• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.156-157
• /
• 2011

고경도 Ni-Co 합금 도금액 개발을 위하여 Ni과 Co의 함량 조성비와 전류밀도에 따라 전기도금을 실시하였다. Ni과 Co의 함량비는 Ni의 농도를 일정하게 유지시키고 Co의 농도를 10~30g/${\ell}$로 하여 실험을 하였다. Ni과 Co의 함량 조성비에 따른 합금 도금층의 성분을 EDS를 이용하여 분석하였고 전류밀도별 표면형상을 FE-SEM을 이용하여 분석하였다. 그리고 도금층의 성분에 따른 경도값을 비커스 경도계를 이용하여 분석하였다.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.9
• /
• pp.142-148
• /
• 2004

It is already known that hardness number of cold-forged product is in close conjunction with its effective strain. This paper presents the method to predict the relation between effective strains and hardness by using FE-simulation of hardness test from the conception that hardness indicates resistance to plastic deformation. The results of FE-simulation for the materials are compared with those of experiments and also compared with those of experiments in reference to show the feasibility of the proposed method. In addition, the present method was applied to the cold-forged product to verify the relation between hardness and effective strain. As a result, the predicted hardness number by the present method is in good agreement with experimental values. Prediction of hardness fur a cold-forged product comes to be possible by estimating the relation between effective strain and hardness using the proposed method in this study.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.305-305
• /
• 2012

Ni-W 합금의 고경도 특성을 연구하기 위하여 전해 도금 방법을 이용하여 Ni-W 합금을 제작하였다. 전해 도금시 여러 가지 제어인자 중 전류밀도, pH, Ni 금속염의 양 그리고 도금욕의 온도 등을 변수로 하여 실험을 하였다. 도금층 내 Ni과W의 함량 조성비를 EDS를 이용하여 분석하였으며, 각각의 변수에 따른 Ni-W 합금의 결정구조를 XRD를 이용하여 측정하였다. Ni-W 합금 도금층내 성분 조성비 및 결정구조에 따른 경도를 비커스 경도계를 이용하여 측정하였다.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.36 no.3
• /
• pp.440-447
• /
• 2009

This study was performed to compare the wear resistance of sealant and flowable resins for analyzing the effect of flowable resin as a sealant in preventive resin restorations. Specimens were made and Vicker's hardness number and surface roughness were measured. SEM observations of the polished and abraded surfaces were established. Kruskal-Wallis rank test and Mann-Whitney U test at the significant level of ${\alpha}$=0.05 were used. The following results were obtained: 1. The microhardness was decreased among groups in following order: Z350 (3M ESPE, U.S.A), Estelite (Tokuyama Dental, Japan) and Ultraseal (Ultradent, U.S.A). There were significant differences in all groups (p<0.0001). 2. The surface roughness was decreased among groups in following order: Ultraseal XT plus, Palfique Estelite LV and Filtek Z350 flowable. However, there is no statistically significant differences in roughness among Estellite, Z350 and Ultraseal at the significance level of ${\alpha}$=0.05, with p=0.116 3. SEM observation of the unworn and worn surfaces revealed the qualitative differences in the wear appearance among groups. The results in this study indicate that flowable resin is better than sealant in aspect of physical properties.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.23 no.4
• /
• pp.315-321
• /
• 2003

The integrity of the turbine rotors can be assessed by measuring the material properties at service temperature. In order to evaluate the remanent life of turbine rotor steel nondestructively, a measurement system of reversible magnetic permeability using an alternating perturbing magnetic field was constructed. We present a new non-destructive method to evaluate the remanent life of 1Cr-1Mo-0.25V steel using the value of reversible magnetic permeability. This method is based on the existence of reversible magnetic permeability in the differential magnetization around the coercive field strength. We measured the first harmonics voltage induced in a coil using a lock-in amplifier tuned to an exciting frequency. The Results of reversible magnetic Permeability and Wickers hardness on the aged samples show that the peak interval of reversible magnetic permeability (PIRMP) and Vickers hardness decreases as aging time increases. A softening curve is obtained from the correlation between Vickers hardness and the PIRMP. This curve can be used as a non-destructive method to evaluate the remanent life of turbine rotor steel.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.25 no.5
• /
• pp.377-383
• /
• 2005

Because explosive fluid is used at high temperature or under high pressure in petrochemistry and refined oil equipment, the interest about safety of equipments is intensive. Specially, the safety of high pressure reactor vessel is required among them. The material selected in this study is 2.25Cr-1Mo steel that is widely used for high pressure reactor vessel material of petrochemical plant. Eight kinds of artificially aged specimens were prepared by differing from aging periods under three different temperatures. The material was iso-thermally heat treated at higher temperatures than $391^{\circ}C$ that is the operating temperature of high pressure reactor vessel. Vickers hardness properties and electrical resistivity properties about artificially aged material as well as un-aged material were measured, and master curves were made out from the correlation with larson-Miller parameter. And electrical resistivity properties as well as Victors hardness properties measured at high pressure reactor vessel of the field were compared with master curves made out in a laboratory. Degradation evaluation possibility in the field of high pressure reactor vessel by using electrical resistivity method was examined. Electrical resistivity property measured in the field is similar with that of artificially aged material in similar aging level.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.47 no.3
• /
• pp.320-326
• /
• 2020

The aim of this study was to compare compressive strength and microhardness of recently introduced alkasite restorative materials with glass ionomer cement and flowable composite resin. For each material, 20 samples were prepared respectively for compressive strength and Vickers microhardness test. The compressive strength was measured with universal testing machine at crosshead speed of 1 mm/min. And microhardness was measured using Vickers Micro hardness testing machine under 500 g load and 10 seconds dwelling time at 1 hour, 1 day, 7 days, 14 days, 21 days and 35 days. The compressive strength was highest in composite resin, followed by alkasite, and glass ionomer cement. In microhardness test, composite resin, which had no change throughout experimental periods, showed highest microhardness in 1 hour, 1 day, and 7 days measurement. The glass ionomer cement showed increase in microhardness for 7 days and no difference was found with composite resin after 14 days measurement. For alkasite, maximum microhardness was measured on 14 days, but showed gradual decrease.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.30 no.5
• /
• pp.464-470
• /
• 2010

The integrity of the industrial equipment in use under high temperature and high pressure must be assessed by regularly measuring the degraded mechanical properties during service time. In order to nondestructively monitor the degraded mechanical properties of industrial equipment, a measuring method of the reversible permeability(RP) using surface type probe is presented. The method for measuring the RP is based on that RP is the differential value of hysteresis loop. The RP is exactly the foundation hatmonics induced in a detecting coil measured by lock-in amplifier tuned to a frequency of the alternating perturbing magnetic field. The peak of RP is measured around the coercive force. Steel material used in this work was 12Cr ferritic heat resisting steel. The eleven kinds of samples aged during different times under same temperature ($700^{\circ}C$) were prepared. Peak interval of reversible permeability(PIRP), Vickers hardness, and tensile strength measured for the aged samples decreased abruptly for short aging time (below 500 h), but the change became small at a long aging time. Vickers hardness and tensile strength linearly decreased as RIRP decreased, so the degraded mechanical properties of 12Cr ferritic heat resisting steel could be nondestructively evaluated by measuring RIRP.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.196-196
• /
• 2016

치과나 기공소로부터 높은 원가로 인한 재료선택에 어려움을 겪고 있어 귀금속 금합금의 물성을 가질 수 있도록 하면서 가격급등으로 인한 문제 해결하기 위한 비귀금속 합금으로 대체가 필요하기에 이에 따른 연구가 이루어져 국산 제품의 상품화를 위해 파라듐을 이용하여 적합한 새로운 합금을 개발하는 것이 필요하다. 치과용 골드합금은 미국치과의사 협회의 구정에 의하면 1형부터 4형까지 분류하고 있으며 3형에 해당하는 강도와 기계적인 특성을 갖도록 파라듐으로 대체하는 연구가 진행중이거나 시판되고 있다. 따라서 본 연구에서는 2형, 3형 및 4형을 대체가능하도록 팔라듐을 기반으로 한 새로운 합금을 설계하고 합금의 성분원 소인 Au(1~5), Pd(20~25), Ag(70~75), In(1.5) 및 Zn(2)등으로 조성을 변화시켜 측량 후 합금을 제조하기 위하여 아르곤 분위기하의 진공아크용해로를 이용하여 용해하였다. 정량된 금속을 진공아크 용해로에 장입하고 용해는 균질한 합금이 되도록 최소한 6회 이상 용융을 실시하며 합금성분의 손실이 발행하지 않도록 보정을 하였다. 합금의 미세조직 관찰을 위하여 샘플을 고속 다이아몬드 정밀 절단기(Acculom-5, STRUERS, Denmark)를 이용하여 절단한 후 2000 grit의 Sic 연마지에서 단계적으로 $0.3{\mu}m$ 알루미나 분말까지 연마한 후 초음파 세척을 하였다. 준비한 시편은 KCN과 $(NH_4)_2S_2O_8$을 1:1로 혼합한 부식액으로 에칭한 후 OM과 SEM을 이용하여 조직을 관찰하였으며 각 샘플의 성분변화는 EDS 분석을 통해 확인하고 결정구조는 XRD를 사용하여 분석하였다. 경도시험은 비커스경도시험기를 이용하여 5kg의 하중을 30초간 작동시켜 압흔을 연결된 micron으로 평균값을 측정하였다. 각 시편의 부식거동은 POTENTIOSTAT(Model PARSTAT 2273, EG&G, USA)을 이용하여 구강 내환경화 유사한 $36.5{\pm}1^{\circ}C$의 0.9% NaCl에서 실시하였다. 인가전위는 -1500mV에서 1000mV까지 1.67 mV/min의 주사속도로 인가하여 시험을 수행하였으며 분극곡선으로부터 부식전위와 부식전류밀도 및 부동태영역의 전류밀도로 금속의 용출거동을 조사하였으며 부식이 끝난 시편은 FE-SEM과 EDS를 사용하여 조사하였다. 기계적인 특성은 Pd-Ag에 3wt%의 Au를 첨가한 합금이 Pd-Ag에 1.5wt%합금을 첨가한 경우에 비하여 기계적인 특성이 증가하고 내식성이 크게 증가하였다. 이들 합금에 Cu를 11wt%를 첨가한 경우는 비커스경도가 200이상으로 높게 나타났지만 내식성이 크게 감소하였다.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.36 no.3
• /
• pp.168-175
• /
• 2020

Purpose: The purpose is to test and evaluate the physical properties of commonly used temporary restoration materials and newly emerged materials. Materials and Methods: Four groups of polymer materials were evaluated: Polymethyl methacrylate (PMMA) 2 groups, Polyetheretherketone (PEEK), Polycarbonate. Four physical properties were tested: surface hardness, bending strength, abrasion resistance during wear, wear behavior. The 3-axis bending strength and Vickers hardness test were measured using a universal testing machines respectively. The microstructure was observed with a scanning electron microscope and weight comparison was evaluated after 100,000 chewing tests using a chewing simulator. Kruskal wallis test was performed to evaluate statistical significance. Results: The four groups showed the highest flexural strength and Vickers hardness of PEEK, followed by PC, PMMA-H, PMMA-T. Microstructure observation also showed the least surface roughness in the PEEK group, followed by PC, PMMA-H, PMMA-T. Conclusion: PC is considered to have sufficient mechanical properties that can be applied to the manufacture of temporary teeth. However, further studies, such as biocompatibility, are considered to be necessary for practical clinical applications.