• International Journal of Highway Engineering
• /
• v.14 no.1
• /
• pp.17-24
• /
• 2012

This study evaluated the performance of Korean epoxy asphalt mixtures using several laboratory tests. Four types of epoxy asphalt mixtures were manufactured based on 13mm dense graded asphalt mixtures: three Korean and one Japanese epoxy asphalt mixtures where 20% or 40% of asphalt binder was replaced by epoxy resins. Curing time was determined as 3 and 6 hours for the mixtures containing 40% and 20% of epoxy resins, respectively. From the laboratory tests including wheel tracking, indirect tension fatigue, bending beam, and moisture susceptibility tests, it was concluded that the epoxy asphalt mixtures had superior performance than conventional asphalt mixtures except moisture susceptibility. Also, the performance of the Korean epoxy asphalt mixtures was comparable to the Japanese mixtures. Thermal coefficient, bond strength, and indirect tension tests were conducted to examine the applicability of the Korean epoxy asphalt mixtures to concrete repair. Its adhesion was strong enough to be bonded to surrounding concrete materials and its tensile strength was comparable to the concrete, but thermal expansion coefficient was 5 times greater than the surrounding concrete.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.37 no.6
• /
• pp.1043-1051
• /
• 2017

Asphalt overlay on deteriorated concrete pavement has a problem of early damage due to reflective cracking. There is a need for a new method capable of reducing reflection cracking and ensuring the durability of pavement. The purpose of this study was to obtain durability of asphalt overlay with stress absorbing membrane interlayer (SAMI) using epoxy asphalt binder. The tensile performance, durability, water resistance and bonding performance of Epoxy-SAMI were evaluated by various tests. As a result of tests, Epoxy-SAMI meets the quality standard of the bridge waterproofing material. The repeated direct tensile test was carried out to investigate the effect of reflective cracking reduction. When the Epoxy-SAMI was applied, it had 1.2~1.56 times higher reflective cracking resistance than PSMA asphalt concrete with the thickness of 10cm even if the section thickness decreased. 4-point bending beam test results showed the number of fatigue failures increased 7.5 times when Epoxy-SAMI was applied. The Epoxy-SAMI was found to be effective in improving the durability of the asphalt pavement overlay because it serves to prevent reflective cracking, increase lifespan, and function as a waterproof layer.