of $B_{2}O_{3}$ in the melt when Fe, C, $B_{2}O_{3}$, and ferroboron mixtures were melted by the high frequency induction melting.