• The Journal of Korean Academy of Prosthodontics
• /
• v.50 no.4
• /
• pp.279-284
• /
• 2012

Purpose: This study evaluated the effect of glass fiber pre-impregnated with light-curing resin on the fracture strength and fracture modes of a maxillary complete denture. Materials and methods: Maxillary acrylic resin complete dentures reinforced with glass fiber pre-impregnated with light-curing resin (SES MESH, INNO Dental Co., Yeoncheongun, Korea) and without reinforcement were tested. The reinforcing material was embedded in the denture base resin and placed different regions (Control, without reinforcement; Group A, center of anterior ridge; Group B, rugae area; Group C, center of palate; Group D, full coverage of denture base). The fracture strength and fracture modes of a maxillary complete denture were tested using Instron test machine (Instron Co., Canton, MA, USA) at a 5.0 mm/min crosshead speed. The flexure load was applied to center of denture with a 20 mm diameter ball attachment. When fracture occurred, the fracture mode was classified based on fracture lines. The data were analyzed with one-way ANOVA at the significance level of 0.05. Results: There were non-significant differences (P>.05) in the fracture strength among test groups. Group A showed anteroposterior fracture and posterior fracture mainly, group B, C and control group showed partial fracture on center area mostly. Most specimen of group D showed posterior fracture. Conclusion: The location and presence of the fiber reinforcement did not affect the fracture strength of maxillary complete denture. However, reinforcing acrylic resin denture with glass fiber has a tendency to suppress the crack.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.3
• /
• pp.389-396
• /
• 2002

The purpose of this study was to compare the microtensile bonding strength of chemomechanically excavated dentin($Carisolv^{TM}$) to conventional caries removal(bur). The following adhesive systems were used; AB: All-Bond 2(3M, USA), PB: Prime & Bond 2.1(Dentsply, DE), AQ: AQ Bond(sun medical, Japan). 42 human molars with occlusal caries were assigned to 6 groups. Sequential caries removal was controlled with laser fluorescence. Each group was devided as follows; group A, B, C were $Carisolv^{TM}$ applied, group D,E,F were bur used. In group A and D, AB was used as a dentin adhesive. group B,E and group C,F was AQ and AQ was used each. The cavity was filled with composite resin(Z-100). The specimens were sectioned vertically into multiple serial 0.7 mm thick slabs. And then those slabs were sectioned into rectangular parts under 0.7 mm width. Finally 0.7-1.0 mm a right hexahedron shape stick become. Microtensile bonding test was carried out with testing apparatus at cross-head speed of $0.5\;mm/min^{-1}$ and fractured surfaces were observed with scanning electron microscope(JSM-6400, Jeol, Japan). The obtained results were summarized as follows ; 1. In the group of caries removal with $Carisolv^{TM}$, micro-tensile bonding strength decreased to $75.8{\sim}80$ percent of bur used group. 2. In the group of caries removal with $Carisolv^{TM}$, decreased degree of micro-tensile bonding strength is not so different in 3 kinds of dentin adhesives(p<0.05). 3. In the group of caries removal with $Carisolv^{TM}$, microtensile bonding strength of AB, PB, AQ was 32.6MPa(2.4), 30.1Mpa (1.8), 21.2Mpa(1.9). 4. In the group of caries removal with Bur and $Carisolv^{TM}$, microtensile bonding strength of AQ was significantly lower than that of AB and PB(p<0.01).

• Korean Journal of Materials Research
• /
• v.5 no.6
• /
• pp.754-762
• /
• 1995

Strontium titanate(SrTiO$_3$) thin film was prepared on Si substrates by RF magnetron sputtering for a high capacitance density required for the next generation of LSTs. The optimum deposition conditions for SrTiO$_3$thin film were investigated by controlling the deposition parameters. The crystallinity of films and the interface reactions between SrTO$_3$film and Si substrate were characterized by XRD and AES respectively. High quality films were obtained by using the mixed gas of Ar and $O_2$for sputtering. The films were deposited at various bias voltages to obtain the optimum conditions for a high quality file. The best crystallinity was obtained at film thickness of 300nm with the sputtering gas of Ar+20% $O_2$and the bias voltage of 100V. The barrier layer of Pt(100nm)/Ti(50nm) was very effective in avoiding the formation of SiO$_2$layer at the interface between SrTiO$_3$film and Si substrate. The capacitor with Au/SrTiO$_3$/Pt/Ti/SiO$_2$/Si structure was prepared to measure the electric and the dielectric properties. The highest capacitance and the lowest leakage current density were obtained by annealing at $600^{\circ}C$ for 2hrs. The typical specific capacitance was 6.4fF/$\textrm{cm}^2$, the relative dielectric constant was 217, and the leakage current density was about 2.0$\times$10$^{-8}$ A/$\textrm{cm}^2$ at the SrTiO$_3$film with the thickness of 300nm.

• Restorative Dentistry and Endodontics
• /
• v.29 no.2
• /
• pp.170-176
• /
• 2004

Objectives : In the unique metal iris method. the developing interfacial gap at the cavity floor resulting from the cavity wall property during polymerizing composite resin might affect the nominal shear bond strength values. The aim of this study is to evaluate that the iris method reduces the cohesive failure in the substrates and the cavity wall property effects on the shear bond strength tests using iris method. Materials and Methods : The occlusal dentin of 64 extracted human molars were randomly divided into 4 groups to simulate two different levels of cavity wall property (metal and dentin iris) and two different materials ($ONE-STEP^{\circledR}$ and $ALL-BOND^{\circledR}$ 2) for each wall property. After positioning the iris on the dentin surface. composite resin was packed and light-cured. After 24 hours the shear bond strength was measured at a crosshead speed of 0.5 mm/min. Fracture analysis was performed using a microscope and SEM. The data was analyzed statistically by a two-way ANOV A and t-test. Results : The shear bond strength with metal iris was significant higher than those with dentin iris (p＝0.034). Using $ONE-STEP^{\circledR}$, the shear bond strength with metal iris was significant higher than those with dentin iris (p＝0.005), but not in $ALL-BOND^{\circledR}$ 2 (p＝0.774). The incidence of cohesive failure was very lower than other shear bond strength tests that did not use iris method. Conclusions：The iris method may significantly reduce the cohesive failures in the substrates. According to the bonding agent systems. the shear bond strength was affected by the cavity wall property.

• Korean Journal of Dental Materials
• /
• v.45 no.4
• /
• pp.233-242
• /
• 2018

The purpose of this study is to evaluate the effect of resin cement color on the color of commercially available zirconia crown. The zirconia and resin cements used for the experiment were $NuSmile^{(R)}$ ZR Zirconia LT Shade (LT), $RelyX^{TM}$ U200 TR, A2, and A3O (TR, A2, A3O). The disks of zirconia and resin cements with diameters of 5 mm and thicknesses of 1 mm were prepared. Five disks were made for each specimen. The CIE $L^*a^*b^*$ values of zirconia, resin cements and the combinations thereof were measured on black and white backgrounds, respectively, using a spectrophotometer. The color effect of resin cement on the color of the zirconia crown was evaluated by calculating translucency parameter (TP), contrast ratio (CR), and color differences (${\Delta}E{^*}_{ab}$) based on the measured CIE $L^*a^*b^*$ values. The statistical significances were verified by one-way ANOVA and the Tukey-multiple comparisons tests. As a result, the TP and CR values were decreased (p<0.05) and increased, respectively, in the combination of zirconia and resin cement disks compared to zirconia disk per se. When using the black background, the ${\Delta}E{^*}_{ab}$ values between zirconia and the combination of the zirconia and three resin cement disks were imperceptible level. The A3O showed the lowest ${\Delta}E{^*}_{ab}$ value among three resin cements. When using the white background, the ${\Delta}E{^*}_{ab}$ values between zirconia and the combination of zirconia and TR resin cement (LT/TR) disks showed acceptable level. However, the ${\Delta}E{^*}_{ab}$ values between zirconia and the combination of zirconia and A2 resin cement (LT/A2) disks showed unacceptable level. Meanwhile, the ${\Delta}E{^*}_{ab}$ values between zirconia and the combination of zirconia and A3O resin cement (LT/A3O) disks showed perceptible but acceptable level. Within the limits of this study, the colors of resin cements did not cause unacceptable color changes of zirconia except the combination of LT/A2 on the white background. The resin cement that gave the least color changes to zirconia was A3O. This means that the resin cement A3O is recommended to use for minimizing color changes when cementing commercially available zirconia crown to tooth.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.2
• /
• pp.110-117
• /
• 2019

Purpose: This study was to evaluate the wear resistance of 3D printed, milled, and conventionally cured provisional resin materials. Materials and methods: Four types of resin materials made with different methods were examined: Stereolithography apparatus (SLA) 3D printed resin (S3P), digital light processing (DLP) 3D printed resin (D3P), milled resin (MIL), conventionally self-cured resin (CON). In the 3D printed resin specimens, the build orientation and layer thickness were set to $0^{\circ}$ and $100{\mu}m$, respectively. The specimens were tested in a 2-axis chewing simulator with the steatite as the antagonist under thermocycling condition (5 kg, 30,000 cycles, 0.8 Hz, $5^{\circ}C/55^{\circ}C$). Wear losses of the specimens were calculated using CAD software and scanning electron microscope (SEM) was used to investigate wear surface of the specimens. Statistical significance was determined using One-way ANOVA and Dunnett T3 analysis (${\alpha}=.05$). Results: Wear losses of the S3P, D3P, and MIL groups significantly smaller than those of the CON group (P < .05). There was no significant difference among S3P, D3P, and MIL group (P > .05). In the SEM observations, in the S3P and D3P groups, vertical cracks were observed in the sliding direction of the antagonist. In the MIL group, there was an overall uniform wear surface, whereas in the CON group, a distinct wear track and numerous bubbles were observed. Conclusion: Within the limits of this study, provisional resin materials made with 3D printing show adequate wear resistance for applications in dentistry.

• Journal of the Korean Wood Science and Technology
• /
• v.2 no.2
• /
• pp.5-7
• /
• 1974

1. This study indicates that above the fiber saturation point the drying rate can be increased with increasing the velocity of the air circutation, i.e., the drying rate of sample boards is proportional to the air velocity, but below the fiber saturation point, the effect of the velocity of air circulation is very low as shown in Figs. 1 and 2. 2. Under the controlled temperature and humidity in the kiln, the more the sample boards have moisture, the higher drying rate of it can be obtained. In other words, this means that even though in the case of drying various moisture content of wood, at the final drying stage, approximately the same percentage of moisture content of wood can be secured by employing the higher velocity of air circulation. 3. This study shows that the rate of drying in kiln changes distinctly at the fiber saturation point, i, e., above the fiber saturation point, the drying curve shows concave aginst the X axsis, but below the fiber saturation point, in the range from 30 percent of moisture content to 20 percent of moisture content, the curve shows convex as shown in Fig. 3. As the drying progresses, however, the drying curve shows concave again below 20 percent of moisture content. This means that inflection point of drying curve may be located clearly at the fiber saturation point, i.e., 30 percent of moisture content. As mentioned above, the 30 percent of moisture content of wood at which the inflectional point appears can be recognized as a critical point, i. e., the fiber saturation point at which all free water was removed from wood. The existence of inflectional point indicates that the evaporation of hygroscopic water in a cell wall is more difficult than the evaporation of free water in a cell cavity and the minor space of cell wall. The convex curve in the range of moisture content from 30 percent to 20 percent means that the evaporation of capillary condensed water has a tendency of the same rates of drying approximately, but as approaching to the 20 percent of moisture, the transfusion of moisture from wood becomes difficult because of having less moisture in cell wall. Below 20 percent of moisture content, the drying curve shows concave again, which means that it is difficult to remove the moisture located nearer to the surface of cellulose molecules and the surface bound water. These relations were revealed in Fig. 4. In comparison AC curve which does not have the two inflection points with BD curve which has two inflection points, i.e., Band D, they are mentioned already, by existence of the inflection points, the curve BD shows that the change of drying rate in the interval from 20 percent of moisture content to 30 percent of moisture content is not greater than in the case of the curve AC in the same interval. At the inflection point of 30 percent of moisture content, it can be noticed that the changing of the drying rate is very conspicuous. This phenomenon also can be recognized, as it is noticed by the Fig. 3, the drying rate from green to 30 percent of moisture content is very great. But the inclination of the curve is very slow from 30 percent of moisture content to 20 percent of moisture content, i.e., the inclination of the curve becomes almost horizontal lines. Acknowledgments Gratitude is expressed to Fred E. Dickinson, Professor of 'Wood Technology, School of Natural Resources, University of Michigan, USA for his suggestion to carry out this study.