• 동력기계공학회지
• /
• 제11권4호
• /
• pp.86-91
• /
• 2007

This study was investigated to know the effect of subzero treatment in austempered ductile cast iron. Retained austenite transformed to martensite by subzero treatment. With decreasing subzero treatment temperature, more volume fraction of retained austenite transformed to martensite and transformed to martensite above 30% by subzero treatment temperature at $-196^{\circ}C$. With decreasing subzero treatment temperature, the value of strength and hardness increased but the value of elongation and impact value decreased. In case of subzero treatment at $-196^{\circ}C$, hardness value increased about 18% and impact value decreased by above 20%. We could find that subzero treated specimens had a little of effect on the tensile properties but had very much effect on the hardness and value of the impact.

• 동력기계공학회지
• /
• 제12권1호
• /
• pp.47-52
• /
• 2008

This study was investigated the effect of subzero treatment in austempered ductile cast iron. Retained austenite transformed to martensite by subzero treatment and strain. With decreasing subzero treatment temperature and increasing strain, retained austenite transformed more to martensite and transformed 30% above by subzero treatment at $-196^{\circ}C$. With decreasing subzero treatment temperature, the value of strength and ratio of increasing of strength, hardness and ratio of increasing of hardness increased but the value of elongation and ratio of decreasing of elongation decreased. With decreasing subzero treatment temperature, impact value and ratio of decreasing of impact value decreased. In case of subzero treatment at $-196^{\circ}C$, hardness value increased about 18% and impact value decreased above 20%. We could find that in subzero treated specimens had a little of effect on the tensile properties but had very much effect on the hardness and value of the impact.

• 한국주조공학회지
• /
• 제41권4호
• /
• pp.331-341
• /
• 2021

3.6wt%C-2.5wt%Si 구상흑연주철을 오스템퍼링 열처리하는 동안 프로세싱 윈도우에 미치는 오스템퍼링 온도, 오스테나이트화 처리 온도와 시간, 구리 첨거량 그리고 사전 열처리의 영향을 연구하였다. 350℃의 오스템퍼링 처리 온도에서 최대 프로세싱 윈도우를 얻었다. 프로세싱 윈도우는 오스테나이트화 처리 온도가 850에서 900℃로 증가함에 따라 증가하였으나 950℃로 증가하면 오히려 감소하였다. 프로세싱 윈도우는 오스테나이트화 처리 시간이 30분에서 2시간까지 증가함에 따라 증가하였다가 4시간일 때 감소하였다. 최적 오스템퍼링 처리 조건은 900℃에서 2시간인 것으로 나타났다. 프로세싱 윈도우는 구리 첨가량이 0.0~0.8wt% 범위에서 증가함에 따라 증가하였다. 프로세싱 윈도우는 주방 상태의 구상흑연주철에 비하여 사전 노르말라이징 처리로 증가하였으며 사정 어닐링 처리로 감소하였다.

• 한국주조공학회지
• /
• 제8권spc1호
• /
• pp.115-124
• /
• 1988

• 산업기술연구
• /
• 제24권A호
• /
• pp.3-8
• /
• 2004

This study was performed to investigate the effect of two step austenitized treatment on the mechanical properties and fracture characteristic of the ductile cast iron and austempered ductile cast iron(ADI). The obtained results of this study were as follows. The matrix structures of specimens were changed differently by austenitizing heat treatment. Microstructure of austempered ductile cast iron obtained by two step austenitized treatment was bainitic ferrite and retained austenite. With two step austenitized treatment, vield strength, tensile strength and hardness decreased, while the elongation increased.

• 동력기계공학회지
• /
• 제12권3호
• /
• pp.72-77
• /
• 2008

This study was investigated to know the effect of Cu addition on austempered ductile cast iron at various temperatures and times. Test results showed that the volume fraction of retained austenite and the carbon contents of retained austenite showed the greatest value at $400^{\circ}C$. Also, in case of specimens having more Cu contents, the volume fraction of retained austenite and the carbon contents of retained austenite showed the lower value. After austempering treatment, tensile strength and Impact value increased, but elongation decreased. With increasing austempering treatment temperature, tensile strength, elongation, and impact value decreased. In case of specimen having more Cu contents, tensile strength showed the higher value, but elongation showed the lower value. Damping capacity was decreased by austempering treatment and was not affected on austempering temperature and time. In case of specimen having more Cu contents, damping capacity showed the higher value.

• 한국주조공학회지
• /
• 제14권1호
• /
• pp.35-44
• /
• 1994

Mechanical properties of austempered ductile iron can be guaranteed if a good knowledge of its metallugical structure is obtained. In this paper, the effects of small Mo additions to austempered ductile iron on its metallurgical structures as a function of section size are examined. From the results, it is found that ${\gamma}-pool$ region and segregation of Mo in ${\gamma}-pool$ region are increased with increase in the section size.

• 미래기술융합논문지
• /
• 제2권2호
• /
• pp.9-14
• /
• 2023

이 연구는 1050MPa급 경량 연성 주철 주관류 컨트롤 암을 개발하기 위한 첫 해의 결과를 보여줍니다. 첫째, 최적 설계 구조를 위한 레이아웃 설계 및 구성 요소 개발, 그리고 컨트롤 암 강성과 최적 구조 디자인 및 강건성 설계를 통해 예상 응력을 제어하는 중점 영역의 강건성을 달성합니다. 둘째, 높은 강성과 고성능 경량 구조를 반영하는 컨트롤 암을 개발합니다. 중공을 통해 소비자가 요구하는 설계와 강성을 충족시키기 위해 개발된 컨트롤 암은 코어 제작 공정을 개발합니다. 셋째, 최적의 합금 조성과 열처리 방법을 통해 철 합금 (Cu, Ni, Mo)의 양과 Austempered 열처리 및 조화 상태를 도출합니다. 넷째, 저강도, 고강성 구성 요소 개발을 위해 최적의 성형기술 개발을 통해 최적의 주조 기술 개발로 이어지는 구성 요소 개발을 위한 높은 강도의 주조 형성 기술을 개발하기 위한 시도를 합니다.

• 한국주조공학회지
• /
• 제11권3호
• /
• pp.228-235
• /
• 1991

The Effects of the matrix structures and the amount of the retained austenite in austempered ductile iron(ADI) which contains Ni, Cu and Mo on fracture characteristics were inverstigated. The structures were changed from lower bainite to mixture of Lower and upper bainite, and then to upper bainite as austempering temperature increased. A higher austempering temperature yielded lower tensile strength and hardness, but higher impact valve and $K_{IC}$. In addition, the amount of the retained austenite increased with the austempering temperatures. Fracture surface showed a fibrous pattern and a dimple pattern with increasing the retained austenite amount.

• 한국주조공학회지
• /
• 제29권2호
• /
• pp.86-94
• /
• 2009

The effect of austenitizing temperature and time on the processing window of 3.60wt%C - 2.50wt%Si - 0.80wt%Cu ductile cast iron and that of the amount of copper added were investigated. The second stage reaction at 400oC was retarded with increased austenitizing temperature. The widest processing window was obtained at the lower austempering temperature with the increased time at the same austenitizing temperature. The width of the widest processing window was decreased with the increase of time at the same austenitizing temperature. The width of processing window was increased with the increased amount of copper added.