• Journal of the Korea Concrete Institute
• /
• v.20 no.6
• /
• pp.713-719
• /
• 2008

Various types of coatings have been developed for use as reinforcement in concrete and to resist chloride environment. The most commonly used coatings are inhibited and sealed cement slurry coating, cement polymer compositing coating and epoxy coating. Cement slurry offers passive protection, epoxy coating offers barrier protection whereas polymer coating offers both passive protection and barrier protection. Moreover, damage during handling of the steel may result in disbondment of the epoxy coating, which would increase the risk of localized corrosion. In the present study, inhibiting technique was used to increase the calcium hydroxide content at the interface up to 20%. Calcium hydroxide provides a high buffering capacity that resists a local fall in pH and thus maintains the alkaline environment necessary to prevent chloride corrosion. This study examines the use of a calcium hydroxide coating on the steel surface to enhance the pH buffering capacity of steel-concrete interface. Finally, the chloride threshold level (CTL) of polymer inhibitive coating calcium hydroxide is evaluated.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.3
• /
• pp.23-30
• /
• 2012

For cracked concrete, it is obvious that cracks should be preferential channel for the penetration of aggressive substances such as chloride ions according to the previous researches. In order to extend the lifetime of cracked concrete, critical issues in the performance of the concrete is the risk of chloride-induced corrosion. Even though crack width can be reduced due to the high reinforcement ratio, the question is to which extend these cracks may jeopardize the durability of cracked concrete. If the size of crack is small, surface treatment system can be considered as one of the best options to extend the service life of concrete structures exposed to marine environment simply in terms of cost effectiveness versus durability performance. Thus, it should be decided to undertake an experimental study on the effect of surface coating system, which can be able to seal the concrete and the cracks to aggressive substances-induced corrosion in particular. In this study, it is excuted to examine the effect of surfaced treated systems on chloride penetration and carbonation through compressive stress induced cracks. Experimental results have showed conclusively that critical stress linked with deterioration, should be existed in compressive stress ratio 50 ~ 70% for chloride penetration and 70 ~ 80% for carbonation, respectively. When the critical stress is exceeded in concrete, a comparatively large deterioration was measured where the critical stress in concrete, the increase in the mass transportation is marginal in spite of the large increase in micro-cracks. As for the effect of surface coating system on crack-sealing, it can be seen conclusively that cracks can be healed.