• Applied Chemistry for Engineering
• /
• v.7 no.3
• /
• pp.543-553
• /
• 1996

Oxygen reduction in an alkaline fuel cell was studied by using perovskite type oxides as an oxygen electrode catalyst. The high surface area catalysts were prepared by malic acid method and had a formula of $La_{0.6}Sr_{0.4}Co_{1-x}Fe_xO_3$(x=0.00, 0.01, 0.10, 0.20, 0.35 and 0.50). From the result of XRD pattern and specific surface area due to the amount of Fe substitution and the consumption of ammonia-water, the complex formation of Fe ion with $NH_3$ was the main factor for both the phase stability of perovskite and the increase of specific surface area. Multi-step calcination was necessary to give a single phase of perovskite in catalyst precursor. The crystal structure of the catalysts was simple cubic perovskite, which was verified from the XRD patterns of the catalysts. The activity of oxygen reduction was monitored by the techniques of cyclic voltammetry, static voltage-current method, and current interruption method. The activity(current density) of oxygen reduction showed its minimum at x=0.01 and its maximum between 0.20 and 0.35 of x-value in $La_{0.6}Sr_{0.4}Co_{1-x}Fe_xO_3$. This tendency was independent of the change of surface area.

• Food Science and Preservation
• /
• v.7 no.4
• /
• pp.395-402
• /
• 2000

To enlarge application field of electrolyzed acid-water(EAW) on food industry, the changes of EAW properties by storage conditions and heating were investigatet. It was showed that storing EAW in closed container is mon effective to keep up the oxidation-reduction potentials(ORP), hyperchloride content and pH than stored in opened ones. ORP of EAW stored in closed container could be kept mon than 1 month as 1,150 mV levels. Ruing heating from 2$0^{\circ}C$ to 95$^{\circ}C$, ORP was increased to 1,150 mV levels at 95$^{\circ}C$ after gradual decrease to 5$0^{\circ}C$. Tyrosinase activity was decreased approximately to 26%~35% in EAW having a 950 mV~1,140 mV ORP. Also it was confirmed that EAW has anti-browning effect as sliced apple and potato, and their juices treated with EAW had conspicous difference in their $\Delta$E value. 12 kinds of pesticides such as aldrine, capful diazinon, diedrin, $\alpha$-endosulfan $\beta$-endosulfan, endosulfan sulfate, endrin, $\alpha$-BHC, o,p'-DDT, procymidone, PCNB added in EAW were recovered from ND~73.6% comparing to ones added in distilled water. The recovered amounts of pesticides, procymidone and diazinon in lettuce after soaking in EAW were 1.12 ppm and ND, compared with those of amounts soaked in distilled water were 3.67 ppm and 3.05 ppm respectively. So, it seems that EAW has potentials to promote the degradation of pesticides.

• Applied Chemistry for Engineering
• /
• v.24 no.5
• /
• pp.507-512
• /
• 2013

Perovskite-type oxides were successfully prepared using microwave-assisted process, and by XRD, XPS, BET, and $H_2-TPR$. Their catalytic activities for the combustion of benzene were also examined. Most of catalysts studied showed the perovskite crystalline phase with the particle size of 21~35 nm. The $LaMnO_3$ catalyst showed the highest activity and the conversion reached almost 100% at $250^{\circ}C$. The catalysts prepared by microwave-assisted process showed higher activity compared to those prepared sol-gel method. In addition, the catalytic activity was increased with an increase of calcination temperature of $LaMnO_3$-type catalyst. The TPR results on the measurement of redox property showed a good correlation with the order of catalytic activity on the benzene combustion reaction.

• Transactions of the Korean hydrogen and new energy society
• /
• v.22 no.4
• /
• pp.443-450
• /
• 2011

The three-reactor chemical-looping process (TRCL) for the production of hydrogen from natural gas is attractive for both $CO_2$ capture and hydrogen production. In this study, redox property of $Fe_2O_3$ and $WO_3$ supported with $ZrO_2$ and $MgAl_2O_4$ were studied with temperature programmed oxidation/reduction (TPO/R) experiment. All metal oxides were prepared by ball mill method. Metal oxides supported with $ZrO_2$ showed the good redox property in TPO and TPR tests. Reduction behavior was matched well the theoretical reduction mechanism. Metal oxides supported with $MgAl_2O_4$ formed a solid solution ($MgFe_{0.6}Al_{1.4}O_4$, $MgWO_4$). $Fe_2O_3$ showed more narrow reaction range and lower reaction temperature than $WO_3$.

• Korean Chemical Engineering Research
• /
• v.51 no.4
• /
• pp.443-454
• /
• 2013

Various metal ions (transition and base metals) incorporated MCM-41 catalysts can be synthesized using colloidal and soluble silica with non-sodium involved process. Transition metal ion-typically $V^{5+}$, $Co^{2+}$, and $Ni^{2+}$-incorporated MCM-41 catalysts were synthesized by isomorphous substitution of Si ions in the framework. Each incorporated metal ion created a single species in the silica framework, single-site solid catalyst, showing a substantial stability in reduction and catalytic activity. Radius of pore curvature effect was investigated with Co-MCM-41 by temperature programmed reduction (TPR). The size of metallic Co clusters, sub-nanometer, could be controlled by a proper reduction treatment of Co-MCM-41 having different pore size and the initial pH adjustment of the Co-MCM-41 synthesis solution. These small metallic clusters showed a high stability under a harsh reaction condition without serious migration, resulting from a direct anchoring of small metallic clusters to the partially or unreduced metal ions on the surface. After a complete reduction, partial occlusion of the metallic cluster surface by amorphous silica stabilized the particles against aggregations. As a probe reaction of particle size sensitivity, carbon single wall nanotubes (SWNT) were synthesized using Co-MCM-41. A metallic cluster stability test was performed by CO methanation using Co- and Ni-MCM-41. Methanol and methane partial oxidations were carried out with V-MCM-41, and the radius of pore curvature effect on the catalytic activity was investigated.

• Applied Chemistry for Engineering
• /
• v.7 no.3
• /
• pp.554-564
• /
• 1996

Oxygen reduction in an alkaline fuel cell was studied by using perovskite of $La_{0.6}Sr_{0.4}Co_{1-x}Fe_xO_3$(x=0.00, 0.01, 0.10, 0.20, 0.35, and 0.50) as an oxygen electrode catalyst. The changes in the catalytic properties as a function of Fe content were investigated by XRD, TG, and TPR. XRD patterns gave different lattice parameters of the catalysts. TG study revealed that Fe was so stabilized in the perovskite structure as to be hardly reduced even up to $900^{\circ}C$, and the amount of oxygen which was eliminated at high temperature increased with the fraction of Fe because Fe induced the increase of Co-O binding energy. From TPR study, ${\alpha}$-(low temperature peak) and ${\beta}$-(high temperature peak)states were observed. The bond strength of the ${\beta}$-species which was associated strongly with Co of the perovskite increased proportionally with the fraction of Fe. The ${\alpha}$-species, reversible oxygen, was the active species in the oxygen reduction. The ${\alpha}$-peak temperature which reflected the binding energy between Co and ${\alpha}$-state oxygen moved to lower temperature with the increase of lattice parameter of the catalytst due to the increase of Fe content. The decrease in the binding energy increased the activity in the oxygen reduction, but the decrease of ${\alpha}$-species with the increase of Fe content decreased the activity. The increase in the surface area with Fe content had little effect on the activity.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.2
• /
• pp.97-104
• /
• 2016

In the preparation of Ag-coated Cu flakes using L-ascorbic acid as a reductant for the electroless Ag plating, the effects of pretreatment methods and the reductant concentration on the uniformity of Ag coating layer and the anti-oxidation property of Ag-coated Cu flakes during the heating in air were evaluated. It was found that the removal degree of surface oxide layer during the pretreatment has great influence on the uniformity of Ag coating layer and the formation degree of hole defects in the flakes has slight effect on the anti-oxidation property of Ag-coated Cu flakes. It was also verified that the reductant concentration has great influence on the coverage uniformity and thickness of Ag coating, thus it was could be considered a main process parameter. When the reductant concentration was 0.04 M, high-quality Ag-coated Cu flakes was obtained. When the concentration increased to 0.06 M, however, the anti-oxidation property of Ag-coated Cu flakes became remarkably worse owing to remnant of Cu surface non-coated with Ag by the formation of pure Ag fine particles.

• Korean Chemical Engineering Research
• /
• v.53 no.6
• /
• pp.824-830
• /
• 2015

The influence of phosphorous precursors, $NH_4H_2PO_4$, $(NH_4)_2HPO_4$, $H_3PO_4$, $(C_2H_5)_3PO_4$, and $P_2O_5$, on the catalytic performance of the $BiFe_{0.65}MoP_{0.1}$ catalysts in the oxidative dehydrogenation of 1-butene to 1,3-butadiene was studied. The catalysts were characterized by XRD, $N_2$-sorption, ICP, SEM and TPRO analyses. It was not observed big difference on the physical properties of catalysts in accordance with used different phosphorous precursors, however, the catalytic performance was largely depended on the nature of the phosphorous precursors. Of various precursors, the $BiFe_{0.65}MoP_{0.1}$ oxide catalyst, which was prepared from a phosphoric acid precursor, showed the best catalytic performance. Conversion and yield to butadiene of the catalyst showed 79.5% and 67.7%, respectively, after 14 h on stream. The cation of phosphorous precursors was speculated to affect the lattice structure of the catalysts during catalyst preparation and this difference was influenced on the re-oxidation ability of the catalysts. Based on the results of TPRO, it was proposed that the catalytic performance could be correlated with re-oxidation ability of the catalysts.

• Korean Chemical Engineering Research
• /
• v.60 no.1
• /
• pp.159-168
• /
• 2022

Catalytic activity in ammonia decomposition reaction was studied on Mo-Al nitride obtained through temperature programmed nitridation of calcined Mo-Al mixed oxide prepared by varying the MoO₃ quantity in the range of 10-50 wt%. N₂ sorption analysis, X-ray diffraction analysis (XRD), X-ray photoelectron spectroscopy (XPS) and H₂-temperature programmed reduction (H₂-TPR), and transmission electron microscopy (TEM) to investigate the physicochemical properties of the prepared catalyst were performed. After calcination at 600 ℃, the XRD of Mo-Al oxide showed γ-Al₂O₃ and Al₂(MoO₄)₃ phases, and the nitride after nitridation showed an amorphous form. The specific surface area after nitridation by topotactic transformation of MoO₃ to nitride was increased due to the formation of Mo nitride, and the Mo nitride was observed to be supported on γ-Al₂O₃. As for the catalytic activity in the ammonia decomposition reaction, 40 wt% MoO₃ showed the best activity, and as the nitridation time increases, the activity increased, and thus the activation energy decreased.

• Clean Technology
• /
• v.25 no.1
• /
• pp.81-90
• /
• 2019

A dielectric barrier discharge (DBD) plasma reactor packed with $Ni-CeO_2/{\gamma}-Al_2O_3$ catalyst was used for the dry ($CO_2$) reforming of propane (DRP) to improve the production of syngas (a mixture of $H_2$ and CO) and the catalyst stability. The plasma-catalytic DRP was carried out with either thermally or plasma-reduced $Ni-CeO_2/{\gamma}-Al_2O_3$ catalyst at a $C_3H_8/CO_2$ ratio of 1/3 and a total feed gas flow rate of $300mL\;min^{-1}$. The catalytic activities associated with the DRP were evaluated in the range of $500{\sim}600^{\circ}C$. Following the calcination in ambient air, the ${\gamma}-Al_2O_3$ impregnated with the precursor solution ($Ni(NO_3)_2$ and $Ce(NO_3)_2$) was subjected to reduction in an $H_2/Ar$ atmosphere to prepare $Ni-CeO_2/{\gamma}-Al_2O_3$ catalyst. The characteristics of the catalysts were examined using X-ray diffraction (XRD), transmission electron microscopy (TEM), field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectrometry (EDS), temperature programmed reduction ($H_2-TPR$), temperature programmed desorption ($H_2-TPD$, $CO_2-TPD$), temperature programmed oxidation (TPO), and Raman spectroscopy. The investigation revealed that the plasma-reduced $Ni-CeO_2/{\gamma}-Al_2O_3$ catalyst exhibited superior catalytic activity for the production of syngas, compared to the thermally reduced catalyst. Besides, the plasma-reduced $Ni-CeO_2/{\gamma}-Al_2O_3$ catalyst was found to show long-term catalytic stability with respect to coke resistance that is main concern regarding the DRP process.