• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.5
• /
• pp.104-111
• /
• 2015

This study shows the mechanical properties of alkali-activated slag cement (AASC) synthesized using sulfate with NaOH solution. The used sulfates were calcium sulfate ($CaSO_4$, denoted CS) and sodium sulfate ($Na_2SO_4$, denoted SS). The replacement ratio of sulfates was 2.5, 5.0, 7.5 and 10.0% by weight of slag. NaOH solution of 2M and 4M concentration was used. A sample was activated with sulfate and activated with blended activator (blending NaOH solution with sulfate) respectively. 24 mix ratios were used and the water-binder weight ratio for the test was set 0.5. This research carried out the compressive strength, flexural strength, ultrasonic pulse velocity (UPV), absorption and X-ray diffraction (XRD). In the case of samples with CS, sample with 7.5% CS, sample with 2M NaOH+5.0% CS and sample with 4M NaOH+5.0% CS showed the good performance in the strength development. In the case of samples with SS, sample with 10.0% SS, sample with 2M NaOH+7.5% SS and sample with 4M NaOH+2.5% SS obtained good performance in strength. The results of UPV and water absorption showed a similar tendency to the strength properties. The XRD analysis of samples indicated that the hydration products formed in samples were ettringite, CSH and silicate phases. In this study, it is indicated that when compared to the use of sulfate only, the use of both sulfate and NaOH solution makes mechanical properties of AASC better.

• The Korean Journal of Mycology
• /
• v.47 no.4
• /
• pp.359-371
• /
• 2019

To optimize the expression and secretion of ferritin protein associated with ion storage in the mushroom, Pleurotus eryngii, a recombinant secretion vector, harboring the ferritin gene, was constructed using a pPEVPR1b vector under the control of the CaMV 35S promoter and signal sequence of pathogen related protein (PR1b). The ferritin gene was isolated from the T-Fer vector following digestion with EcoRI and HindIII. The gene was then introduced into the pPEVPR1b secretion vector, and it was then named pPEVPR1b-Fer. The recombinant vector was transferred into P. eryngii via Agrobacterium tumefaciens-mediated transformation. The transformants were selected on MCM medium supplemented with kanamycin and its expression was confirmed by SDS-PAGE and western blotting. Expression of ferritin protein was optimized by modifying the culture conditions such as incubation time and temperature in batch and 20 L airlift type fermenter. The optimal conditions for ferritin production were achieved at 25℃ and after incubating for 8 days on MCM medium. The amount of ferritin protein was 2.4 mg/g mycelia, as measured by a quantitative protein assay. However, the signal sequence of PR1b (32 amino acids) seems to be correctly processed by peptidase and ferritin protein may be targeted in the apoplast region of mycelia, and it might not be secreted in the culture medium. The iron binding activity was confirmed by Perls' staining in a 7.5% non-denaturing gel, indicating that the multimeric ferritin (composed of 24 subunits) was formed in P. eryngii mycelia. Mycelium powder containing ferritin was tested as a feed additive in broilers. The addition of ferritin powder stimulated the growth of young broilers and improved their feed efficiency and production index.

• Maxillofacial Plastic and Reconstructive Surgery
• /
• v.33 no.2
• /
• pp.103-111
• /
• 2011

Purpose: Choukroun's platelet-rich-fibrin (PRF) is composed of platelets, white blood cells and fibrin matrix. It does not induce enough bone formation by itself but it can improve bone formation with calcium. Silk fibroin does not cause inflammatory reactions because it is bio-compatible and degradable. The purpose of this study was to exam the bone formation when a combination of Choukroun's PRF and silk fibroin was used. Methods: In this study, cell reactions to silk powder with differing molecular weights was first tested to select the appropriate silk powder. Then we applied these bone graft materials on defects of skull and in a peri-implant bony defect model in New Zealand rabbits. The results between the experimental and control s (non-grafted) group were analyzed. Results: The small sized silk fibroin powder showed increased cellular proliferation for bone-regeneration. There was no statistically significant difference between the experimental group and the control group at 6 weeks, but more new bone formation was observed in the combination graft group at 12 weeks (P<0.05). And in the dental implant model, the combination bone graft group showed much improved torque test results, which was statistically significant. Histomorphometric analysis showed more regenerated cortical bone and a higher mean bone to implant in the experimental group. Both were statistically significant. Conclusion: The combination graft of Choukroun's platelet-rich-fibrin (PRF) and silk fibroin powder can successfully restore the bony defects in a skull defected model and a peri-implant bony defects model.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.204-209
• /
• 2002

In this study, $UO_4{\cdot}2NH_4F$, the precipitates which has low solubility, was obtained by chemical precipitation method to recover and reuse the trace uranium from the liquid waste producing in AUC process and for this compound it was characterized by means of chemical analysis, TG-DTA, XRD and FT-IR analyses. This compound was analyzed as $UO_4{\cdot}2NH_4F$ and shape of this precipitate was hexagonal type, having the size of 2∼3 ${\mu}m$. Also, the intermediates were obtained as $UO_4F,\;UO_4,\;UO_3,\;and\;U_3O_8$ by the thermal decomposition over the temperature of 220, 310, 515 and 640$^{\circ}C$, respectively. It is concluded that under the condition of a constant heating rate of 5$^{\circ}C$/min in air atmosphere range of between room temperature and 800$^{\circ}C$, thermal decomposition reaction mechanism of $UO_4{\cdot}2NH_4F$ is as follow; $UO_4{\cdot}2NH_4F{\rightarrow}UO_4F{\rightarrow}UO_4{\rightarrow}UO_3{\rightarrow}U_3O_8$.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.3
• /
• pp.37-43
• /
• 1999

Co-firing incompatibility between the low temperature sinterable Glass/ceramic and Ag-thick film was studied. The dielectric material, which has been developed for microwave frequency applications, consists of $SiO_2-TiO_2-Bi_2O_3$-$Bi_2O_3$-RO system(RO:BaO -CaO-SrO) crystallizable glass and $Al_2O_3$as a ceramic filler. The large camber in the sintered specimen and cracks at the Ag-film under the influence of the camber occurred due to the difference of densification rate between the ceramic sheet and the Ag-film $B_2O_3$addition to the Glass/ceramic mixture reduced the severe camber. The cambers decreased with increasing the $B_2O_3$ content, and completely disappeared with 14 vol% $B_2O_3$addition. With additions of $B_2O_3$, $\varepsilon_{r}$ decreased abruptly, Q$\times$f value increased largely and the $\tau_f$ value of the material quickly shifted to positive one.

• Journal of the Korea Concrete Institute
• /
• v.24 no.5
• /
• pp.509-516
• /
• 2012

The aims of this research is to develop a fire resistant admixture to enhance high-pressured pumping of high-strength concrete (HSC) with a compressive strength of 60~80 MPa. Generally, the efficiency of HSC high-pressured pumping is dramatically reduced due to entanglement of short fibers added to prevent fire spalling. Therefore, the fire resistant admixture that can facilitate pumping of fire resistant HSC is urgently needed presently. The fire resistant HSC mix is comprised of Polypropylene fiber, Nylon fiber and Polymer powder. The test results showed that the slump-flow was improved by approximately 70% of the HSC without fire resistant admixture. However, the air void content was increased slightly due to the addition. The standard design compressive strength at 28-days was satisfied, while its flexural strength was similar to the concrete without the admixture. Since the flexural strength was 12~15% of its compressive strength, the general trend of flexural to compressive strength ratio in normal concrete was maintained. Even though its elastic modulus was decreased by adding the admixture, the study results showed that the concrete can be used for construction since all of the test results exceeded the code requirements.

• Applied Chemistry for Engineering
• /
• v.21 no.5
• /
• pp.590-592
• /
• 2010

Li-Mn spinel ($LiMn_2O_4$) is prepared by a hydrothermal process with K-Birnessite ($KMnO_4{\cdot}yH_2O$) as a precursor. The K-Birnessite obtained via a hydrothermal process with potassium permanganate [$KMnO_4$] and urea [$CO(NH_2)_2$] as starting materials are converted to Li-Mn spinel nanoparticles reacting with LiOH. The molar ratio of LiOH/K-Birnessite is adjusted in order to find the effect of the ratio on the structural, morphological and electrochemical performances of the Li-Mn spinel. X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDS), and thermogravimetry (TG) are used to investigate the crystal structure and morphology of the samples. Galvanostatic charge and discharge are carried out to measure the capacity and rate capability of the Li-Mn spinel. The capacity shows a maximum value of $117\;mAhg^{-1}$ when the molar ratio of LiOH/K-Birnessite is 0.8 and decreases with the increase of the ratio. However the rate capability is improved with the increase of the ratio due to the reduction of the particle size.

• 한국공간정보시스템학회:학술대회논문집
• /
• 2000.06a
• /
• pp.181-186
• /
• 2000

국가지리정보체계사업을 시작으로 여러 응용분야에서 지리정보시스템을 구축하고 있으며, 특히 지자체에서는 도시정보화 차원에서 UIS(Urban Information System;도시정보시스템)를 구축하고 있다. 지자체의 업무들은 지자체의 상황에 따라 조금씩 차이를 보이지만 업무 단위로 따져 볼 때 공통적으로 수행되는 업무들이 많으며, 지리정보 관련 업무 또한 예외가 아니다. 지금까지 각 지자체의 도시정보시스템은 공통업무에 대하여 중복개발이 불가피 하였으며, 재사용성을 기대하기 어려웠다. 이런 비효율을 극복하는 방안으로 컴포넌트 기술이 대두되었으며, 컴포넌트 기술을 이용하여 업무변화에 유연하고 재활용을 극대화할 수 있는 업무 컴포넌트 개발이 필요한 시점이다. 본 논문은 지자체의 지리정보 관련 업무의 하나인 하수도 업무 중 하수배출용량 산정을 위한 하수도 관망해석 컴포넌트 설계를 제시하였다. 하수도 관망해석 컴포넌트는 하수배출용량을 산정하고, 하수 배출용량을 토대로 통수능이 부족한 하수관거를 추출하며, 통수능 부족 관거에 대하여 적정한 교체 관경 결정을 지원할 수 있도록 설계하였다 컴포넌트 설계과정은 표준업무를 지원할 수 있도록 업무분석을 수행하였으며, 이의 결과물로 하수도 관망해석 알고리즘을 도출하였으며, 알고리즘을 기반으로 하수도 관망해석 업무를 수행하는 하수도 관망해석 컴포넌트를 설계하고 설계 내용을 UML(Unified Modeling Language)로써 명세화 하였다. 현재 설계에 따라 하수도 관망해석 컴포넌트가 개발되고 있으며, 개발된 컴포넌트를 이용한 하수도 관망해석 시스템을 구축할 예정이다. 추후에는 하수도 관망해석 컴포넌트와 하수도 업무 컴포넌트와의 통합부분에 대한 연구가 진행되어야 할 것이다.7.0로 하고 표준(標準) EDTA 용액(溶液)을 소량(少量)넣고 8N-KOH로 pH $12{\sim}13$으로 하고 N-N 희석분말(稀釋粉末)을 지시약(指示藥) 으로써 표준(標準) EDTA 용액(溶液)으로 적정(滴定)하여 Ca 치(値)를 얻었다. Ca와 Mg의 합계결정치(合計決定値)와 Ca 적정치(滴定値) 차(差)로 Mg 치(値)를 얻었다. 음(陰) ion 구분(區分)으로부터 상법(常法)에 의하여 $MgNH_4PO_4$의 침전(沈澱)을 만들어서 HCl에 녹키고 일정량(一定量)의 표준(標準) EDTA 용액(溶液)을 넣어 pH 7.0로 한다음 완충액(緩衝液)으로 pH 10으로 하고 BT 지시약(指示藥)을 써서 표준(標準) Mg $SO_4$용액(溶液)으로 적정(滴定)하여 P 치(値)를 얻었다. 본법(本法)으로 Na-phytate를 분석(分析)한 결과(結果) Na-phytate의 분자식(分子式)을 $C_6H_6O_{24}P_6Mg_4CaNa_2{\cdot}5H_2O$라고 하였을 때의 이론치(理論値)에 비(比)하여 P가 98.9% Cark 97.1%, Mg가 99.1%이고 통계처리(統計處理)한 결과분석치(結果分析値)와 이론치(理論値)는 잘 일치(一致)된다. 그러나 종래법(從來法)에 의(依)한 분석치(分析値)는 이론치(理論値)에 비(比)하여 P가 92.40%, Cark 86.80%, Mg가 93.80%로서 이론치(理論値)와 일치(一致)하지 않는다. 3) Na-phytate를 전분(澱粉)과 일정(一定)한 비(比)로 혼합(混合)하고 본법(本法)으로 P,Ca 및 Mc를 정량(定量)한 결과(結果) 이들의 회수율(回收率)은 거의 100%이었다. 4) 본분석법

• Journal of Life Science
• /
• v.27 no.12
• /
• pp.1500-1506
• /
• 2017

Plants are reservoirs of naturally occurring chemical compounds and of structurally diverse bioactive molecules. The aim of this investigation was to screen for the presence of phytochemicals responsible for the lipolysis activity in mulberry (Morus alba) leaves, which are important in traditional Asian medicinal plants. Powdered mulberry leaves were extracted with hexane, ethyl acetate, and methanol. Daucosterol was isolated from the EtOAc extract of mulberry leaves, and its structure was elucidated by NMR spectral analyses. The NMR assignments for the compound were determined using $^1H$, $^{13}C$, DEPT, COSY, HSQC, and HMBC NMR spectral data. Daucosterol showed a concentration-dependent lipolysis activity that may impart medicinal properties that can be exploited by medical practitioners for the treatment of various diseases. However, further studies should be conducted to elucidate additional mechanisms of daucosterol.

• Journal of Conservation Science
• /
• v.34 no.1
• /
• pp.23-29
• /
• 2018

This study synthesized poly-urea and used it as a filler material for the restoration of porcelain. The synthesized poly-urea was manufactured as a resin and hardener mix that does not undergo contraction during curing, and is unfading. Given an adhesion strength of $180kg/cm^2$ and shearing strength of $200kg/cm^2$, the synthesized poly-urea exhibited the same efficacy as the epoxy putty currently sold in the market. Moreover, it also overcame the drawback of foaming encountered by urethane restoratives, which are a structurally similar type. The hardening time and pot life could also be controlled using additives. The poly-urea used for the restoration of modern artifacts presented a pot life of approximately one hour and took 12 h for complete hardening ($T_{90}$). When a $2{\times}2{\times}2cm$-sized test sample was added to xylene, poly-urea started to separate approximately two hours later and completed perfect pulverization within the solution 24 h later, demonstrating its reversibility. When directly applied to contemporary artifacts, it demonstrated the potential for restoration, as well as convenience and colorfulness.