• Journal of the KSME
• /
• v.51 no.11
• /
• pp.45-50
• /
• 2011

연료전지 자동차의 700MPa 고압수소저장을 위한 기술 개발이 진행되고 있다. 고압수소저장에서 재료 문제는 고압수소가스에 재료가 노출되는 데 다른 수소취화가 중요하여 그에 관한 연구가 진행되고 있다. 이 글에서는 차량탑재 용기와 수소 스테이션의 안전성 확보를 위한 규제를 비롯한 수소취화에 대응하여 그 재료 규제에 관한 국제 동향을 소개한다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.12
• /
• pp.1497-1502
• /
• 2013

When using hydrogen gas as an ecofriendly energy sources, it is necessary to conduct a safety assessment and ensure thereliability of the hydrogen pressure vessel against hydrogen embrittlement expected in the steel materials. In this study, by applying the in-situ SP test method, the gas hydrogen embrittlement behaviors in SA372 steel, which is commonly used as a pressurized hydrogen gas storage container, were evaluated. To investigate the hydrogen embrittlement behavior, SP tests at different punch velocities were conducted for specimens with differently fabricated surfaces at atmospheric pressure and under high-pressure hydrogen gas conditions. As a result, the SA372 steel showed significant hydrogen embrittlement under pressurized hydrogen gas conditions. The effect of punch velocity on the hydrogen embrittlement appeared clearly; the lower punch velocity case indicated significant hydrogen embrittlement resulting in lower SP energy. The fractographic morphologies observed after SP test also revealed the hydrogen embrittlement behavior corresponding to the punch velocity adopted. Under this pressurized gas hydrogen test condition, the influence of specimen surface condition on the extent of hydrogen embrittlement could not be determined clearly.

• Journal of the KSME
• /
• v.51 no.11
• /
• pp.42-44
• /
• 2011

이 글에서는 철강재료의 생산공정 및 사용 중 수소취화에 의해 발생하는 현상과 방지대책에 대하여 소개하고자 한다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.193-195
• /
• 2011

강판재 사용에 있어 수소취성현상은 강판재가 고강도화됨에 따라 그 감수성이 커지는 것으로 알려져 있다. 특히 노출강판재의 경우, 표면으로부터 침투해 들어가는 수소에 의한 수소취화 거동에 대한 연구가 필요하다. 본 연구에서는 고강도 DP강을 시험편으로 하여, 음극전기분해법에 의해 수소를 강제주입시킨 후, DP강 표면하 subsurface zone의 수소취화 거동을 평가하고자 하였다. 미소경도분포 측정결과, 수소주입시간이 증가함에 따라 표면하 subsurface zone의 경도 또한 증가하는 것으로 조사되었다. 이는 수소에 의해 표면하 subsurface zone의 경화가 일어나 DP강의 기계적 특성에 영향을 미친것으로 판단된다. 미소경도분포의 측정결과와 미세조직 관찰결과로부터 수소임계침투깊이를 평가하였고, 이를 통해 DP강내 수소확산에 의한 수소임계침투깊이가 존재함을 확인할 수 있었다.

• Journal of Energy Engineering
• /
• v.18 no.1
• /
• pp.49-55
• /
• 2009

Occurrence of hydrogen embrittlement could be one of the main obstacles for using structural equipment under hydrogen environment. It is required to develop assessment methods of hydrogen embrittlement for the metals used in production, storage, transmission and application utilities of hydrogen. The most probable method of hydrogen mass transmission is using existing natural gas pipeline. Base or weld part of the pipeline can be damaged by mixed gas of hydrogen in the pipeline. In this study small punch (SP) testing was employed to evaluate the hydrogen embrittlement behavior for a line pipe steel (API X65) with electrochemically hydrogen charged specimens. Results showed that the SP test can be a good candidate test method for hydrogen damage evaluation method. Strength of steel is known to be decreased with the level of hydrogen charging. However, for API X65 steel base metal need in this study, the effect of hydrogen to strength was not significant. It can be negligible regardless of the hydrogen contents in the steel. With this test different strength levels with various hydrogen charging conditions were observed. It can also be anticipated that more sensitive evaluation of material behavior be obtainable by the SP test method.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.6
• /
• pp.753-760
• /
• 2013

The hydrogen embrittlement of metallic materials is an important issue from the viewpoint of structural integrity. In this regard, the estimation of mechanical properties and fracture toughness under hydrogen conditions provides very important data. This study provides an experimental validation of the approach for simulating the small punch of Inconel 617 using finite element damage analysis, as recently proposed by the authors, and applies an inverse method for the determination of the constitutive tensile behavior of materials. The mechanical properties obtained from the inverse method are compared with those obtained from the tensile test and validated. The mechanical properties and fracture toughness are predicted by using the inverse method and finite element damage analysis.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.11
• /
• pp.1377-1382
• /
• 2011

Recently, alternative and novel energy resources have been developed for use in the future because of the current environmental problems and exhaustion of fossil energy resources. Hydrogen energy has many merits, such as its environmental friendliness, easy storage, and easy production, but it also has disadvantages, in that it is highly combustible and explosive. In this study, a test procedure using a simple SP test under highly pressurized hydrogen gas conditions was established. In order to evaluate its applicability, SP tests were carried out using a stainless steel (SUS316L) sample under atmospheric, pressurized helium, and pressurized hydrogen gas conditions. The results under the pressurized hydrogen gas condition showed fissuring and produced a reduction of the elongation in the plastic instability region due to hydrogen embrittlement, showing the effectiveness of the current in-situ SP test.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.7
• /
• pp.637-646
• /
• 2016

This study is to investigate the influence of hydrogen attack and UNSM on fatigue behaviors of the Inconel 718 alloy. The decrease of the fatigue life between the untreated and the hydrogen attacked material is 10-20%. The fatigue lives of hydrogen attacked specimen decreased without a fatigue limit, similar to those of nonferrous materials. Due to hydrogen embrittlement, about 80% of the surface cracks were smaller than the average grain size of $13{\mu}m$. Many small surface cracks caused by the embrittling effect of hydrogen attack were initiated at the grain boundaries and surface scratches. Cracks were irregularly distributed, grew, and then coalesced through tearing, leading to a reduction of fatigue life. Results revealed that the fatigue lives of UNSM-treated specimens were longer than those of the untreated specimens.

• Transactions of the Korean hydrogen and new energy society
• /
• v.21 no.4
• /
• pp.340-345
• /
• 2010

For the conversion into hydrogen society, not only studying facilities of hydrogen production, storage, transportation and charging system but also developing technique of ensuring safety are essentially needed. Hence, for the first step of that, evaluated the hydrogen embrittlement of Inconel alloy 617, Ni-based super heat-resisting alloy, by small punch test. Prepared the various specimens through changing electrochemical charging time and measured the toughness degradation of the specimens by small-punch test. The analysis of hydrogen embrittlement behavior were carried out by investigating the fractured surface of specimens. This study has significance on revealing mechanism of hydrogen embrittlement behavior and the factor affecting hydrogen embrittlement in the future study.

• Journal of Welding and Joining
• /
• v.8 no.3
• /
• pp.39-52
• /
• 1990

The research is to insure the soundness of the stainless steel overlaid weld metal(21/4Cr-IMo steel + SUS 309L) for a pressure vessel application. Detail studies were conducted for the PWHT influence on the micrstructure and intergranular corrosion characteristics of the overlaid weld metal as well as initiation of hydrogen embrittlement crack(or Disbonding) when welded metal are exposed to the hydrogen atmosphere. Hydrogen was experimentally charged to the overlaid weld metal in order to study PWHT effect on the susceptibility of hydrogen embrittlement crack. The results of this research are as follows: 1. At the bond region, austenite grain of the stainless steel side became coarsed and Cr23C6 type carbide was precipitated at the coarsed austenitic grain boundaries. Intergranular Corrosion width(by Straiss test) increased with increasing PWHT temperature and PWHT time.