• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.5
• /
• pp.144-152
• /
• 2007

This study investigated the failure mechanism of RC beams strengthened with AFRP sheets. Total 5 half-scale RC beams were constructed and tested to estimate the effectiveness of various methods to prevent the debonding failure of AFRP sheets. From the experimental results, it was found that increasing bonded length or end U-wrappings does not prevent debonding failure. On the other hand, the beams with center U-wrappings and shear-keys reached the ultimate state with their sufficient performance. The center U-wrappings tended to control debonding of the longitudinal AFRP sheets because the growth of the longitudinal cracks along the edges of the composites was delayed. In case of shear-keys, it was sufficient to eliminate debonding and the beams failed by AFRP sheets rupture due to the sufficient bond mechanism.

• Magazine of the Korea Concrete Institute
• /
• v.11 no.2
• /
• pp.105-113
• /
• 1999

This study was conducted to evaluate the structural behaviors of Aramid fiber sheet reinforced slabs. Seven concrete slabs with $45{\times}8.5{\times}200cm$ were made for this experiment one slab with out being reinforced completely loaded until failure and the maximum load was obtained from this test. 70% of the maximum load was applied to 3 Aramid fiber sheet reinforced slabs after cracking and to the rest of 3 Aramid fiber sheet reinforced slabs without loading and cracking. Test results shows that maximum loading flexural rigidity and ductility for the Araimid fiber sheet reinforced slabs after initial cracking are similar as those for the Armied fiber sheet reinforced slabs without loading and cracking.

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.4 s.97
• /
• pp.13-18
• /
• 1999

섬유강화금속적층재(Fiber Reinforced Metal Laminates. FRMLs)는 고강도금속과 섬유강화복합재료(Fiber Reinforced Composite Materials)를 적층한 새로운 종류의 하이브리드 재료이다. 국산 아라미드 섬유인 헤라크론(Heracron, 코오롱)과 국내 복합재료 제작기술(한국화이바)을 사용하여 섬유강화금속적층재를 제작하고, 이를 HERALL(Heracron Reinforced Aluminum Laminate)이라 명명하였다. HERALL(Heracron Reinforced Aluminum Laminate)의 피로균열성장특성 및 피로균열진전 방해기구를 ARALL(Aramid-fiber Reinforced Aluminum alloy Laminates) 및 Al 2024-T3과 비교해석하였다. HERALL과 ARALL은 균열진전을 저지하는 아라미드 섬유로 인해 뛰어난 피로균열성장특성 및 피로저항성을 보여주었다. 아라미드 섬유의 균열브리드징으로 인한 $K_{max}$의 감소량과 Al 2024-T3의 균열닫힘으로 인한 $K_{max}$의 증가량을 구할 수 있는 응력-COD법을 사용하여 실제로 균열성장에 영향을 준 유효응력확대계수범위를 측정하였다. 균열선단으로부터 균열을 가공하면서 COD 변화량을 측정하여 균열브리징 영역을 구하였다.

• Composites Research
• /
• v.36 no.6
• /
• pp.383-387
• /
• 2023

Carbon fiber-reinforced composites have excellent mechanical properties. However, the fracture toughness is a disadvantage due to brittle failure mode. The fracture toughness can be enhanced using hybridization with large-elongation fibers. In this study, polyamide (aramid) fibers are hybridized with carbon fiber with various stacking sequences. As a result, the Izod impact strength was enhanced by 63% with 25% aramid fiber hybridization. It is also shown that there is an optimal point in laminated composite hybridization, [CF/CAF₂/CF]_s stacking sequence.

• Composites Research
• /
• v.26 no.2
• /
• pp.129-134
• /
• 2013

The strength of adhesive joints employed in composite structures under cryogenic environments, such as LNG tanks, is affected by thermal residual stress generated from the large temperature difference between the bonding process and the operating temperature. Aramid fibers are noted for their low coefficient of thermal expansion (CTE) and have been used to control the CTE of thermosetting resins. However, aramid composites exhibit poor adhesion between the fibers and the resin because the aramid fibers are chemically inert and contain insufficient functional groups. In this work, electrospun meta-aramid nanofiber-reinforced epoxy adhesive was fabricated to improve the interfacial bonding between the adhesive and the fibers under cryogenic temperatures. The CTE of the nanofiber-reinforced adhesives were measured, and the effect on the adhesion strength was investigated at single-lap joints under cryogenic temperatures. The fracture toughness of the adhesive joints was measured using a Double Cantilever Beam (DCB) test.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.6
• /
• pp.201-210
• /
• 2023

This study is to evaluate the ductility strengthening effect of aramid fiber sheets on piloti-type structures. Two piloti-type structure specimens were prepared and tested under statical cyclic lateral loads. The ductility strengthening effect was validated from the analysis of lateral load-displacement relationship, displacement ductility ratio, work damage index and torsion behavior. Test results showed that the post-peak behavior of piloti-type structures with columns strengthened with aramid fiber sheets tended to be ductile resulting from preventing shear failure and minimizing torsion due to the effective lateral confinement of column concrete by aramid fiber sheet. Consequently, the displacement ductility ratio and work damage index of piloti-type structures with columns with strengthened with aramid fiber sheets were 4.63 and 42.81 times higher than those of non strengthened piloti-type structures.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2011.03a
• /
• pp.106-106
• /
• 2011

아라미드 소재는 내열성, 난연성이 우수하고 일반 섬유보다 강한 물성을 지닌 수퍼섬유 소재의 하나로 보호복이나 군용, 특수의류 분야에 많은 용도전개가 가능하나 유리전이온도 및 결정화도가 상대적으로 높아서 난염성 섬유소재로 염색메카니즘의 명확한 규명이 없다. 따라서 본 연구에서는 아라미드 소재(m-Aramid, p-Aramid)의 염색방법에 대한 연구로, 캐치온 염료를 이용하여 팽윤제 종류 및 농도, 염색온도 조건, 중성염 효과 등 염색조건에 따른 염색특성을 알아보았다. 또한 분산염료 및 기타 염료 등의 적용을 통하여 다양한 염료적용 가능성에 대해 연구를 진행하였다.

• Composites Research
• /
• v.25 no.3
• /
• pp.82-89
• /
• 2012

This paper investigated the composite materials application examples and trends in the future to the solid rocket motor cases. The motor case must be stiff and tolerate at the high pressures, and light weight. In accordance to these kind of requirements, the composite materials showed the adaptable efficiency, and glass fibers, aramid, carbon fibers are applied to orderly. The comparison of the motor case efficiencies of the D6AC steel alloy, aramid, carbon fibers results in the carbon fibers best. Also the capacity of the payload will be increased more than 20% by using the high strength ones.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.5
• /
• pp.151-158
• /
• 1998

최근 들어 구조물을 보강하는 방법으로 강판 또는 섬유쉬트를 외부에 부착시키는 공법이 많이 사용되고 있다. 섬유쉬트 중에서 가장 널리 사용되는 것은 탄소섬유쉬트이지만, 성능면에서 뒤지지 않고 가격면에서는 오히려 유리한 아라미드섬유쉬트에 관한 연구는 전무한 실정이다. 본 연구에서는 아라미드섬유쉬트로 휨보강한 RC보의 파괴양상 및 강도성능, 변형성능을조사하고, 여섯 개의 보강변수에 대한 보강효과를 조사하였다. 인장철근비, 보강길이, 보강겹수, 앵커볼트 정착 유무가 각각 다른 16개의 실험체와 밑면 마감처리 및 부재손상 여부가 다른 2개의 실험체, 그리고 이들 보강 실험체의 비교 근거가 되는 비보강 실험체 2개를 실험하여 그 특성을 연구하였다. 실험결과, 보강성능과 파괴양상에 가장 큰 영향을 미치는 변수는 보강길이로 나타났다. 보강겹수도 어느 정도의 영향을 미치는 것으로 나타났으나 그외 다른 변수들의 영향은 미비한 것으로 판단된다.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2011.03a
• /
• pp.29-29
• /
• 2011

아라미드 섬유는 열에 강한 튼튼한 방향족 폴리아마이드 섬유이다. 아마이드는 "85%이상의 아미드(CO-NH)기가 두 개의 방향족 고리에 직접 연결된 합성 폴리아미드로부터 제조된 섬유"로 정의된다. 아라미드 섬유는 크게 파라계와 메타계로 대별되는데 본 연구에서 사용한 파라계 아라미드는 인장강도, 강인성, 내열성이 뛰어나며 고강력 고탄성률을 지니고 있다. 일반적인 유기 섬유와는 다른 우수한 성질을 바탕으로 부직포, UD laminatig, staple 등의 형태로 크게 섬유보강 고무 복합재료 등의 각종 복합재료, 로프, 케이블, 방탄방호용과 같은 산업자재의 용도로 자동차, 우주항공, 정보통신, 국방, 등 다양한 관련 산업분야에서 사용이 확대되고 있는 고부가 소재이며 가격대비 성능비가 우수하기 때문에 세계적으로 산업용 섬유 및 초고성능 섬유시장에서 비중이 증가될 것으로 예상되고 있다. 본 연구에서는 Para-Aramid 필라멘트를 이용하여 ATY를 생산할 때 제조공정조건에 따른 ATY 물성을 알아보고 고강도를 요구하는 방화복, 고무 보강용 섬유 등의 소재에 맞는 ATY 사가공 최적공정조건을 도출하여 체계화된 data-base를 구축하여 생산성 향상 및 품질개선과 함께 산업자재용 직물개발에 응용하고자 한다. 아라미드를 ATY로 제조할 경우, 표면에 생기는 loop로 인하여 타소재와 접착시, 접착제 담지 성능이 향상되어 접착력이 상승되는 반면, 아라미드 ATY가 기존의 아라미드의 물성보다 저하되는 약점을 가지고 있으므로 이를 보완하기 위해 본 연구에서는 ATY 제조공정에서 중요 공정인자인 사속, heater 온도, over feed ratio를 변화시켜 시료를 제조하여 이들의 물성을 분석하여 최적의 물성을 갖는 ATY 사가공 공정을 도출함으로써 물성이 저하되는 문제를 보완 가능할 것으로 기대된다. 물성분석은 강신도, 초기탄성률을 각각 측정하여 인장특성을 확인하였으며, 습열수축률과 건열수축률을 측정하여 시료의 열수축률에 대해 측정을 하였다. 표면의 루프 발현 정도를 보기 위하여 Crimp Rigidity(CR%), 형태 불안정성(instability)등을 측정하였으며, 영상 현미경 시스템을 사용하여 ${\times}40$ 배율로 표면특성을 측정하였다.