• Journal of Welding and Joining
• /
• v.21 no.2
• /
• pp.64-69
• /
• 2003

The bonding phenomena and mechanical property of duplex stainless steel during brazing have been investigated. The UNS32550 was used for base metal, and the MBF50 was used for insert metal. Brazing was carried out under the various conditions (brazing temperature : 1473K, 1498K, holding time : 0∼1.8ks). There were various microconstituents in the bonded interlayer because of reaction between liquid insert metal and base metal. In the early stage of brazing, BN is formed in the bonded interlayer and base metal near the bonded layer. Cr made is formed in the bonded interlayer. The amount of BN and Cr nitrides decrease with the increase of bonding temperature and holding time. Superior shear strength of 550MPa is obtained by restraining the formation of nitrides. (Received January 17, 2003)

• Journal of Welding and Joining
• /
• v.19 no.5
• /
• pp.534-539
• /
• 2001

The formation mechanism of microconstituents in brazed joints of duplex stainless steel and Cr-Cu alloy which is an essential process of rocket engine manufacturing was investigated using Cu base insert metal. $SUS329J_3L$ and C18200 were used for base metal and AMS 4764 was used for insert metal. The brazing was carried out under various conditions. There were various phases in the joints, because of reaction between liquid insert metal and base metals. Since liquid insert metal reacts with duplex stainless steel, liquid Cu from insert metal infiltrated into the $\alpha/\beta$ interface of duplex stainless steel. Through the process of Cu infiltration, isolated stainless steel pieces come into the liquid insert metal. Since liquid insert metal reacts with Cr-Cu alloy. Cr precipitates from C18200 come into the liquid insert metal. With increment of bonding temperature and holding time, amounts and sizes of phases increased. but Cr-Mn compounds decreased at 1303k for 1.2ks and Mn-rich phases disappeared Fe-Cr compounds formed.

• Journal of Welding and Joining
• /
• v.34 no.2
• /
• pp.36-45
• /
• 2016

Recent developing tendency for technologies of high efficient brazing are studied by searching of NDSL, Science Direct, KIPRIS, PCT and so on. Active metal brazing, arc brazing, fluxless brazing, brazing with low melting point, reactive air brazing, laser brazing, laser droplet brazing are investigated. By optimal selecting of the above mentioned technologies, it needs to investigate an economical metallurgical design and the advanced brazing methods. To improve the embrittlement of intermetallic compound at brazing interface, it must be studied the inexpensive variant metals including nonmetals and the heat sources(MIG, TIG, Laser) by hybrid techniques.

• Journal of Welding and Joining
• /
• v.32 no.1
• /
• pp.66-70
• /
• 2014

In Ti active brazing of YSZ to STS 430 using Ag-Cu Filler Metal, the effect of Ti contents on the shear bonding strength were investigated together with the effect of brazing temperature and holding time. The addition of Ti in Ag-Cu Filler Metal increased the bonding strength up to 4.68% Ti, followed by the decrease with further addition. This seems to be caused by formation of TixOy at the reaction layer. Brazing temperature was optimized at $960^{\circ}C$ among a given temperature ranges. The addion of Sn to Ag-Cu filler metal brought the decrease of its melting temperature its melting temperature without a significant decrease of bonging strength.

• Journal of Welding and Joining
• /
• v.7 no.2
• /
• pp.12-24
• /
• 1989

천이액상확산접합법은 접합계면에 일시적으로 액상이 형성되기 때문에, 고상확산접합법과 비교 하여 비교적 쉽게 금속결합을 이룰 수 있을 뿐만 아니라, 정밀하게 표면을 가공할 필요가 없으 며, 접합압력이 거의 필요 없다는 것이 잇점이라고 할 수 있다. 도한, 접합온도에서 등온응고되 기 때문에, 브레이징법과 비교하여 접합계면에 취약한 금속간화합물(Metallic Compound)이 생 성되지 않으므로, 기계적성질 및 내식성이 우수한 접합이음부를 얻을 수 있다는 잇점이 있다. 따라서, 본 접합법은 원리적으로 모재(Base Metal)와 거의 같은 정도의 물리적, 화학적, 기계적 성질을 갖는 접합이음부(Joint or Bonded Interlayer)를 얻을 수 있는 접합법이라고 생각되어진 다. 본 해설에서는 천이액상확산접합법의 기본원리, 접합기구, 접합인자 및 실용된 예에 대해서 서술하고자 한다.

• Journal of the KSME
• /
• v.57 no.11
• /
• pp.44-49
• /
• 2017

항공용 가스터빈엔진 개발은 전문성과 경험을 요하는 많은 요소기술과 시험설비, 그리고 상당한 개발기간과 세부단계별 검증을 필요로 하는 복잡한 프로세스로 구성된다. 고온/고압 및 고속 회전 등 매우 가혹한 조건에서 운용되는 제품 특성 때문에 장납기 및 고가의 내열/고강도 소재 혹은 주단조 개발, 정밀한 제작 치수 및 공정관리, 코팅/브레이징/용접 등 고 난이도의 특수공정관리, 정교한 조립 및 다양한 종류의 엔진 검증 시험 등을 필요로 하며 이러한 이유로 상세설계 이후의 조립/시험 단계에서 설계변경이 발생할 경우 개발일정 및 비용 관점에서 제품개발에 큰 부담을 초래하게 된다. 공력/이차유로/열전달/구조/동특성/시스템 설계 등 개발 단계별 다양한 기법의 시뮬레이션 및 사전 검증시험 등의 중요성이 크게 부각된다. 이 글에서는 한화테크윈(혹은 HTW 로 표기)의 엔진개발 경험에 기반한 단계별 개발 시험의 종류, 필요 시험 설비 및 한화테크윈의 설비 운용 특징에 대해 소개하고자 한다.

• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.134-146
• /
• 1995

Aluminium nitride(AlN) is currently under investigation as potential candidate for replacing alumium oxide(Al$_{2}$ $O_{3}$) as a substrate material for for electronic circuit packaging. Brazing of aluminium nitride(AlN) to Cu with Ag base active alloy containing Ti has been investigated in vacuum. Binary Ag$_{98}$ $Ti_{2}$(AT) and ternary At-1wt.%Al(ATA), AT-1wt.%Ni(ATN), AT-1wt.% Mn(ATM) alloys showed good wettability to AlN and led to the development of strong bond between brate alloy and AlN ceramic. The reaction between AlN and the melted brazing alloys resulted in the formation of continuous TiN layers at the AlN side iterface. This reaction layer was found to increase by increase by increasing brazing time and temperature for all filler metals. The bond strength, measured by 4-point bend test, was increased with bonding temperature and showed maximum value and then decreased with temperature. It might be concluded that optimum thickness of the reaction layer was existed for maximum bond strength. The joint brazed at 900.deg.C for 1800sec using binary AT alloy fractured at the maximum load of 35kgf which is the highest value measured in this work. The failure of this joint was initiated at the interface between AlN and TiN layer and then proceeded alternately through the interior of the reaction layer and AlN ceramic itself.

• Journal of Welding and Joining
• /
• v.14 no.4
• /
• pp.99-108
• /
• 1996

The microstructure and bond strength are examined on the SiC/SiC and SiC/mild steel joints brazed by the Ag-Ti based alloys with different Ti contents. In the SiC/SiC brazed joints, the thickness of the reaction layers at the bond interface and the Ti particles in the brazing alloy matrices increase with Ti contents. When Ti is added up to 9 at% in the brazing alloy. $Ti_3SiC_2$ phase in addition to TiC and $Ti_5Si_3$ phase is newly created at the bond interface and TiAg phase is produced from peritectic reaction in the brazing alloy matrix. In the SiC/mild steel joints brazed with different Ti contents, the microstructure at the bond interface and in the brazing alloy matrix near SiC varies similarly to the case of SiC/SiC brazed joints. But, in the brazing alloy matrix near the mild steel, Fe-Ti intermetallic compounds are produced and increased with Ti contents. The bond strengths of the SiC/SiC and SiC/mild steel brazed joints are independent on Ti contents in the brazing alloy. There are no large differences of the bond strength between SiC/SiC and SiC/mild steel brazed joints. In the SiC/mild steel brazed joints, Fe dissolved from the mild steel does not affect on the bond strength of the joints. Thermal contraction of the mild steel has nearly no effects on the bond strength due to the wide brazing gap of specimens used in the four-point bend test. The brazed joints has the average bond strength of about 200 MPa independently on Ti contents, Fe dissolution and joint type. Fracture in four-point bend test initiates at the interface between SiC and TiC reaction layer and propagates through SiC bulk. The adhesive strength between SiC and TiC reaction layer seems to mainly control the bond strength of the brazed joints.

• Journal of Welding and Joining
• /
• v.35 no.2
• /
• pp.23-29
• /
• 2017

Mechanical properties and hardness distributions in arc brazed joints of Dual phase steel using Cu-Al insert metal were investigated. The maximum tensile shear load was 10.4kN at the highest brazing current. It was about 54% compared to tensile load of base metal. This joint efficiency is higher than that of joint of DP steel using Cu-based filler metals which are Cu-Si, Cu-Sn. Fracture positions can be divided into two types. Crack initiation commonly occurred at three point junction among upper sheet, lower sheet and the fusion zone. However crack propagations were different with increasing the brazing current. In case of the lower current, it instantaneously propagated along with the interface between fusion zone and upper base material. On the other hand, in case of higher current, a crack propagation occurred through fusion zone. When the brazing current is low (60, 70A), the interface shape is flat type. However the interface shape is rough type, when the brazing current is high (80A). It is thought that the interface shapes were the reason why the crack propagations were different with brazing current. The interface was the intermetallic compounds which consisted of $(Fe,Al)_{0.85}Cu_{0.15}$ IMC formed by crystallization at $1200^{\circ}C$during cooling. Therefore the maximum tensile shear load and the fracture behavior were determined by a interface shape and effective sheet thickness of the fracture position.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2007.11a
• /
• pp.114-118
• /
• 2007

Design and fabrication of a 30-tonf-class full-scale regenerative cooling combustion chamber of a liquid rocket engine for a ground hot firing test are described. It has chamber pressure of 60 bar and nozzle expansion ration of 12 and manufactured to have a single welded structure of· the mixing head and the chamber. The material of the mixing head is STS316L which has excellent mechanical property in cryogenic condition. The chamber comprise of the cylinder, nozzle throat, and 1st/2nd nozzle parts. The material of the inner jacket is copper alloy/STS329J1/STS316L and that of the outer jacket is STS329J1. The components of· the combustor were manufactured by mechanical processing including lathing, milling, MCT, rolling and pressing. The machined components were integrated to a single body by means of general welding, electron beam welding(EBW), and brazing.