• Journal of the Korea Concrete Institute
• /
• v.17 no.3 s.87
• /
• pp.427-434
• /
• 2005

An experimental investigation was carried out in order to verify the compressive strength, flexural strength, equivalent bending strength, rebound rate of shotcrete according to silicate accelerator, aluminate accelerator, cement mineral accelerator respectively and to especially evaluate the performance of shotcrete using cement mineral accelerator for high quality. The test result of compressive strength was showed that all accelerators were satisfied the required test value for each age, for the requirement of having the $75\%$ or higher compressive strength ratio to plain concretes at 28 days, cement mineral accelerator with $87\%$ compressive strength ratio was only satisfied. In flexural strength test, cement mineral accelerator was satisfied the flexural strength requirement in steel fiber reinforced shotcrete for each age. Aluminate type was conformed to the requirement for 28 days, but not at 1 day, silicate type was failed to satisfy standard requirement. Rebound rate was measured between $11{\~}19\%$ and cement mineral accelerator was showed comparatively lower rebound rate. Based on the test results, cement mineral accelerator exhibited excellent strength improvement and lower rebound rate compared to the conventional accelerator, its result is showed the possibility of making high performance shotcrete.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.8 no.3
• /
• pp.237-247
• /
• 2006

The use of high-performance shotcrete lining is indispensable to improve long-term durability of a tunnel and to apply the single-shell tunnelling method. Among a lot of shotcrete admixtures, pozzolan materials such as silica fume have positive effects on increasing the strength and the durability of shotcrete. It is also well known that a cement-based accelerator is much faster in setting time and more eco-friendly than conventional accelerators. This study aimed to improve the properties of wet-mix shotcrete by incorporating with Metakaolin and the calcium aluminate based accelerator. To compare Metakaolin with silica fume, mixing ratios of each material were varied as 4% and 8% of cement weight. Moreover, Metakaolin was blended with silica fume, and their binder was also set to 4% and 8% of cement weight. At each mixing condition, setting time, compressive strength, flexural strength, permeability and freezing-thawing resistance were measured. From the experiments, it was revealed Metakaolin could be a substituting material for silica fume.

• Cement Symposium
• /
• no.30
• /
• pp.239-247
• /
• 2003

• Cement Symposium
• /
• no.26
• /
• pp.145-152
• /
• 1999

• Magazine of korean Tunnelling and Underground Space Association
• /
• v.13 no.6
• /
• pp.50-57
• /
• 2011

• Geotechnical Engineering
• /
• v.21 no.10
• /
• pp.52-55
• /
• 2005

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.2
• /
• pp.86-93
• /
• 2020

Shotcrete concrete is generally used in the form of ready-mixed concrete products using type I ordinary portland cement(hereinafter referred to as OPC) and about 5% of accelerator mixed separately in the field. In this study, we tested the effect of addition of slag powder(SP) and limestone powder(LSP) on a penetration resistance, compressive strength of binder for shotcrete using calcium aluminate type accerlerator. And we analysed hydrates and pore structure effects on mortar performance. In the future, it is expected to be useful for manufacturing optimized composite cement as a binder for shotcrete.

• Magazine of korean Tunnelling and Underground Space Association
• /
• v.6 no.2
• /
• pp.38-50
• /
• 2004

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.2
• /
• pp.78-85
• /
• 2020

Shotcrete concrete is generally used in the form of ready-mixed concrete products using type I ordinary portland cement(hereinafter referred to as OPC) and about 5% of accelerator mixed separately in the field. In this study, we tested the effect of OPC fineness and SO₃ content on a penetration resistance, compressive strength of binder for shotcrete using calcium aluminate type accerlerator. And we analysed hydrates and pore structure effects on mortar performance. In the future, it is expected to be useful for manufacturing optimized OPC as a binder for shotcrete.

• Journal of the Korea Concrete Institute
• /
• v.19 no.6
• /
• pp.701-706
• /
• 2007

This study evaluated the durability of high-performance shotcrete mixed in the proper proportions using alkali-free and cement mineral accelerators as a permanent support that maintains its strength for the long term. Durability tests were performed the chloride permeability, repeated freezing and thawing, accelerated carbonation, and the effects of salt environments. Test results showed that all the shotcrete mixes included silica fume had low permeability. In addition, after 300 freeze/thaw cycles, the shotcrete mix had excellent freeze/thaw resistance more than the 85% relative dynamic modulus of elasticity. The accelerated carbonation test results were no effect of accelerator type but, the depth of carbonation was greater in the shotcrete mix containing silica fume. No damage was seen in a salt environments. Therefore, the high performance shotcrete mix proportions used in this study showed excellent durability.