• Journal of the Korean Society for Nondestructive Testing
• /
• v.30 no.5
• /
• pp.464-470
• /
• 2010

The integrity of the industrial equipment in use under high temperature and high pressure must be assessed by regularly measuring the degraded mechanical properties during service time. In order to nondestructively monitor the degraded mechanical properties of industrial equipment, a measuring method of the reversible permeability(RP) using surface type probe is presented. The method for measuring the RP is based on that RP is the differential value of hysteresis loop. The RP is exactly the foundation hatmonics induced in a detecting coil measured by lock-in amplifier tuned to a frequency of the alternating perturbing magnetic field. The peak of RP is measured around the coercive force. Steel material used in this work was 12Cr ferritic heat resisting steel. The eleven kinds of samples aged during different times under same temperature ($700^{\circ}C$) were prepared. Peak interval of reversible permeability(PIRP), Vickers hardness, and tensile strength measured for the aged samples decreased abruptly for short aging time (below 500 h), but the change became small at a long aging time. Vickers hardness and tensile strength linearly decreased as RIRP decreased, so the degraded mechanical properties of 12Cr ferritic heat resisting steel could be nondestructively evaluated by measuring RIRP.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.3
• /
• pp.267-274
• /
• 2002

This research is described on the applicability of a electrochemical techniques for evaluating nondestructive material degradation with various polarization characteristics for Cr-Mo-V steel. The applied electrochemical technique is anodic polarization test which are widely used to evaluate the corrosion rate and/or sensitization at depleted zone of strengthening elements mainly caused by thermal experience for stainless steels. The evaluation of material degradation is performed by small punch test which has been well known as micromechanics test method using specimen size of $10{\times}10{\times}0.5mm$. The 1,000hrs aged material at $630^{\circ}C$ shows the highest material degradation$({\Delta}[DBTT]_{SP})$, but the 2,000hrs and 3,000hrs aged materials show the decrease of ${\Delta}[DBTT]_{SP}$ as aging time increases. It is observed that the difference of current density $({\Delta}I_{FP}\;and\;{\Delta}I_{SP})$.