• 동력기계공학회지
• /
• 제15권2호
• /
• pp.42-48
• /
• 2011

440A martensitic stainless steels which were modified with reduced carbon content(~0.5%) and addition of small amount of nickel, vanadium, tungsten and molybdenum were manufactured. Effects of alloying elements and tempering temperatures on the uniform corrosion in the solution of lN H2S04 were investigated through the electrochemical polarization test. When tempering temperature is constant, corrosion current density in active-passive transition point, Icorr, decreased a little with an increase of austenitizing temperature. In addition to this, when austenitizing temperature is constant, longer holding time showed a little lower Icorr and Ipass, passive current density. And when austenitized at $1050^{\circ}C$ and tempered in a range of $350{\sim}750^{\circ}C$, best anti-corrosion properties were obtained at $350^{\circ}C$ tempering temperature while worst at $450^{\circ}C$ or $550^{\circ}C$. The specimens tempered at below $450^{\circ}C$ and above $550^{\circ}C$, similar and good anti-corrosion characteristics were obtained regardless of alloying elements added, showing anti-corrosion characteristics are influenced more by tempering temperature than by alloying elements.

• Journal of Advanced Marine Engineering and Technology
• /
• 제41권3호
• /
• pp.230-237
• /
• 2017

본 연구에서는 해상풍력 타워 지지구조물용 강재인 S355ML 강에 대하여 전기화학적 기법으로 전기방식 설계에 필요한 최적 방식전위를 규명하고자 하였다. 동전위분극 실험 결과, 양극분극 곡선 상에서는 부동태 구간은 존재하지 않으며, 음극분극 곡선 상에는 용존산소환원반응에 의한 농도분극 구간과 수소가스 발생에 의한 활성화분극 구간이 관찰되었다. 음극방식 시 방식전위에 해당하는 농도분극 구간은 약 - 0.72 V ~ - 1.0 V의 전위 구간인 것으로 확인되었다. 다양한 전위에서 정전위 실험을 실시한 결과 전류밀도 변화는 시간에 따라 안정화되는 경향을 나타냈다. 1200초 동안 정전위 실험 후 주사전자현미경과 3D 분석 현미경을 이용한 시험편 표면 분석 결과, 양극분극 전위에 해당하는 0 V ~ - 0.50 V의 전위구간에서는 양극용해반응에 의한 부식손상이 관찰되었다. 이에 반해 음극분극 전위 영역에서는 대체적으로 손상이 없는 양호한 표면을 유지하였으며 석회질 피막 형성을 확인할 수 있었다. 연구결과, 농도분극 영역에 해당하는 - 0.8 V ~ - 1.0 V의 전위영역이 S355ML 강의 외부전원법에 의한 음극방식 적용 시 최적 방식 전위 구간으로 사료된다.