• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.15-20
• /
• 2000

The hydrogen-storage properties of a mechanically-alloyed Mg-18wt.%Ni mixture were investigated. Among the mixtures mechanically alloyed for 1h, 3h, and 6h, the mixture mechanically alloyed for 6h(MA 6h sample) shows the best properties of activation, hydriding, and dehydriding. The $Mg_2Ni$ phase forms in the mechanically-alloyed Mg-18wt.%Ni mixture along with hydriding-dehydriding cycling. The MA 6h sample is relatively easily activated and has higher hydriding rate than the pure Mg, the Mg-10wt.%Ni alloy, and a little lower hydriding rate than the $Mg_2Ni$alloy. The MA 6h sample lower dehydriding rate than the $Mg_2$Ni alloy but higher dehydriding rate than the pure Mg and the Mg-25wt.%Ni alloy. The MA 6h sample has larger hydrogen-storage capacity than the pure Mg and the other alloys.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.243-249
• /
• 1998

상용 핵연료 피복관 재료로 사용되고 있는 Zircaloy-2와 Zircaloy-4 및 ZIRLO$^{TM}$에 대한 수소와의 반응거동 및 속도론적(kinetic) 자료를 얻기 위하여 electro-microbalance가 장착된 TGA (thermogravimetric analysis) 장치를 이용하여 30$0^{\circ}C$~50$0^{\circ}C$의 온도범위에서 1기압 수소와의 반응에 따른 무게증가를 in-situ로 측정하였다. Zircaloy와 수소와의 반응거동은 chamber내 온도상승시 생성되는 산화막에 의해 초기에는 느린 반응이 진행되는 영역이 존재하고 온도가 낮은 35$0^{\circ}C$ 이하에서는 이것이 잠복기 형태로 나타난 후 직선속도법칙(linear rate law)을 따르며 반응이 가속화되는 것으로 나타났고 40$0^{\circ}C$ 이하의 저온에서는 직선속도법칙에서 반응이 지연되는 방향으로 약간의 편차(deviation)가 관찰되었다. 그 결과 Zircaloy-2와 ZIRLO$^{TM}$가 Zircaloy-4보다 수소와의 반응속도가 빠르고 활성화에너지가 낮은 것으로 나타났으며 직선속도법칙을 근거로 하여 각각 1.1x$10^{7}$ exp(-20,800/RT)와 1.5x$10^{6}$exp(-18,000/RT) 및 6.9x$10^{7}$ exp(-23,800/RT) (mg/dm$^2$/min) 의 속도상수를 도출하였다. 또한, 열구배가 존재하지 않는 out-of-pile 조건하에서도 'sunburst' 형태의 국부적 수소침투가 발생할 수 있음이 ～l,000 ppm이상의 수소침투 시편에서 확인되었다. ～3,000ppm이상 침투하게 되면 표면에 수소화물이 농축되어 있는 hydride layer가 형성됨을 관찰하였으며 ～5,000ppm 이상의 경우에는 수소화물의 방향성이 random하였으며 특히, ZIRLO$^{TM}$ 시편의 경우에서는 원주방향으로 길게 이어진 수소화물과 기계적 성질에 치명적인 반경방향의 수소화물이 평행하게 배열된 것을 관찰하였다.

• 대한공업교육학회지
• /
• v.35 no.2
• /
• pp.204-223
• /
• 2010

The purpose of this study was to investigate the high temperature creep behavior of anisotropic Zr-2.4%Nb alloy which includes the hydride. To minimize the effect of the anisotropy and to achieve the bi-axial stress condition, SP creep test was performed using the Zr alloys which have the 50 ppm, 100 ppm and 200 ppm hydride. Each SP creep curve was obtained and compared. While the creep degradation of 50 ppm and 100 ppm hydride specimens was clearly found, the degradation of 200 ppm was not cleared. By the comparison of SP creep constant and stree exponent, this fact was confirmed. As the degradation of 50 ppm and 100 ppm hydride was processed, the SP creep constant was decreased and the stress exponet was increased. However, while the SP creep constant of 200 ppm hydride was decreased, the stree exponent was decreased. Finally, it was confirmed that the creep degradation of 200 ppm was not found. In conclusion, the hydride was the major parameter to control the hight temperature creep degradation of Zr alloy.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.23 no.4
• /
• pp.334-341
• /
• 2003

When the pressure tubes(f are in contact with the calandria tube(CT) in the pressurized heavy water reactor(PHWR), the temperature difference between inner and outer wall of W results in a thermal diffusion of hydrogen (deuterium) and hydride blisters are formed on the outer surface of PT. Because the hydride blisters and zirconium matrix are acoustically continuous, it is not easy to distinguish the blisters from the matrix with conventional ultrasonic method. An ultrasonic velocity ratio method was developed to detect small hydride blisters on the zirconium pressure tube. Hydride blisters were grown in the PT specimen using a steady state thermal diffusion device. The flight times of longitudinal echo and reflected shear echo from the outer surface were measured accurately. The velocity ratio of the longitudinal wave to the shear wave was calculated and displayed using contour plot. Compared to the conventional flight time method of longitudinal wave, the velocity ratio method shows superior sensitivity to detect smaller blisters as well as better images for the blister shapes. Detectable limit of the outer shape of the hydride blisters was conservatively estimated as $500{\mu}m$, with the same specifications of ultrasonic transducer used in the actual PHWR pressure tube inspection.

• Applied Chemistry for Engineering
• /
• v.5 no.2
• /
• pp.263-273
• /
• 1994

Titanium powder prepared by dehydrogenating the titanium hydride which is synthesized by reacting Ti-sponge (99.67%) with hydrogen using the self-propagating high-temperature synthesis method. In the synthesis of titanium hydride, the particle size of the product was found dependent on the amount of hydrogen incorporated into the titanium such that the particle size of titanium hydride decreased with increasing hydrogen pressure and after-burn time. In the dehydrogenation process, as the dehydrogenation time increase, the particle size of titanium powder increased due to partial melting and sintering of titanium particles.

• Analytical Science and Technology
• /
• v.14 no.5
• /
• pp.416-421
• /
• 2001

The optimization of the reductant and acid concentration for stannane($SnH_4$) generation was investigated by using a continuous flow hydride generator combined with an inductively coupled plasma-atomic emission spectrometer. Several different prereductants were studied to remove the interfering effect of fluoride ion on the hydride generating of tin. The optimum acid concentration was 0.5-1.0 M for the 1-2% $NaBH_4$ and 1.0 M NaOH and the interfering effect of fluoride ion was minimized using boric acid and L-cysteine mixed solution as a prereductant. The reconveries of tin at 20 ng/mL level in the solution containing fluoride ion were 100~108 %.

• Korean Journal of Materials Research
• /
• v.6 no.2
• /
• pp.188-196
• /
• 1996

LiOH 용액에서 핵연료피복관용 Zr합금의 부식이 가속되는 현상을 규명하기 위하여 autoclave를 이용하여 순수물, 다른 농도의 Li 용액 및 여러 가지 알카리 수산화물 조건에서 부식시험을 실시하였다. LiOH 용액에서 부식이 가속되는 현상은 용액 내에 Li 농도가 2.2ppm 이상에서부터 일어나기 시작하며 30ppm 이상에서는 급격한 가속 현상이 일어난다. 부식반응 동안에 발생되는 수소 흡수현상은 220ppm Li에서는 물에 비해 약 2배의 높은 수소흡수율을 나타내며 산화막은 주로 수소화물이 모여 있는 지역에서 우선적으로 성장한다. Li가속 부식기구와 관련하여 본 연구 결과는 지금까지 다른 연구자들이 제안한 부식 기구들과는 일치하지 않았다. LiOH 용액 내에서는 수소흡수와 수소화물 형성이 가속되고 이로 인해 산화막의 성질이 비보호성의 산화막으로 변함으로서 부식은 가속된다는 새로운 모델을 제시하였다.

• Journal of Hydrogen and New Energy
• /
• v.7 no.1
• /
• pp.93-110
• /
• 1996

금속수소화물은 열에너지 및 수소저장 또는 에너지변환장치 등에 많은 응용이 기대되고 있다. 특히 금속수소화물을 이용한 최근의 에너지 변환기술은 기술적으로 뿐만 아니라 경제성면에서도 그 가능성이 한층 높아지고 있다. 본문에서는 이와 같은 열변환장치의 하나인 열펌프의 제작에 필요한 동적특성을 P-C-T, 열 및 물질전달, 흡 탈착반응속도 그리고 성능 등의 관계에서 그 발전과정을 살펴보고, 그밖에 실용화에 따른 문제성도 논의하였다.

• Proceedings of the Korea Society for Energy Engineering kosee Conference
• /
• 2004.05a
• /
• pp.119-124
• /
• 2004

최근 소형 다기능, 고기능 전자장비의 개발로 인하여 고밀도 전원이 필요성이 대두되고 있다. 연료전지는 높은 전력 밀도를 가짐으로 인하여 소형 전원 장비에 가능성을 가지는 것으로 여겨지고 있다. 연료전지 중 특히 고분자 전해질 연료전지는 높은 전력밀도와 낮은 작동온도 등으로 인하여 이차전지의 자리를 대체할 수 있을 것으로 보여지지만 현재까지 연료 공급장치의 문제로 인하여 실용화되지 못하고 있다. 본 연구에서는 여러 가지 수소저장 물질 중에서 알칼리 붕소 수소화물을 이용하여 연료전지에 수소를 공급하고자 하며, 수소발생에 사용되는 촉매에 대한 연구를 진행하였다. 알칼리 붕소 수소화물의 수소발생 반응에 사용되는 촉매로는 Pt, Ru, Co, Ni 등이 사용되어질 수 있다. 이중에서 가장 수소발생 능력이 높은 촉매는 Ru이며, 비귀금속 촉매 중에는 Co가 높은 활성을 나타내었다. 본 연구에서는 Ru 촉매와 Co 촉매의 특성을 비교하였으며 연료전지에 수소를 공급할 수 있는 가능성을 확인하였다. Ru와 Co 촉매의 공통적인 특징은 알칼리 붕소화물인 NaBH$_4$의 농도가 높아질수록, 온도가 높아질수록 수소의 발생속도를 높이는 현상을 보였다. 또한 안정화제인 NaOH에 대하여, Ru의 경우는 농도가 높아질수록 수소발생 속도가 낮아졌으며, Co는 그 반대의 결과를 보였다. NaBH$_4$의 분해 반응으로 발생된 수소를 연료전지에 공급하여 2W급의 휴대폰용 연료전지를 구동할 수 있었다. 이로써 알칼리 붕소수소화물로부터 발생된 수소를 이용하여 안정적으로 연료전지를 구동할 수 있는 가능성을 확인하였다. 유류 분해정도를 파악하는 지시자로써 특정 무기 오염물질을 이용할 수 있을 가능성이 있으므로 좀더 이들 관계성에 대한 연구가 진행될 필요성이 있다고 판단된다.고 과학적으로 분석할 수 있는 방법이 될 수 있을 것으로 기대된다. 의미를 되새기는 것으로 짧은 연구를 시작하겠다. 등은 활성 값이 70% 이상으로 퇴적물 독성이 상대적으로 낮았다. 이중나선 DNA 함량은 28.4 % - 49%로 대조군에 비해서 감소가 크다. 대부분의 정점이 대조군의 30% 내외로 정점 간의 차이는 크지는 않다. 그러나 다른 측정자료와 같이 정점 22에서 18%로 최소치를 나타내고, 정점 2, 12에서 20% 내외의 값을 보인다. 종합적으로 볼 때 오염물질의 유입이 크고, 광양제철 인근 정점 들이 모두 다른 정점에 비해서 낮아서, 퇴적물 독성이 높은 정점으로 조사되었다.hiwo의 광합성 능력은 낮은 농도들에서는 대조구와 유사하였으나, 5 $\mu\textrm{g}$/l의 높은 농도에서는 초기에 매우 낮은 광합성 능력을 보이다가 시간이 경과하면서 대조군보다 더 높은 경향을 나타냈다. 이러한 결과는 식물플랑크톤이 benso[a]pyrene의 낮은 농도에서 노출될 때는 이 물질을 탄소원으로 사용할 가능성이 있음을 시사한다. 본 연구의 결과들은 연안해역에 benso[a]pyrene과 같은 지속성 유기오염물질이 유입되었을 때 내정여부에 따라 식물플랑크톤 군집내 종 천이와 일차생산력에 크게 영향을 미칠 수 있음을 시사한다.TEX>5.2개)였으며, 등급별 회수율은 각각 GI(8.5%), GII(13.4%), GIII(43.9%), GIV(34.2%)로 나타

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2007.04a
• /
• pp.87-90
• /
• 2007

Fuel cell power system was developed for high-endurance unmanned aerial vehicle (UAV). Liquid chemical hydride was selected as a fuel due to its high energy density. Liquid storage of the fuel is an ideal alternative solution of the existing compressed hydrogen storage. The fueling system that extracts hydrogen from chemical hydride consists of catalytic reactor, micro-pump, fuel cartridge, separator, and controller. The fuel cell power system including the fueling system and the fuel cell that generates electricity was integrated into a proposed UAV. The performance verification of the fuel cell power system was performed to use as a power plant of the UAV.