• Journal of Conservation Science
• /
• v.32 no.2
• /
• pp.223-234
• /
• 2016

Two-component epoxy resin is widely used in the cultural heritage restoration field. However according to mixing ratio of resin and hardener, curing property, mechanical strength and chemical structure differ which have possibility to effect the stability of cultural heritage. Result of questionnaire survey shows hands-on workers in the conservation field tend to mix the epoxy resin with his or her eye measurement when the using amount is small or mix additional hardener to shorten the pot life of epoxy resin. This research aims to analyze the curing property, mechanical strength and chemical structure of rapid curing type epoxy resin and medium curing type one depending on relative ratio of 0.25~4 of hardener to resin. When the amount of hardener was 0.5~2 times more than the resin, exothermic heat and curing speed were both increased. In case of included hardener to resin was lower than official ratio, mechanical strength (tensile shear strength, tensile strength and compressive strength) became higher along with active cross-linking bonding of the epoxy resin. Medium curing type epoxy relatively had lower exothermic heat and slower reaction during curing process. It was observed to be put to definite point of mechanical strength under lower content of hardener than official ratio. While, hardener ratio more than twice the resin slowed down the curing greatly and lowered the adhesion strength also. In conclusion, under the lower mixing rate of hardener than official ratio would show relatively fast reaction with similar mechanical strength. Over the official ratio on the other hand, material property drops rapidly. Accordingly, mixing ratio of epoxy resin is expected to be influential to the stability of cultural heritage.

• Journal of Adhesion and Interface
• /
• v.13 no.4
• /
• pp.171-181
• /
• 2012

The demand characteristics of the conventional 12 kinds of epoxy resins which have been used for restoration of the ceramic relics were investigated to provide standards of the effective materials in this study. The result of durability analysis showed that a liquid type is more effective in ceramic relics (low damage, high strength), and a paste type is more effective in earthenware relics (high damage, low strength). The result of workability analysis appears that the liquid type is higher than the paste type, and a slow curing type is higher than a fast curing type in surface hardness. Therefore, in the case of the liquid type which is hard to reprocess due to high surface hardness, it is necessary to conduct a study on improving physical properties by adding filler. The result of the gloss analysis on epoxy resins showed that the liquid type (colorless) has higher gloss than the paste type, and the slow curing type has higher gloss than the fast curing type in liquid types. CDK-520A/520B and Araldite SV 427-2/HV 427-1 showed the most similar gloss to $700^{\circ}C$ earthenware, Devcon 5 minute, EPO-TEK 301-2, and Quik Wood showed the most similar gloss to celadon and whiteware, Quik Wood, EPO-TEK 301-2, and Devcon 5 minute showed the most similar gloss to buncheongware. It is necessary for conservator to decide the range of the restoration surface by predicting the increase and decrease of the restoration surface because most of the epoxy resins caused the volume change in curing process.

• Journal of Conservation Science
• /
• v.28 no.2
• /
• pp.131-139
• /
• 2012

The exothermic cure kinetics of epoxy resin was controlled by hardener containing fast and slow curing agents. The epoxy risen comprises hydrogenated bisphenol A-based epoxide (HBA), fast curing agent (FH) and slow curing agent poly(propyleneglycol)bis(2-aminopropylether) (SH). Talc was used as an inorganic additive. In the process of curing, cure kinetics along with temperature was monitored by differential scanning calorimeter (DSC) and thermocouple to show that the temperature increase was well controlled by adjusting the hardener mixture. Additionally, bending and tensile strengths of the epoxy/talc composites were also measured to be lower and higher with the amount of the talc inorganic additive, respectively. It is thus concluded that the increase in the temperature during exothermic curing reaction and mechanical properties of epoxy resins are tuned by optimizing hardener mixture for successful stone conservation.

• Journal of Conservation Science
• /
• v.28 no.3
• /
• pp.265-276
• /
• 2012

Physicochemical properties of HBA epoxy resins were controlled by varying hardener mixture and reactive diluent to improve applicability for stone conservation. The epoxy risen comprises hydrogenated Bisphenol-A based epoxide (HBA), fast curing agent (FH), slow curing agent poly(propyleneglycol)bis(2- aminopropylether) (SH) and difunctional polyglycidyl epoxide (DPE). Talc was used as an inorganic additive. The changes in viscosity and temperature during curing reactions depending on the composition of the epoxy resins were investigated. Additionally, bending, tensile and adhesive strengths were measured to identify the effective mechanical strength in stone conservation. Finally various compositions of epoxy resin/inorganic additives were developed for stone conservation by controlling cure kinetics and mechanical properties.