염기용액을 이용한 태양전지용 실리콘 기판의 절삭손상층 식각 특성 (The Saw Damage Etching Characteristics of Silicon Wafer for Solar Cell with Alkaline Solutions)

  • 권순우;이종협;윤세왕;김동환
    • 신재생에너지
    • /
    • 제5권1호
    • /
    • pp.26-31
    • /
    • 2009

  • The surface etching characteristics of single crystalline silicon wafer were investigated using potassium hydroxide (KOH) and tetramethylammonium hydroxide (TMAH). The saw damage layer was removed after 10min by KOH 45wt% solution at $80^{\circ}C$. The wafer etched at high temperature ($90^{\circ}C$) and in low concentration (4wt%) of TMAH solution showed an increased etch rate of silicon wafer and wavy patterns on the surface. Especially, pyramidal textures were formed in 4wt% TMAH solution without alcohol additives.

  • PDF

단결정 실리콘 태양전지용 텍스쳐링 용액의 계면활성제 첨가 효과 (Effects of Surfactant Addition in Texturing Solution for Monocrystalline Si Solar Cells)

  • 강병준;권순우;이승훈;천승주;윤세왕;김동환
    • 한국신재생에너지학회:학술대회논문집
    • /
    • 한국신재생에너지학회 2010년도 춘계학술대회 초록집
    • /
    • pp.74.1-74.1
    • /
    • 2010

  • 단결정 실리콘 태양전지 공정에서 이방성 습식 식각 용액을 이용하여 기판 표면에 피라미드 구조를 형성하는 것을 텍스쳐링이라고 한다. 실리콘 기판의 표면을 식각하여 요철구조를 만들어줌으로써 셀 내부로 입사되는 광량을 증가시켜 태양전지의 단락 전류 및 효율 향상 효과를 얻을 수 있다. 일반적인 태양전지 공정에서는 요철구조를 형성할 시 따로 마스크를 사용하지 않으며, 태양전지 급 웨이퍼를 절삭손상층 식각 한 후, 강염기성 용액과 알코올의 혼합용액에 담가서 이방성 식각을 실시하여 요철 구조를 형성한다. 본 연구는 기존의 텍스쳐링 공정에서 사용되는 대표적인 용액인 수산화칼륨(potassium hydroxide, KOH)과 알코올의 혼합용액과 사메틸수산화암모늄(Tetramethylammonium Hydroxide, TMAH)과 알코올의 혼합용액에 Triton X-100 계면활성제를 각각 첨가하여 실험을 진행하였다. 식각된 태양전지용 실리콘 기판의 표면은 주사전자현미경(Scanning Electron Microscope)을 통하여 관찰하였고, 분광광도계(UV/VIS/NIR Spectrophotometer)로 반사도 값을 측정하여 기판의 특성을 평가하였다.