• Journal of Ocean Engineering and Technology
• /
• v.8 no.2
• /
• pp.173-184
• /
• 1994

원자력 압력용기강의 탄소성 파괴인성값 $J_IC$를 CT형 시험편을 이용하여 검토하였으며, 평활 시험편 및 측면홈 시험편의 두께는 각각 $B_O$=25.4mm, $B_N$=20.4mm 이다. 측면홈의 깊이는 19.7% 이며, 홈의 각도는 90 .deg.로 가공하였다. 탄소성 파괴인성시험은 ASTM E813-81과 JSME S001-81의 추천방법에 따라 실시하였다. 두 추천방법으로 실험한 결과 ASTM 방법에 의한 $J_IC$값이 과대평가됨으로써 부대조건에 만족되지 못하였지만 JSME방법은 만족되었다. 측면홈 시험편은 R고선법에 의한 ductile tearing의 결정이 평활 시험편보다 용이하였으며, 이에 따른 $J_IC$값의 정확성을 배가 할 수 있었다. 또한 임계 스트레치존 폭($SZW_C$)은 측면홈에 의한 높은 3축응력이 발생되어 평활시험편보다 적게 나타났으며, 이러한 복합적인 원인에 기인하여 스트레치존법에 의한 $J_IC$평가는 R곡선법에 의한 평가보다 약간 과대평가됨을 알 수 있었다.

• Journal of Ocean Engineering and Technology
• /
• v.7 no.2
• /
• pp.91-102
• /
• 1993

The elastic-plastic fracture thoughness J sub(IC) of Nuclear Reactor Vessel Steel(SA 508-3) which has high toughness was discussed at temperatures RT, $-20^{\circ}C$, $200^{\circ}C$ and 1/2/CT specimen was used for this study. Especially the two methods recommended in ASTM and JSME were compared. It was difficult to find J sub(IC) by ASTM R-curve method with the specimen used for this research, while JSME R-curve method yielded good result. The stretched zone width menthod gave slightly larger J sub(IC) values than those by the R-curve method for SA 508-3 steel.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.3 s.174
• /
• pp.710-717
• /
• 2000

Tensile and fracture toughness tests of the cold-rolled STS 304 steel plate for membrane material of LNG storage tank were performed at wide range of temperatures, 11 IK(boiling point of LNG), 153K , 193K and 293K(room temperature). Tensile strength significantly increases with a decrease in temperature, but the yield strength is relatively insensitive to temperature. Elongation at 193K abruptly decreases by 50% of that at 293K, and then decreases slightly in the temperature range of 193K to 111K. Strain hardening exponents at low temperatures are about four times as high as that at 293K. Elastic-plastic fracture toughness($J_c$) and tearing modulus($T_{mat}$) tend to decrease with a decrease in temperature. The $J_c$ values are inversely related to effective yield strength in the temperature range of 111K to 293K. These phenomena result from a significant increase in the amount of transformed martensite in low temperature regions.