• Journal of the Korean Ceramic Society
• /
• v.28 no.3
• /
• pp.189-196
• /
• 1991

Si(OC2H5)4, commercial AlN and Y2O3 powder were used as the precusor of Si3N4, AlN, Y2O3, respectively. After Si3N4 powder was synthesized by carbothermal reduction and nitridation at 135$0^{\circ}C$ for 13h in N2 atmosphere, characteristics of synthesized powder and the ceramics sintered at 178$0^{\circ}C$ for 1h under 30MPa were investigated. In order to evaluate the reliability of sintered body, Weibull modulus was investigated. Premixing of carbon black as a reduction agent had no effect on Si(OH)4 formation, and Si3N4 powder synthesized from Si(OC2H5)4 was $\alpha$-Si3N4 single phase. Mechanical properties of sintered body were measured as follows : flexural strength ; 750MPa, fracture toughness ; 3.71Mn/3/2, hardness : 17.4GPa, thermal shock resistence temperature ; $600^{\circ}C$. Flexural strength at room temperature was 750MPa and was retained up to 110$0^{\circ}C$. The Weibull modulus of sintered body was 10.7.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1992.04a
• /
• pp.33-34
• /
• 1992

현재 이용되는 막들은 대부분 유기계 혹은 고분자계로 열적인 안정성이 적고 내약품성이 낮다. 그래서 본 실험에서는 내열, 내약품성이 우수한 무기기와 유기기를 조합하여 복합막을 제조하려 시도하였다. 이때 유-무기 복합상의 반응은 졸-겔 법을 이용하였는데 이 졸-겔 법이란 출발물질인 금속알콕사이드를 용액상에서 가수분해하여 졸을 얻고 축합반응을 통해 겔을 형성하여 무기고분자를 제조하거나 소결하여 필름, 분말, 섬유상, 괴상 등의 다양한 형태로 산화물을 제조하는 공정이다. 이는 분자적 차원에서 혼합하여 반응하므로 산화물간의 반응보다 반응성의 입장에서 훨씬 유리하며 또한 용액상에서 저온반응 하므로 기존에는 유기-무기기를 조합하는데 존재하는 문제를 해결 할 수 있다.

• Korean Journal of Materials Research
• /
• v.6 no.2
• /
• pp.182-187
• /
• 1996

물과 에탄올의 혼합용액에 HCI을 촉매로하여 금속알콕사이드의 가수분해로부터 코오디어라이트 분말을 제조하였다. 이때 HCI/precursor 몰비로써 촉매의 양을 조절하였다. 건조분말 중의 용매를 제거하기위해 80$0^{\circ}C$에서 3시간 하소처리하였다. 이들 하소된 분말에 대하여 시차열분석과 X-선회절분석을 행한 결과-92$0^{\circ}C$에서 $\mu$-cordierite, -103$0^{\circ}C$에서 $\alpha$-cordierite 결정상의 생성을 확인하였다. 또한, 하소분말을 가압성형한 후 130$0^{\circ}C$에서 4시간 열처리한 결과 HCI양에 따라 기공율 19.45-25.45%, 부피비중 2.06-1.70g/㎤, 유전상수 1.38-3.38 범위의 소결체를 얻었다. HCI양이 증가할수록 기공율은 증가한 반면에 비유전상수와 부피비중은 감소하였다.

• Journal of the Korean Ceramic Society
• /
• v.38 no.7
• /
• pp.660-666
• /
• 2001

수용계를 이용하여 졸겔법으로 중성 TiO$_2$졸을 제조하였다. 용매로 에탄올을 사용한 경우 메탄올에 비해 졸의 안정성이 우수하였다. 졸 제조시 에탄올을 사용하면, 메탄올을 용매로 사용할 경우보다 중심 금속에 부착되는 알콕시족의 크기가 작아져서 티타늄알콕사이드의 가수분해 속도가 빨라지기 때문이다. TTIP : AcAc : EtOH : $H_2O$ : PEG : HCl의 몰비가 1 : 1 : 8 : 50 : 0.5 : 0.15의 조성을 갖는 에탄올 용매 졸은 30일까지도 안정한 상태를 유지하였고 코팅성이 양호하였다. 10회 반복 침지, 건조 및 50$0^{\circ}C$에서 열처리된 두께 약 $1.5mu extrm{m}$의 TiO$_2$박막은 표면이 균질하고 치밀한 미세구조를 보였다. 제조한 TiO$_2$박막은 가시광선 영역에서 약 70%의 투과도를 나타내었다.

• Journal of the Korean Ceramic Society
• /
• v.30 no.3
• /
• pp.243-249
• /
• 1993

Coated type Al2O3-SiC composite powders were synthesized by surface modification method. Transformation temperature to $\alpha$-Al2O3 of Al2O3 monolith was 115$0^{\circ}C$ whereas increased to 1200, 1250, 130$0^{\circ}C$ with increment of SiC content to 5, 15, 25wt%. Transformation temperature to $\alpha$-Al2O3 was lowered by $\alpha$-Al2O3 seeding. FTIR data analysis and electron micrographs showed that Al2O3 particles were effectively coated on SiC particles.

• Journal of the Korean Ceramic Society
• /
• v.28 no.7
• /
• pp.568-576
• /
• 1991

The powder characterization and sintering behavior of alkoxide-derived alumina powders prepared by esterification were investigated. The dried powders were calcined at 700$^{\circ}C$, 900$^{\circ}C$, 1080$^{\circ}C$, 1170$^{\circ}C$ for 1 h. and the resulting crystalline forms were amorphous, {{{{ gamma }} phase, {{{{ theta }}+{{{{ alpha }} phase, and {{{{ alpha }} phase, respectively. The sinterability was best in the case of being calcined at 1170$^{\circ}C$. It was most effective to disperse sintering additive in the initial stage from which acetate was formed. At 1600$^{\circ}C$ for 4 h, 98.5% of relative density was obtained when MgO and Fe2O3 were simultaneously doped, and dense sintered body whose density was near theoretical value was obtained when heating schedule was controlled.

• Journal of the Korean Ceramic Society
• /
• v.30 no.2
• /
• pp.123-130
• /
• 1993

Dispersed type Al2O3-SiC composite powders were synthesized from Al-isopropoxide (Al(i-OC3H7)3) and Si(OC2H5)4 precursors by hydrolysis of mixed alkoxides and carbothermal reaction method. The characteristics of the synthesized (dispersed type) Al2O3-SiC composite powders were investigated using XRD, SEM, TEM, BET and particle size analyzer. Carbothermal reaction to produce Al2O3-SiC composite was completed in 10h at 135$0^{\circ}C$ on 3~4㎤/s (0.21~0.28cm/s) of H2 flow rate and about 1/1 of carbon/oxides(=SiO2＋Al2O3) molar ratio. The synthesized powders were observed to have the mean particle size range of 0.4~1.26${\mu}{\textrm}{m}$ and showed finer particle size with increasing SiC content.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.76-76
• /
• 2010

유기박막트랜지스터의 특성을 개선하기 위해서는 유기반도체와의 좋은 접합과 유전상수가 주요한 요인으로 작용한다. 무기 산화물 전구체와 유기고분자를 이용하여 유기 고분자의 단정인 낮은 유전율을 개선하였다. 스핀코팅 방법이 아닌 딥코팅 방법을 이용하여 절연막 두께를 10nm정도로 낮추어 구동전압을 개선하였으며 무기 절연체의 높은 누설전류 또한 그 특성이 개선되어 우수한 절연 특성을 보였다. 유-무기 복합체를 이용한 게이트 절연막과 펜타센을 이용한 유기박막트랜지스터의 구동전압은 1V정도에서 구동가능하며, 점멸비, 이동도 모두 개선된 결과를 보였다.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.499-504
• /
• 1994

PbTiO3 thin films were prepared by sol-gel spin coating method using metal alkoxide and diethanolamine (DEA). The precipitation of the PbTiO3 sol occurred at pH 7.3 with HNO3 addition, regardless of the amount of DEA. The gelation time of the PbTiO3 sol was reduced with increasing amount of HNO3 and/or water. When the PbTiO3 films prepared by 0.2 molar coating solution were annealed at $650^{\circ}C$ for 30 min, dense and single phase perovskite films were obtained. Dielectric constant and loss tangent of the film were 239 and 0.01 at 1 kHz, respectively.

• Journal of the Korean Ceramic Society
• /
• v.32 no.10
• /
• pp.1212-1218
• /
• 1995

Al2O3-coated SiC composite powder and mechanically mixed Al2O3-SiC composite powder were synthesized using Al-isopropoxide and commercial SiC as the starting materials. Experiment results showed that the sinterability of Al2O3-coated SiC composite powder was more improved than the mechanically mixed Al2O3-SiC composite powder by the effect of homogeneous coating of alumina around SiC particles. Hence, the mechanical properties of the former was also much more improved than the latter.