• Journal of the Korean Magnetics Society
• /
• v.15 no.5
• /
• pp.270-275
• /
• 2005

Dust cores (compressed powder cores) of $Fe-6.0wt\%Si$ alloy with a size of $35\~180\;{\mu}m$ in diameter have been prepared by phosphate coatings and annealings at $600\~900^{\circ}C$ for 1 h in nitrogen atmosphere. Further the magnetic and mechanical properties of the powder cores were investigated. As a general trends, the compressive strength and core loss decreased with the increase in annealing temperature. When annealed at $800^{\circ}C$, the compressive strength was 15 kgf, the permeability and quality factor were 74 and 26, respectively. Moreover the core loss at 50 kHz and 0.1 T induction was $750\;mW/cm^3$, and the percent permeability under the static field of 50 Oe was estimated to be about 78. In addition, the cut-off frequency in the cure representing the frequency dependence of effective permeability was measured to be around 200 kHz. These properties of the $Fe-6.0wt\%Si$ alloy dust cores could be considered to be due to the good insulation effect of iron-phosphate coats, the decrease in magnetocrystalline anisotropy and saturation magnetostriction and the increase in electric resistivity.

• Journal of Food Hygiene and Safety
• /
• v.38 no.2
• /
• pp.55-62
• /
• 2023

This study aimed to investigate the effect of a coating agent on pork storage. Pork was coated with a coating agent containing sodium carboxymethyl cellulose (CMC) and mandarin peel powder (M). The treatments were divided into control, a 0.1% CMC treatment, and a 0.1% CMC +5% M treatment, and pH, color, 2-thiobarbituric acid reactive substances (TBARS), volatile basic nitrogen (VBN), and the number of viable cell counts were measured. In the case of redness (a), it was found that the reduction over the storage period was less in the 0.1% CMC + 5% M treatment than in the control and the 1% CMC treatment. When stored at 4℃ and 25℃, TBARS of pork tended to increase during the storage period, followed by control, 0.1% CMC treatment, and 0.1% CMC + 5% M treatment, indicating that lipid oxidation was most suppressed in pork coated with mandarin peel powder. As a result of measuring the VBN of pork stored at 4℃ and 25℃, the 0.1% CMC + 5% M treatment showed lower values than the control and 0.1% CMC treatment. When the film-coated pork was stored at 4℃, the number of viable cell counts in the 0.1% CMC +5% M treatment area was 7.13±0.96 log CFU/g on the 12th day of storage, delaying the growth of viable cell counts for approximately 3 d more than other treatments. Therefore, coating pork with a film containing CMC and mandarin peel powder has been confirmed to delay the increase in the number of viable cell counts while reducing the quality change during pork storage, which is an effective alternative to improving the storage of fresh food as an edible film.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2011.11a
• /
• pp.737-744
• /
• 2011

The success of continuous aluminum powder combustion with steam plasma is different from hydrocarbon ignition source. Ignition characteristics of aluminum powder with high temperature thermal plasma is studied with oxidizer-free environment. Experiment with argon plasma has same temperature conditions at 4500 K and particle feeding condition for previous combustion test with steam plasma and swirl combustor. The temperature of the plasma was measured using Optical Emission Spectroscopy method. Ignition characteristics were analyzed by SEM image and EDS. Aluminum powder with plasma has rapid evaporation mechanism contrast to hydrocarbon ignition source. It enhances to aluminum powder effective ignition characteristics.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.24 no.3
• /
• pp.285-293
• /
• 2016

The high velocity oxygen fuel(HVOF) thermal spray is a kind of surface modification techniques to produce the sprayed coating layer. This process is to form the coating layer after spraying the powder to molten or semi-molten state by the ultra-high speed at the high-temperature heat source and conflicting with a substrate. The efficiency of thermal spraying is dropped, however, because the semi-molten powder in a spray process become a factor that degrades the mechanical property by the formed pore within the coating layer. Therefore, it is necessary to melt completely the thermal spray powder in order to produce the coating layer with an optimal adhesive force. In this study, to improve the wear resistance, corrosion resistance and heat resistance, the plungers of high-speed and ultra-high pressure reciprocating hydraulic pumps used in ironworks are manufactured with STS $420J_2$ and are coated by the powders of WC-Co-Cr and WC-Cr-Ni including the WC of high hardness using a HVOF thermal sprayer developed in this laboratory. These are called by the surface-modified plungers. The surface roughness, hardness, and surface and cross-sectional microstructure of these two surface-modified and conventional ceramic plungers are measured and compared before operation with after operation for 100 days. It is found that the values of centerline average surface roughness and maximum height for conventional ceramic plunger are 9.5 to 10.8 and 5.2 to 5.7 times higher than those of surface-modified ones coated by WC-Co-Cr and WC-Cr-Ni because the fine tops and bottoms on surface roughness curve of conventional ceramic plunger are approximately 100 times higher than those of surface-modified ones. In addition, the pores and scratches in the surface microstructure are considerably formed in the order of conventional ceramic, WC-Cr-Ni and WC-Co-Cr surface-modified plungers. The greater the WC content of high hardness powder is less the change in the plunger surface.

• Journal of Powder Materials
• /
• v.19 no.3
• /
• pp.196-203
• /
• 2012

$TiO_2$ was successfully formed on a Ti specimen by MAO (Micro-Arc-Oxidation) method treated in $Na_3PO_4$ electrolyte. This study deals with the influence of voltage and working time on the change of surface microstructure and phase composition. Voltage affected the forming rate of the oxidized layer and surface microstructure where, a low voltage led to a high surface roughness, more holes and a thin oxidized layer. On the other hand, a high voltage led to more dense surface structure, wider surface holes, a thick layer and fewer holes. Higher voltage increases photocatalytic activity because of better crystallization of the oxidized layer and good phase composition with anatase and rutile $TiO_2$, which is able to effectively separate excited electrons and holes at the surface.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.20 no.1
• /
• pp.50-54
• /
• 1983

Contact resistance variation which may be called sliding noise in carbon film variable resistors whose resistance elements consists of linear resistivity distribution were measured with several kinds of sliders and were analyzed to reduce the contact resistance variation. About the measuring method, the standard method of measuring contact resistance variation specified by the variable Resistance Components Institute was adupted. By analyzing the experimental results, it has been shown that the primary cause of contact resistance variation is due to current constriction and small discharge sparks in the resistance film in the area close to the slide contact. Moreover, it has been found that the sliding noise would be reduced by increasing the number of contact points, sliding speed, and pressure, and by using some kinds of insulation oil on the contacting surface. High contact resistance variation is likely to occur in the area of high resistance variation in a logrithmic resistance taper.

• Journal of Welding and Joining
• /
• v.18 no.5
• /
• pp.98-104
• /
• 2000

Aluminum alloys are being employed in automobile parts as strive to reduce overall vehicle weight to meet demands for improved fuel economy and reduction in vehicle emissions. Al-based composites reinforced with ceramic ($Al_2O_3,\;SiC,\;TiC\;and\;B_4C$) applications in a variety of components in automotive engines, such as liners, where the tribological properties of the material are important. In this study, Al-base composites reinforced with TiC particle powders has been developed for producing plasma spray coatings. The composite plasma spray powders were prepared Al-13Si-3Mg(wt%) alloy with TiC(40, 60 and 80wt%) particles ($0.2~5{\mu}textrm{m}$) by drum type ball milling. The composite powders ($36~76{\mu}textrm{m}$) were sprayed with plasma torch. Plasma sprayed coatings were heat-treated at $500^{\circ}C$ for 3 hours. The wear resistances of the plasma sprayed coatings were found to decrease with increasing TiC content and improved with heat treatment. AlSiMg-40% TiC heat-treated coatings were showed the best wear resistance in this study.

• Food Science and Preservation
• /
• v.22 no.5
• /
• pp.683-689
• /
• 2015

Response surface methodology (RSM) is a statistical procedure frequently used for optimization studies. The purpose of this study was to determine the optimal spray drying condition for manufacturing Sikhye powder using RSM. Independent variables included the additive contents of maltodextrin (MD), inlet temperature, and velocity of sample feed velocity. The dependent variables were water uptake (g), solubility (%) and particle size (${\mu}m$). Regression models describing the changes of water uptake (g), solubility (%) and particle size (${\mu}m$) with respect to the independent variables were statistically significant with coefficients of determination, $R^2$, greater than 0.9. The results indicated that the inlet temperature of the spray dryer was the most important independent variable that affected the water uptake (g), while the additive content of MD and the sample feed velocity had maximum effects on the solubility (%) and particle size (${\mu}m$) of the Sikhye powder, respectively. The optimum final product was expected to have the lowest possible water uptake (g) and particle size (${\mu}m$) but the highest possible solubility (%). In conclusion, the best spray drying conditions were as follows: additive MD content, 22%; inlet temperature, $140^{\circ}C$ ; and spray dryer sample feed velocity, 51 mL/min.

• Journal of the Korean Magnetics Society
• /
• v.15 no.2
• /
• pp.67-75
• /
• 2005

For th aim of lightweight microwave absorbers, conductive and magnetic microspheres are fabricated by plating of Co films on hollow ceramic microspheres of low density. Metal plating was carried out in a two-step electroless plating process (pre-treatment of activation and plating). Uniform coating of the film with about $2{\~}3{\cal}um$ thickness was identified by SEM. High-frequency magnetic and microwave absorbing properties were determined in the rubber composites containing the Co-coated microspheres. Due to conductive and ferromagnetic behavior of the Co thin films, high dielectric constant and magnetic loss can be obtained in the microwave frequencies. Due to those electromagnetic properties, high absorption rate (25 dB) and thin matching thickness ($2.0{\~}2.5{\cal}mm$) are predicted in the composite layers containing the metal-coated microspheres of low density (about 0.84 g/cc) for the electromagnetic radiation in microwave frequencies.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.170-171
• /
• 2012

$Fe_2O_3$, Al, Cr과 Si 분말을 고 에너지 볼 밀링해서 나노분말을 제조한 후 고주파유도 가열 활성 연소합성 장치로 1분 이내의 짧은 시간에 합성 및 소결한 $Al_2O_3+4.65(Fe_{0.43}Cr_{0.17}Al_{0.323}Si_{0.077})$, $Al_2O_3$ + 5.33 ($Fe_{0.375}Cr_{0.11}Al_{0.3}Si_{0.075}$), $Al_2O_3$ + 6.15 ($Fe_{0.325}Cr_{0.155}Al_{0.448}Si_{0.072}$), $Al_2O_3$ + 3.3 ($Fe_{0.6}Cr_{0.3}Al_{0.6}$) 소결체 시편을 $700^{\circ}C$의 온도에서 100시간 동안 공기 중에서 산화 및 $N_2-H_20-H_2S$ 혼합 가스 내에서 황화 부식을 실시하였다. 그 결과 산화 및 황화 부식 후에 ${\alpha}-Al_2O_3$가 표면에 생성되어 보호 피막으로 작용하여 우수한 내식성을 보였다.