• Journal of Welding and Joining
• /
• v.14 no.4
• /
• pp.53-61
• /
• 1996

It was attempted to improve the wear resistance of Al alloy under the load condition by making a formation of the thicker surface hardening alloy layers. The thicker surface hardening alloy layers were formed on 6061 Al alloys overlayed by MIG and TIG welding process with Cu powders feeding. The characteristics of hardening and wear resistance have been investigated in relation to the microstructures of alloyed layers, with a selection of optimum alloying conditions for formation of overlaying layer. The results obtained were summarized as follows With increasing feeding rate of Cu powders by MIG welding, the hardness and specific wear of the overlay weld alloys were increased. It is considered that these high hardness and specific wear of overlay weld alloys were due to the formation of Θ($Al_2Cu$) phases. With increasing feeding rate of Cu powders by TIG welding, the hardness and specific wear of the overlay weld alloys were increased in feeding rates 12 and 18g/min. However, the hardness and specific wear were decreased in the powder feeding rate 38g/min. It is considered that considered that decrease of hardness and specific wear in the powder feeding rate 38g/min due to formation of ${\gamma}$($Al_4Cu_9$) phases.

• Journal of Welding and Joining
• /
• v.15 no.1
• /
• pp.135-148
• /
• 1997

It was attempted to improve wear resistance and durability under the load surface pressure that make a formation of the thick (mm-order) hard-surfacing layer for aluminum alloy of 5083. The thick hard layers were formed on the surface of 5083 by TIG overlay method. Al-(25.4, 33.6, 45.7 mass%) Cu filler metals which were newly developed were overlaid on two base metals forming the one bead, one layer and two layers. The investigation was made on the characteristics of hardening and wear resistance in relation to the microstructure of overlaid layers with selection of optimum overlaying condition.

• Journal of Welding and Joining
• /
• v.15 no.5
• /
• pp.92-103
• /
• 1997

The purpose of this study is to improve the wear resistance and hardness of Al alloy by making a formation of the thick surface hardening layers. The thick surface hardening layers were formed by PTAW(Plasma Transferred Arc Welding), with the addition of metal powders (Cu), ceramics powders (NbC, TiC), and mixture powders (Cu+NbC) in Al alloy (A1050, A5083). Mechanical properties of overlaid layers (wear resistance, hardness) were investigated in relation to the microstructure. The results obtained are summarized as follows: The depth of penetration was increased with increasing powder feeding rate. It is considered that these increase were due to the thermal pinch effect by the addition of powders, especially, for the Cu powders, were due to the heat of reaction with the matrix. The hardness and wear resistance of overlaid layers were improved with increasing powder feeding rate. For the Cu powders, it is considered that these increase were due to the increase of the formation of ${\theta}(CuAl_2)$ phase with increasing feeding rate of Cu powers.