• 열처리공학회지
• /
• 제20권5호
• /
• pp.243-249
• /
• 2007

The age hardening behavior and mechanical properties of an extruded Al-Zn-Mg-(Cu)-0.1 wt.%Sc alloy were investigated with the Sc addition and ageing temperature. The results showed that the $Al_3Sc$ compounds were formed by Sc addition and distributed preferentially along the extrusion direction. The age hardening of Al-Zn-Mg-Cu-0.1 wt.%Sc alloy which was treated by T6 process was more significant than that of Al-Zn-Mg-0.1 wt.%Sc alloy. The tensile property of Al-Zn-Mg-Cu+0.1 wt.%Sc alloy was also higher than that of Al-Zn-Mg-0.1 wt.%Sc alloy, which is 691 MPa and 584 MPa in strength and 9% and 11% in elongation, respectively.

• 대한의용생체공학회:의공학회지
• /
• 제17권2호
• /
• pp.247-254
• /
• 1996

The relationship between the isothermal age-hardening behavior and the phase transformation in the commercial dental Au-Ag-Cu-Pd alloy was investigated Age-hardening was mostly attributed to the lattice distortions of the supersaturated w phase resulting from the transformation to the metastable phasel which were more distinct at lower aging temperature. The lattice distortions resulting from the transformation of the metastable phases to the equilibrium phases also made a contribution to the age-hardening.

• 열처리공학회지
• /
• 제24권4호
• /
• pp.193-198
• /
• 2011

Effect of CaO addition on age hardening response has been studied by using optical microscopy, scanning electron microscopy and differential thermal analysis in AZ91 and CaO-containing ECO-AZ91 alloys. After solution treatment, the ${\beta}$($Mg_{17}Al_{12}$) phase formed during solidification mostly disappeared in the microstructure in the AZ91 alloy, whereas numerous ${\beta}$ precipitates containing Ca were still observed in the ECO-AZ91 alloy due to its enhanced thermal stability. The ECO-AZ91 alloy showed the delayed peak aging time and higher peak hardness compared with those of the AZ91 alloy. The activation energies for ${\beta}$ precipitation calculated by means of Kissinger method increased from 71.4 to 85.6 kJ/mole by the addition of CaO, which implies that CaO plays a role in reducing ${\beta}$ precipitation rate in the AZ91 alloy.

• 한국주조공학회지
• /
• 제12권5호
• /
• pp.397-402
• /
• 1992

The effect of the solution & aging treatment on the tensile strength, yield strength, elongation, reduction of area, hardness was studied in the 17-4 PH stainless steel. SEM pictures were also taken in order to examine the fracture surfaces and precipitated particles. X-ray diffraction patterns for the heat treated samples were also observed. Mechanical properties of the heat treated samples were superior to those of as cast samples. Tensile strength, yield strength, hardeness decreased with the increase of aging temperature. On the other hand, elongation and reduction of area increased as the aging temperature increased.

• 한국주조공학회지
• /
• 제19권5호
• /
• pp.433-439
• /
• 1999

Rapidly solidified Mg-Al-Si base alloys containing Ca were obtained by melt spinning. The melt-spun ribbons were aged isochronally or isothermally to investigate age hardening phenomena and microstructural change according to the alloy composition. Age hardening occurred after aging at $200^{\circ}C$ for 1h mainly due to the precipitation of $Al_2Ca$ and $Mg_2Ca$, which have coherent interfaces with the matrix. With the increase of Ca content, the hardness values of the alloy ribbons were increased. Among the alloys, Mg-10Al-2 Si-3Ca alloy showed a good thermal stability at elevated temperature.

• 한국재료학회지
• /
• 제4권6호
• /
• pp.651-661
• /
• 1994

급냉응고법과 기계적합금화를 병행하여 자동차 산업용 부품에 널리 사용되고 있는 AC4A 합금에 열적으로 안정한 $SiC_p$세라믹 입자를 첨가하여 가공경화 및 미세균일화에 의한 분산강호 효과를 갖는 복합재료를 제조하고, 그에 따른 기계적특성을 조사하여 다음과 같은 결과를 얻을 수 있었다. 420분간 기계적합금화를 시켰을 때 10~20$\mu \textrm{m}$ 정도의 미세하고 균일한 구형의 복합분말을 얻을수 있었으며, 이 상태에서 정상상태를 의미하는 포화 경도값이 나타났다. 기계적합금화에 따른 분말의 X-선 회절시험에서 기계적 합금화 시간에 따라 결정립 미세화와 불균일 변형에 의해 강도가 떨어지고, 회절폭이 넓어진다. 분말 압출재의 시효경화는 1000분 시효에서 최대 경도값을 나타낸다. 인장시험에 있어서 압출재는 주조재에 비해 2배 이상의 인장값을 얻을 수 있었으며, $500^{\circ}C$에서도 우수한 인장값을 얻을 수 있었다.

• 한국주조공학회지
• /
• 제24권1호
• /
• pp.45-51
• /
• 2004

Fe and Si are common impurity elements in the aluminum alloys. In this investigation, the effects of the addition of Fe and Si on the age-hardening behaviors of the Al-Cu-Mn-Ti-Zr-Cd casting alloys were examined through hardness measurements, calorimetric techniques and observation of the transmission electron microscopy. The addition of Fe depresses the formation of GPII and ${\theta}'$, and thus retards the peak aging time and reduces the peak hardness of the Al-Cu-Mn-Ti-Zr-Cd alloys. On the contrary, the addition of Si accelerates the formation of GPII and ${\theta}'$ and thus accelerates age-hardening behaviors of the Al-Cu-Mn-Ti-Zr-Cd alloys.

• 한국재료학회지
• /
• 제25권9호
• /
• pp.468-474
• /
• 2015

Evaluations of the microstructure and mechanical properties of age hardenable Cu-2.0wt%Be alloy are performed in order to determine whether it can be used as a welding electrode for projection welding. The microstructure examinations, hardness measurements, and tensile tests of selective aging conditions are conducted. The results indicate that the aging treatment with the fine-grained microstructure exhibits better hardness and high tensile properties than those of the coarse-grained microstructure. The highest hardness value and high tensile strength are obtained from the aged condition of $300^{\circ}C$ for 360 min due to the presence of the metastable ${\dot{\gamma}}$ precipitates on the grain boundaries. The values of the highest hardness and tensile strength are measured as 374 Hv and 1236.2 MPa, respectively. The metastable ${\dot{\gamma}}$ precipitates are transferred to the equilibrium ${\gamma}$ precipitates due to the over-aged treatment. The presence of the ${\gamma}$ precipitates appears as nodule-like precipitates decorated around the grain boundaries. The welding electrode with the best aging treated condition exhibits better welding performance for electrodes than those of electrodes used previously.

• 한국재료학회지
• /
• 제17권12호
• /
• pp.648-653
• /
• 2007

Plasma electrolytic oxidation (PEO) treatment was performed on cast Mg-6 wt%Al alloy solution-treated at 693K for 16h and aged at 498K. The surface roughness, thickness, micro-hardness, wear and corrosion properties of coatings on solution-treated and aged Mg-6 wt%Al alloy were investigated. The coatings on aged Mg-6 wt%Al alloy had thinner layer and lower micro-hardness and wear resistance than the solution-treated Mg-6 wt%Al alloy. As the aging time increased, the thickness of coatings decreased while the surface roughness was almost no changed. In addition, the micro-hardness and wear property of coatings decreased with increasing the aging time unlike the uncoated Mg-6 wt%Al alloy showing the peak micro-hardness and the best wear property after aging for 16 h. However, the coatings on Mg-6 wt%Al alloy peak-aged for 16h revealed the best corrosion resistance in 3.5% NaCl solution, which was explained based on the microstructural characteristics.

• Journal of Welding and Joining
• /
• 제11권2호
• /
• pp.53-61
• /
• 1993

One of the most interesting and promising steel groups considered for the rocket motor case, aircraft and aerospace component is the maraging(martensitic plus aging) nickel steel, developed by International Nickel Company in 1960. This material attains a very high strength with good fracture toughness by simple heat treatments which do not involve a quenching. Full strength can be obtained by "maraging" at 480.deg. for 3 hours for the 18% Ni maraging steel. The effect of heat treatments was considered on the residual stress field of 18% Ni maraging steel weldments. In experiments, various heat treatments such as stress relieve heat treatment, aging and solution heat treatment were carried out of the GTA weldments and the residual stresses were measured by using the hole drilling method. Whereas the conventional pattern of residual stress shows the stresses to be maximum along the weld centerline with tensile stress extending into the heat affected zone, the pattern in maraging steels shows the centerline stress to be compressive. After welding, a series of aging, solution heat treatment and solution heat treatment plus aging treatment were carried out and the residual stresses were measured to reveal that these heat treatments almost completely remove the welding residual stresses.