• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2007.04a
• /
• pp.47-50
• /
• 2007

This study investigates the properties of light weight foamed concrete (LWC) designed with various content of fine grains (FG). Test showed that LWC containing diverse powder materials with addition, more than 15% of FG, tended to decrease the fluidity of fresh concrete. 10% of FG content in LWC exhibited 4mm in sinking depth, which is the lowest value. This value dramatically increased at more than 15% of addition. However the concrete incorporating LSP proportionally increased the sinking depth in overall. As for the strength, the values of all specimens were under standardization of KS, except for the concrete adding 5 and 10% of FG. Apparent density of LWC showed the lowest value when used 10% of FG which was satisfied the 0.5 grade in KS. For the thermal conductivity, it was also indicated at 0.5 grade in KS, which is under $0.160W/(m{\cdot}k)$. In conclusion, it is demonstrated that adding 10% of FG in LWC was effective in the aspects of recycling of materials, cost effectiveness and quality.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.349-352
• /
• 2005

In this work, effects of limestone powder on hydration of $C_3A-CaSO_4\cdot2H_2O$ system was discussed based on the XRD Quantitative analysis, and the possibility of Delayed Ettringite Formation was also discussed. The early hydration of $C_{3}A$ was delayed by addition of $CaCO_{3}$ powder. The delay effect was enhanced by increasing of $CaCO_{3}$ content and finer powder of $CaCO_{3}$ addition. After consumption of $CaSO_4\cdot2H_2O$, the reaction of $CaCO_{3}$ is started. Delayed Ettringite Formation would take place because monosulfoaluminate is not stable in presence of $CaCO_{3}$. In order to prevent the delayed ettringite formation in $C_3A-CaSO_4\cdot2H_2O-CaCo_3$ system, the reduction of monosulfoaluminate formation is important. Therefore, by increasing the amount of $CaCO_{3}$ addition and finer $CaCO_{3}$ powder addition, the delayed ettringite formation can be prevented.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.497-500
• /
• 2008

This research carries out experiments for hydration exothermic rate and adiabatic temperature rise of concrete to examine the characteristics of the hydration heat of high flowing self-compacting concrete with a normal strength. As a result of the hydration exothermic rate experiment, the high flowing self-compacting concrete that used Lime stone powder and fly ash as polymers shows that its hydration heat amount reduces due to the reduction of unit cement. The result measured the adiabatic temperature rise of concrete presents that high flowing self-compacting concrete having lots of binder contents has a good performance in temperature reduction due to the effect of polymer and that triple adding high flowing self-compacting concrete has a similar temperature rise speed with conventional concrete. As a result of the research, high flowing self-compacting concrete shows a better temperature reduction performance for the binder content per unit than conventional concrete. In addition, it is judged that triple adding high flowing self-compacting concrete with a specified concrete strength 30 MPa is more beneficial in temperature reduction and early hydration heat than double adding high flowing self-compacting concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.4
• /
• pp.545-552
• /
• 2021

In this study, strength and durability evaluations are performed on vibrated-rolled method mortar mixtures containing desulfurized gypsum and ferronickel slag powder. Desulfurized gypsum and ferronickel slag fine powders were substituted for 25% limestone fine powders u sed in the manu factu re of VR tu bes, and mortar specimens were prepared u sing vibrated-rolled method. Accordingly, flexural and compressive strengths were performed to evaluate the strength, and chlorine ion penetration resistance and sulfuric acid resistance tests were performed to evaluate durability. Flexural and compressive strength were improved in the range 20 to 60% of desu lfu rized gypsu m among admixtu res, and the amou nt of passing charge decreased in the choride ion penetration resistance test in the range of 20 to 80% of desulfurized gypsum. As for the resistance to su lfu ric acid, when the proportion of desu lfu rized in the admixtu re was 40%, the strength and weight change rate according to the immersion period was reduced. Appropriate use of desulfurized gypsum and ferronickel slag powder is expected to improve performance in terms of strength and durability.