• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.4 s.37
• /
• pp.307-313
• /
• 2005

Electromigration behavior in the Sn96.5Ag3.0Cu0.5 solder lines was investigated and compared Sn96.5Ag3.0Cu0.5 with eutectic SnPb. Measurements were made for relevant parameters for electromigration of the solder, such as drift velocity, threshold current density, activation energy, as well as the product of diffusivity and effective charge number (DZ$\ast$). The threshold current density were measured to be $2.38{\times}10^4A/cm^2$ at $140^{\circ}C$ and the value represented the maximum current density which the SnAgCu solder can carry without electromigration damage at the stressing temperatures. The electromigration energy was measured to 0.56 eV in the temperature range of $110-160^{\circ}C$. The measured products of diffusivity and the effective charge number, DZ$\ast$ were $3.12{\times}10^{-10} cm^2/s$ at $110^{\circ}C$, $4.66{\times}10^{-10} cm^2/s$ at $125^{\circ}C$, $8.76{\times}10^{-10} cm^2/s$ at $140^{\circ}C$, $2.14{\times}10^{-9}cm^2/s$ at $160^{\circ}C$ SnPb solder existed incubation stage, while SnAgCu did not have incubation stage. It was thought that the diffusion mechanism of SnAgCu was different from that of SnPb.