• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.1
• /
• pp.39-48
• /
• 2020

The present study investigates the chemical reaction and performance of ternary blended binders by mixing ferronickel slag. Cement was replaced using ground granulated blast furnace slag and ferronickel slag, combined up to 50% of the replacement rate. The blended cements were tested by setting times, length change, compressive strength at 1, 3, 7, 28 days. X-ray diffraction and scanning electron microscope were conducted for detecting hydration products while the MIP and microhydation heat were used for examining morphological characteristics. The results showed that by adding ferronickel slag, Pozzolanic reaction occurred, forming a dense pore structure and the effect of reducing hydration heat and dry shrinkage was also found. The compressive strength at 28 days was lower than that of 100% OPC control specimen (OSP0), but ternary blended cements showed no significant difference compared to binary blended (OSP50). If the optimal mix is derived later and used for the purpose, the potential for use as a cement binder is expected.

• Journal of the Korea Institute of Building Construction
• /
• v.19 no.6
• /
• pp.485-494
• /
• 2019

This study is to evaluate the effect of admixtures such as blast-furnace slag and fly ash on adhesion in flexure and tension of polymer cement mortar(PCM) using SAE emulsion. The test specimens are prepared with five polymer-cement ratios and five admixture contents, and tested for flexural strength, adhesion in flexure, tensile strength and adhesion in tension. Based on the test results, no improvement of flexural strength and adhesion in flexure caused by admixtures in PCM can be indicated, but the tensile strength and adhesion in tension is improved due to mixing of the admixtures. In particular, the maximum of adhesion in tension of PCM with P/C 20% and BF content of 10% is 3.35MPa which is about 2.36 times higher than that of ordinary cement mortar, and 1.32 times that of PCM that does not contain any admixture. The average ratio of adhesion in tension to tensile strength of PCM was 48.7%. It is apparent that admixture contents of 5% or 10% could be proposed for improvement of tensile strength and adhesion in tension of PCM.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.6
• /
• pp.142-152
• /
• 2010

In this study, eleven reinforced concrete beams, without stirrup, using high ductile fiber-reinforced mortar with ground granulated blast furnace slag(SHF Series, SHFSC Series) and standard specimens without or with stirrup(SSS, BSS) were constructed and tested under monotonic loading. Experimental programs were carried out to improve and evaluate the shear performance of such test specimens, such as the load-displacement, the failure mode, the maximum strength, and shear strength. All the specimens were modeled in scale-down size. Test results showed that test specimens(SHF Series, SHFSC Series) was increased respectively the shear strength carrying capacity by 26%, 20% and the ductility capacity by 5.27, 5.75 times in comparison with the standard specimen without stirrup(SSS). And the specimens(SHF Series, SHFSC Series) showed enough ductile behavior and stable flexural failure.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.6
• /
• pp.527-532
• /
• 2018

The objective of the present study is to evaluate a practical approach for enhancing the compressive strength and minimizing deforming of aerated concrete. Test results measured in the aerated concrete mixes that were produced using 40% ground granulated blast-furnace slag (GGBS) as a replacement of cement and cured under different conditions (i.e., high temperatures of $40^{\circ}C$ and $60^{\circ}C$ for 10 hrs or 15 hrs) were compared with those obtained from the specimens cured under room temperature. No deforming was observed in the mixes with 40% GGBS. The compressive strength of the prepared aerated concrete cured under high temperature was higher than that of the concrete cured at room temperature, even at the lower ranges of the apparent dry density. However, the curing time is needed to be controlled as not exceeding 10 hrs at the temperature of $60^{\circ}C$ to prevent the decrease in the compressive strength due to foam mergences.

• Journal of the Korea Concrete Institute
• /
• v.26 no.5
• /
• pp.607-614
• /
• 2014

The purpose of this dissertation was to investigate the effect of mineral admixtures, such as fly ash, blast furnace slag powder, meta kaolin and silica fume, on the basic properties and durability of crushed sand shotcrete, selecting a series of shotcrete mixtures with a variable admixture. Compressive strength increased as the content of mineral admixtures increased, specially it was the most effective when using meta kaolin both at sample specimen and core after shotcreting. Rapid chloride ion permeability test and sulfuric acid resistance test showed that both durability increased as the substitute rate of mineral admixture increased. In air void analysis with image analysis, the targeted the spacing factor and specific surface were not satisfied because air-entrained agent was not used.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.2
• /
• pp.26-33
• /
• 2016

The alkali-slag-red mud(ASRC) cement belongs to clinker free cementitious material, which is made from alkali activator, blast-furnace slag(BFS) and red mud in designed proportion. This study is to investigate strength and pore characteristics of alkali-activated slag cement(NC), clinker free cementitious material, and ordinary portland cement(C) mortars using polymer according to red mud content. The results showed that the hardened alkali-activated slag-red mud cement paste was mostly consisted of C-S-H gel, being very fine in size and extremely irregular in its shape. So the hardened ASRC cement paste has lower total porosity, less portion of larger pore and more portion of smaller pore, as compared with those of hardened portland cement paste, and has higher strength within containing 10 wt.(%) of alkali-activated slag cement(NC) substituted by red mud.

• Resources Recycling
• /
• v.16 no.4
• /
• pp.33-39
• /
• 2007

Titanium scrap was re-melted and refined by using a DC-ESR (Direct Current Electro Slag Remelting) apparatus. A graphite rod was used as an anode. The used slag was $CaF_2-TiO_2-CaO$ slag system. The effect of slag composition on the shape and oxygen content of re-melted ingot was studied. The titanium ingot was produced very well from the $CaF_2-TiO_2$ slag system, and the oxygen content of the ingot was less than that of titanium scrap. The addition of CaO into $CaF_2-TiO_2$ slag system made the bad shape of titanium ingot. The oxygen content of the ingot was also higher than that of titanium scrap.

• Resources Recycling
• /
• v.19 no.5
• /
• pp.50-57
• /
• 2010

Ternary blended concrete(TBC), which contains both fly ash and granulated blast furnace slag, has an initial cost effective and is environment friendly. Furthermore, it has a lot of technical advantages such as the improvement of long term compressive strength, high workability, and the reduction of hydration heat. However, as the use and study on the performance of ternary blended concrete is limited, it is low short term compressive strength. This study was performed to evaluate the characteristics which are a long and short term compressive strengths, permeability and chemical attacks resistance of hardened high early concrete containing slag powder and fly-ash using high early strength cement(HE-TBC). Replacement rate of FA is fixed on 10% and replacement rate of slag powder are 0%, 10%, 20% and 30%. The test results showed that compressive and flexural strength of HE-TBC increased as the slag contents increased from 0% to 30% at the short term of curing. The permeability resistance of HE-TBC(fly ash 10%, blast 30%) was extremely good at the short and long terms. However, high early strength ternary blended concrete had weak on carbonation of chemical attack.

• Journal of the Korea Concrete Institute
• /
• v.25 no.1
• /
• pp.115-123
• /
• 2013

The steel industry, a representative industry that significantly consumes raw materials and energy, produces steel as well as a large amount of by-product steel slag through the production process. The vast habitat foundation of marine life has been destroyed due to recent reckless marine development and environment pollution, resulting in intensification of the decline of marine resources, and a solution to this issue is imperative. In order to propose a method to recycle large amounts of by-product slag into a material that can serve as an alternative to natural aggregate, the engineering properties and applicability for each mixing factor of environment friendly porous concrete as a material for the composition of marine ranches were evaluated in this study. The test results for percentage of voids per mixing ratio revealed that the margin of error for all conditions was within 2.5%. The compressive strength test results showed that the most outstanding environmental friendly porous concrete can be manufactured when mixing 30% slag aggregate and 10% specially treated granular fertilizer for the optimum volume fraction. As concrete for marine applications, the best seawater resistance was obtained with mixing conditions for high compression strength. An assessment of the ability to provide a marine life habitat foundation of environmentally friendly porous concrete showed that a greater percentage of voids facilitated implantation and inhabitation of marine life, and the mixing of specially treated granular fertilizer led to active initial implantation and activation of inhabitation. The evaluation of harmfulness to marine life depending on the mixture of slag aggregate and specially treated granular fertilizer revealed that the stability of fish is secured.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.5
• /
• pp.389-396
• /
• 2014

The set accelerator used for shotcrete at high pH environment often causes the dusting problem in practice. In this research, a slurry-type set accelerator was developed to avoid this problem and its effectiveness was investigated by applying it to shotcrete mortars. Set time, stiffening, compressive strength, and chloride ion penetration resistance were examined with different amounts of slag, used as partial replacement of cement. According to the experimental results, it was found that the earlier responses such as set time, stiffening, and 1-day compressive strength were probably affected by the amount of ettringite, formulated by the hydration between C12A7 and calcium sulfate polymorphs present in blast furnace slag. Whereas, it is believed that the result of compressive strength after 3 days was attributed to the hydration of tricalcium silicates. As for the results of a chloride ion penetration test, the partial replacement of cement with slag significantly reduced the total charge passed through the shotcrete mortar.