• Journal of Advanced Marine Engineering and Technology
• /
• v.18 no.2
• /
• pp.41-53
• /
• 1994

In this paper, rotating-bending fatigue tests of the SiC-whisker- reinforced 6061-T6 aluminum alloy and 6061-T6 alumiunm alloy made by power metallurgy were carried out to investigate the fatigue characteristics of plain and notched specimens at room temperature. The fatigue mechnisms in both materials were clarified through successive surface observations using the plastic replica method. In the case of the SiC-whisker-reinforced composites, there are whisker rich and poor zones and the fatigue crack is nucleated from the end of whiskers near the boundary. On the other hand, in the case of the 6061-T6 aluminum alloy, the fatigue crack is nucleated from defects and propagates by shear. Moreover, the results were discussed based on linear notch mechanics.

• Journal of the Korean Society for Railway
• /
• v.3 no.2
• /
• pp.92-99
• /
• 2000

Composites are very useful material for light train carbody due to its high specific strength and lightweight characteristics. The composites, called 3-D board, are developed with a special stitching method. In this process, the glass fiber fabrics of skin material and foam core material are stitched together with glass fiber thread. The glass thread in Z-axis turns into FRP form. The conventional delamination problem can be solved with 3-D sandwich structure. In addition, with the lower density of foam, the weight of the panel and the operation expenses can be highly reduced. To evaluate the usefulness of the 3-D board, the double-deck light train carbody is studied. The stress analyses are carried out under various loads and boundary conditions with FEM Code, ANSYS. On comparing with the aluminum carbody, 3-D board carbody can be reduced by about 2 ton for the total weight of carbody.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.3
• /
• pp.69-75
• /
• 1997

A A12024-T3 plate has been reinforced with AFRP to be a Hybrid-Composite, APAL. The fatigue life of the APAL has been investigated. The effects of bonding surface, numbers of AFRP bonded and AFRP orientation on fatigue life have been compared with A12024-T3 plate. Fatigue life of APAL has been remarkedly increased compared with that of A12024-T3 plate. The fatigue life has depended on bonding surface and AFRP orientation, but no relationship could be found with numbers of AFRP laminates.

• Journal of Power System Engineering
• /
• v.15 no.5
• /
• pp.77-82
• /
• 2011

SiC particulate reinforced Al matrix composites with different SiC volume fractions were fabricated by thermal spray process. And the dry sliding wear test were performed on these composites using the applied load of 10 N, rotational speed of 30 rpm, radius of rotation 15 mm. Wear tracks on the Al/SiC composites were investigated using scanning electron microscope(SEM) and energy dispersive spectroscopy (EDS). It was observed that wear behavior of Al/SiC composites and formation of MML was changed dramatically according to reinforcement volume fraction.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.251-255
• /
• 2005

본 연구는 한국형 틸팅 차량의 하이브리드 복합재 차체에 대한 비용 모델링과 전주기 평가{LCA}를 기존 차체 재질인 스틸 및 알루미늄 재질과 병행하여 수행였다. 원자재 생산에서 차체제작, 수명이 끝나는 시점까지의 사용에 대한 모든 단계에서의 비용을 분석했다. 개발과정을 거쳐 향후 양산 예정인 5년 동안 년간 90대정도의 생산량에 대해 금속 차체, 2종의 복합재 차체에대해 비교하였다. 2종의 복합재 차체는 하이브리드 스틸-복합재 구조와 전체 복합재 차체를 나타낸다. 또한, 이 두 경우 모두에 대해 오토클레이브, 진공 성형, 레진 인퓨젼 공법의 성형에 대해 분석하였다. 제작시의 모든 성형 공법에 대해 하이브리드 차체는 전체 복합재 차체보다 4${\sim}$6 % 비용이 낮았다. 전체 복합재 차체의 경우, 레진 인퓨젼의 경우가 오토클레이브에 대해서는 11%낮은 가장 낮은 제작 비용이 소요되었다. 비용-전주기 분석을 통해 전체 복합재 차체는 가장 높은 제작비용이 소요되고 사회 경제학적 측면에서 전체 전주기 비용과 환경영향은 단순 차량 구입 비용보다 더 중요한 변수이며 전체 복합제 차체가 분명한 최적의 해답 임을 확인하였다.

• Composites Research
• /
• v.18 no.2
• /
• pp.1-12
• /
• 2005

Fracture behaviors of single-edge-notched monolithic aluminum plates and glass fiber/aluminum laminates under tensile loadings have been studied using acoustic emission(AE) monitoring. AE signals from monolithic aluminum could beclassified into two different types. For glass fiber/aluminum laminates, AE signals with high amplitude and long duration were additionally confirmed on FFT frequency analysis, which corresponded to macrocrack propagation and/or delamination. AE source location determined by signal arrival time showed the zone of fracture. On the basis of the above AE analysis and fracture observation, characteristic features of fracture processes of single-edge-notched glass fiber/aluminum laminates were elucidated according to different fiber ply orientations and fiber/aluminum lay-up ratios.

• Korean Journal of Materials Research
• /
• v.6 no.12
• /
• pp.1170-1178
• /
• 1996

저용융점을 가진 새로운 무기 접착제인 단사정 HBO2가 알루미나 분말의 선택적 레이저 소결을 하기 위한 접착제로서 개발되었다. 이것을 이용하여 만들어진 green body는 현재까지 알루미나 분말의 선택적 레이저 소결을 위하여 개발된 다른 무기 접착제들인 알루미늄(Ai)과 Ammonium Phosphate(NH4H2PO4)을 이용하여 제조된 것에 비교하여 훨씬 높은 굽힘 강도를 가지고 있고 또 정밀도가 우수하였다. Green Body는 후속의 열처리를 받음으로써 저밀도 단상 세라믹 AI18B4O33과 다상 세라믹 복합재료 AI2O3-AI4B2O9으로 된다. AI18B4O33과 AI4B2O9의 결정립의 모양은 휘스커 구조와 유사하였다. 재료인자와 가공변수가 이 세라믹의 기계적 및 물리적 성질에 미치는 영향이 조사되었다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.17.1-17.1
• /
• 2009

발포금속은 1948년에 Sosnik에 의해 알루미늄에 수은을 증발시키는 방법으로 발포 알루미늄을 제조한 이래, 1951년 Elliot에 의해 진보된 방식인 발포 매개체를 용탕에혼입하는 방법으로 발포금속을 제조하기 시작하였다. 현재 이들 선진국가의 생산방법 및 현황은 균질 기공의 조절, 연속주조 방식과 원가절감, 그리고 제조기술의 진보를 통하여 다양한 분야에 적용되고 있다. 그러나 실용화를 위해서는 요구특성을 만족하고 동시에 가격 경쟁력을 가진 제조기술의 보유 및 개발과 독특한 특성을활용한 새로운 적용 분야의 개척이 필요하다고 생각되며, 이를 위해 Harvard, MIT, Aachen, HMI 등 구미 유수 대학과 NASA, 미국방성등의 연구기관, ERG, 신강(新鋼) wire등 산업체를 중심으로제조 및 특성평가에 관한 기초연구와 활용방안이 활발히 모색중에 있다. 그리고 일부 자동차 생산 업체를중심으로 발포금속을 적용한 초경량, 에너지 절감형의 자동차 부품 소재,항공기 방열판 등에 대한 연구가 활발하게 진행되고 있다. 특히 금속 기체의 GASAR 공법은 Lotus 공법으로 Osaka 대학에서 개발되어 열교환기, 항공기, 방열기 등으로 응용이 확대되고 있다 국내에서 완제품생산은 실내장식용 복합패널로서 한소 프라임이 운영상의 문제로 생산을 중단하였으며, 유닉슨(주), 금강(주)에서 Batch식, 금성산업에서 Pot식이 일부 생산 및 연구가 진행되었으나 현재는 본연구실의 협조로 (주) 폼텍에서 발포패널을 주로 생산하고 있고 (주)드림메탈과 (주)아크로폼텍에서일부 생산되고, (주)동일알루미늄에서는 폐 scrap을 이용한 발포 Al 제조가 연구단계에 있다. 생기원에서는 분말 가열 흡음패널이 개발되었으나 강도와 내열성이 낮아 이들 특성을 향상시크는 연구가 진행중이다. 이들 제품은 성능상으로는 동양강판의 흡음패널과 KIMM의 필터용은연구개발이 낮은 수준이며, 본 연구팀과 공동 개발한 (주)폼텍의 복합패널은 10여 가지의 실용특허로 건축마감재로서 오히려 선진국수준을능가한 상태이다, 한편, 발포금속 기능성 개발은, 이들이 가지고 있는 우수한 특성 때문에 군수용으로부터 민수 산업용까지 전분야에 적용이 가능한 소재이므로 수요처를확장하고 있으므로 제품의 균질성, 안정성과 기능성 개발 향상을 위해 지속적이고 체계적인 연구가 필요하다고 생각된다.

• Fire Science and Engineering
• /
• v.26 no.6
• /
• pp.85-91
• /
• 2012

To reduce human life and property damage at the fire in a building, it is most critical to control flame spread in the early stage. Fire spread prevention measure generally includes fire resistance performance securing of structure member in the arson zone and use limitation based on combustion performance of finishing material. The latter is most fundamental fire safety design to determine flame spread, but domestic combustion test determines combustion performance by specimen sized fire test method. Thus, there are many restrictions in the determination of combustion performance by composite material such as sandwich panel. Especially, outer finishing material uses a variety of composite material such as dry bit, aluminum composite panel, and metal panel compared to inner finishing material. Therefore, this study would determine vertical fire spread features by a full scaled fire experiment through the test method of ISO 13785-2, an international test standard.

• Composites Research
• /
• v.29 no.4
• /
• pp.209-215
• /
• 2016

The failure of composite sandwich structures with thickness and material variation was studied. The main body of the structure is sandwich plate made of the carbon composite face and Aluminum honeycomb core. It is connected with composite laminated flange without core through transition region of tapered sandwich panel with foam core. Tension and compression tests were conducted for the total of 6 panels, 3 for each. Test results showed that the panels under compression are vulnerable to the face failure along the material discontinuity line between two different cores. However the failure load of which panel does not show such failure can carry 16% more load and fails in honeycomb core and face debonding. For the tensile load, the extensive delamination failure was observed at the corner radius which connects the panel and the flange. The average failure load for compression is about 7 times the tensile failure load. Accordingly, these sandwich structures should be applied to the components that endure the compressive loadings.