• 한국재료학회지
• /
• 제8권3호
• /
• pp.274-279
• /
• 1998

0.05wt%C-Cu첨가열연강판에서 590MPa급을 가지며 10% pre-strain을 가한 후 780MPa급 이상을 가지는 Cu첨가형 열연강판의 최적 Cu 및 Mn첨가량 규명을 위해 경도 및 인장시험과 투과 전자현미경으로 조사하였다. Cu 첨가형 열연강판에서 고용강화와 시효경화를 고려한 적정 Cu 첨가량은 1.2wt% 전후였으며, Mn첨가량은 0.75-0.85wt%범위였다. 0.05%C-1.2%Cu-0.75%Mn-0.04%Nb첨가 강판에서 과시효조건에서 관찰되는 조대한 석출물은 면심입방정 구조인 $\varepsilon$-Cu인 것으로 확인되었으며, 열연상태에서는 590MPa급을 가지며, 10% pre-strain을 부여한 후 $550^{\circ}C$에서 30분 열처리할 경우 780MPa급의 인장강도를 가지는 Cu첨가형 열연강판의 제조가 가능하였다.

• 소성∙가공
• /
• 제32권4호
• /
• pp.173-179
• /
• 2023

In this study, the age-hardening behavior and tensile properties of a cast AZ91-0.3Ca-0.2Y (SEN9) alloy are investigated and compared with those of a commercial AZ91 alloy. Even after homogenization heat treatment, the SEN9 alloy contains numerous undissolved secondary phases, Al₈Mn₄Y, Al₂Y, and Al₂Ca, which results in a higher hardness value than the homogenized AZ91 alloy. Under aging condition at 200 ℃, both the AZ91 and SEN9 alloys exhibit the same peak-aging time of 8 h, but the peak hardness of the latter (86.8 Hv) is higher than that of the former (83.9 Hv). The precipitation behavior of Mg₁₇Al₁₂ phase during aging significantly differs in the two alloys. In the AZ91 alloy, the area fraction of Mg₁₇Al₁₂ discontinuous precipitates (DPs) increases up to ~50% as the aging time increases. In contrast, in the SEN9 alloy, the formation and growth of DPs during aging are substantially suppressed by the Ca- or Y-containing particles, which leads to the formation of only a small amount of DPs with an area fraction of ~4% after peak aging. Moreover, the size and interparticle spacing of Mg₁₇Al₁₂ precipitates of the peak-aged SEN9 alloy are smaller than those of the peak-aged AZ91 alloy. The homogenized AZ91 alloy exhibits a higher tensile strength than the homogenized SEN9 alloy due to the finer grains of the former. However, the peak-aged SEN9 alloy has a higher tensile elongation than the peak-aged AZ91 alloy due to the smaller amount of brittle DPs in the former.

• 한국주조공학회지
• /
• 제24권1호
• /
• pp.45-51
• /
• 2004

Fe and Si are common impurity elements in the aluminum alloys. In this investigation, the effects of the addition of Fe and Si on the age-hardening behaviors of the Al-Cu-Mn-Ti-Zr-Cd casting alloys were examined through hardness measurements, calorimetric techniques and observation of the transmission electron microscopy. The addition of Fe depresses the formation of GPII and ${\theta}'$, and thus retards the peak aging time and reduces the peak hardness of the Al-Cu-Mn-Ti-Zr-Cd alloys. On the contrary, the addition of Si accelerates the formation of GPII and ${\theta}'$ and thus accelerates age-hardening behaviors of the Al-Cu-Mn-Ti-Zr-Cd alloys.

• 한국재료학회지
• /
• 제25권9호
• /
• pp.468-474
• /
• 2015

Evaluations of the microstructure and mechanical properties of age hardenable Cu-2.0wt%Be alloy are performed in order to determine whether it can be used as a welding electrode for projection welding. The microstructure examinations, hardness measurements, and tensile tests of selective aging conditions are conducted. The results indicate that the aging treatment with the fine-grained microstructure exhibits better hardness and high tensile properties than those of the coarse-grained microstructure. The highest hardness value and high tensile strength are obtained from the aged condition of $300^{\circ}C$ for 360 min due to the presence of the metastable ${\dot{\gamma}}$ precipitates on the grain boundaries. The values of the highest hardness and tensile strength are measured as 374 Hv and 1236.2 MPa, respectively. The metastable ${\dot{\gamma}}$ precipitates are transferred to the equilibrium ${\gamma}$ precipitates due to the over-aged treatment. The presence of the ${\gamma}$ precipitates appears as nodule-like precipitates decorated around the grain boundaries. The welding electrode with the best aging treated condition exhibits better welding performance for electrodes than those of electrodes used previously.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2009년도 제33회 추계학술대회논문집
• /
• pp.619-622
• /
• 2009

INCONEL 718합금은 상온, 고온 및 저온환경에서 기계적 특성이 아주 우수하다. 상온에서의 모재 강도는 약 900MPa이며, 열처리 후 시효경화처리에 의해 강도가 약 1300MPa까지 증가한다. 이러한 INCONEL 718합금의 기계적 특성은 시험결과에서도 유사한 값을 나타내었고, GTAW 용접부의 상온 기계적 특성도 모재보다 우수한 강도를 나타내었다. 또한 저온에서의 기계적 특성은 모든 시험조건에서 상온보다 높은 강도를 나타내었으며, 열처리 모재시편과 용접시편은 1400MPa에 달하는 고강도를 나타내었다. 이러한 결과를 바탕으로 INCONEL 718합금의 저온 기계적 특성이 우수한 것을 증명하였고, 용접성 또한 모재의 특성과 같이 상온 및 저온 특성이 우수한 것을 알 수 있었다. INCONEL 718 합금과 STS 316L의 이종접합의 경우에도 $-100^{\circ}C$환경의 인장강도가 상온보다 300MPa 이상 증가하는 것을 알 수 있었다. 따라서, INCONEL 718합금은 $100^{\circ}C$이하부터 일정온도까지는 기계적 특성이 계속 증가 할 것으로 사료되며, 극저온 고압 상태로 공급되는 산화제 배관 제작에 적합한 소재로 판단된다.

• 한국주조공학회지
• /
• 제30권1호
• /
• pp.29-33
• /
• 2010

The microstructure of Al-5%Mg based alloy mainly consists of aluminum matrix with a small amount of AlMn phase. The addition of Sc or Zn to the base alloy significantly improved the as-cast tensile strength, while the addition of Fe deteriorated both strength and ductility. Although the Al-5%Mg based alloy was not heat-treatable, aging hardening could be observed in the case that Sc or Zn was added to the base alloy. TEM analysis showed that very fine AlSc or AlMgZn precipitates were formed after T6 heat treatment, resulting in enhanced strength. The corrosion resistance measured as corrosion potential was found to decrease a little by adding Zn, whereas other alloying elements were not clearly influential.

• 대한기계학회논문집A
• /
• 제28권4호
• /
• pp.427-434
• /
• 2004

Ferritic stainless steel is recently used in high temperature structures because of its good properties of thermal fatigue resistance, corrosion resistance, and low price. Tensile and low-cycle fatigue (LCF) tests on 429EM stainless steel used in exhaust manifold were performed at several temperatures from room temperature to 80$0^{\circ}C$. Elastic Modulus, yield strength, and ultimate tensile strength monotonically decreased when temperature increased. Cyclic hardening occurred considerably during the most part of the fatigue life. Dynamic strain aging was observed in 200~50$0^{\circ}C$, which affects the cyclic hardening behavior. Among the fatigue parameters such as plastic strain amplitude, stress amplitude, and plastic strain energy density (PSED), PSED was a proper fatigue parameter since it maintained at a constant value during LCF deformation even though cyclic hardening occurs considerably. A phenomenological life prediction model using PSED was proposed considering the influence of temperature on fatigue life.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 춘계학술대회 논문집
• /
• pp.471-474
• /
• 2005

This study investigates the nano/microstructure, the aging response, and the mechanical/tribological properties of the eutectic regions in rheoformed A356 alloy-T5 parts using nano/micro-indentation and mechanical scratching, combined with optical microscopy and atomic force microscope (AFM). Most eutectic Si crystals in the A356 alloy showed a modified morphology as fine-fibers. The loading curve for the eutectic region was more irregular than that of the primary Al region due to the presence of various particles of varying strength. The aging responses of the eutectic regions in the rheoformed A356 alloys aged at $150^{\circ}C$ for different times (0, 2, 4, 8, 10, 16, 24, 36, and 72 h) were investigated. Both Victors hardness $(H_v)$ and indentation $(H_{IT})$ test results showed a similar trend of aging curves, and the peak was obtained at the same aging time of 10 h. A remarkable size-dependence of the tests was found.

• 한국재료학회지
• /
• 제2권6호
• /
• pp.389-397
• /
• 1992

Li의 양과 Al의 양을 달리한 $\alpha$(HCP) 단상 및 $\alpha$(HCP)+${\beta}$ (BCC) 2상 조직인 Mg-Li-Al합금을 시료로 하여 이 합금의 가공성과 시효경화륵성을 조사한 결과 $\alpha$단상보다는 $\alpha$+${\beta}$ 2상 조이,$\alpha$+${\beta}$ 2상조직에서는 Al양이 많을수록 가궁성이 증가하였으며 Mg-8.08Li-4.26Al의 경우 가공한계값은 62%였다. 이와같이 가공성이 증가한 이유는 basal plane뿐만 아니라 pyramidal plane과 prism plane에서도 슬립이 일어났기 때문이다. $\alpha$단상의 경우 MgL$i_2$ Al(${\theta}$)의 석출이 일어나지 않았으나 $\alpha$+${\beta}$ 2상 조직의 곁우 ${\beta}$상 내에서 ${\theta}$의 석출에 의한 피크경도같이 나타났으며, 2상 조직의 경우 경도값은 Al양이 많을수록 증가하였는데 이것은 Al양의 증가에 따른 Al Partition에 의한$\alpha$ 상의 강화와 ${\beta}$상에서의 석출물 증가에 의한 것으로 생각된다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2005년도 춘계학술대회 논문집
• /
• pp.1398-1401
• /
• 2005

The nano/microstructure, the aging response (in T5 heat treatment), and the mechanical/tribological properties of the eutectic regions in squeeze-cast A356 alloy were investigated using nano/micro-indentation and mechanical scratching, combined wit optical microscopy and atomic force microscope(AFM). Most eutectic Si crystals in the A356 alloy showed a modified morphology as fine-fibers. The loading curve for the eutectic region was more irregular than that of the primary Al region due to the presence of various particles of varying strength. In addition, the eutectic region showed lower pile-up and higher elastic recovery than the primary Al region. The aging responses of the eutectic regions in the squeeze-cast A356 alloys aged at $150^{\circ}C$ for different times(0, 2, 4, 8, 10, 16, 24, 36 and 72 h) were investigated. As the aging time increased, acicular Si particles in the eutectic regions gradually came to a fine structure. Both Vickers hardness ($H_V$) and indentation ($H_{IT}$) test results showed almost the same trend of aging curves, and the peak was obtained at the same aging time of 10 h. A remarkable size-dependence of the tests was found. The friction coefficient for the eutectic region was lower than that for the primary Al region.