• 한국정밀공학회지
• /
• 제18권2호
• /
• pp.84-89
• /
• 2001

In recent years, there is increasing demand of esthetic design and complex function in aerospace, automobile and die/mold industry, which brings into limelight high-precision, high-efficient machining of sculptured surface. This paper deals with the establishment of the optimal tool path on free form surface in high speed ball end milling. Ball end milling is widely used for free form surface die and mold. In this machining, the cutting direction was changed with tool path. The cutting characteristics, such as cutting force and surface form are varied according to the variation of cutting directions. In this paper, the optimal tool path with down cutting in free form surface cutting is suggested.

• 한국재료학회지
• /
• 제13권9호
• /
• pp.631-634
• /
• 2003

To fabricate W-Cu nanocomposite powder, $WO_3$-CuO powder mixture was high-energetically ball-milled and subsequently hydrogen-reduced. The effect of ball-milling on the hydrogen-reduction behavior of$ WO_3$-CuO was investigated with non-isothermal hygrometric analysis during hydrogen-reduction. Increasing the ball-milling time, the reduction peak temperatures of humidity curves were shifted to low temperature. It was considered that the reduction temperature should be decreased because the specific surface area of each oxide considerably increased with increasing the ball-milling time. In case of ball-milling for 0 h, $WO_3$and CuO were independently hydrogen-reduced and W particles were nucleated on the surface of Cu adjacent to W by CVT. However, in case of ball-milling for 50 h, the aggregates of about 200-300 nm were observed. W particles of size below 30-50 nm were homogeneously distributed with Cu in the aggregates.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2012년도 춘계학술발표대회
• /
• pp.94.2-94.2
• /
• 2012

에너지 하베스터에 적용 가능한 $0.72Pb(Zr_{0.47}Ti_{0.53})O_3-0.28Pb((Ni_{0.55}Zn_{0.45})_{1/3}Nb_{2/3})O_3$ (PPZNN) 후막세라믹의 구조적 압전 특성을 조사하였다. $850^{\circ}C$에서 하소를 마친 파우더를 72시간 볼 밀링 처리한 후, 테잎 캐스팅 공정을 이용하여 0.3mm의 두께로 PPZNN 압전 세라믹을 제조하였다. $900^{\circ}C$에서 $1200^{\circ}C$까지 다양한 온도에 소결하여 온도가 증가될수록 정방형 구조로 상전이 거동하는 모습을 보였으며, 특히 $1050^{\circ}C$에서 소결된 PPZNN후막 세라믹은 이차상이 없는 고밀도의 미세구조가 관찰되었다. $d_{33}$=440 pC/N 그리고 kp = 0.46의 우수한 압전 특성을 보였으며, 에너지 변환 성능을 나타내는 $d33{\cdot}g33$ 값은 약 $20439{\times}10^{-15}\;m^2/N$ 로 매우 우수하였다. PPZNN후막 세라믹을 유니몰프 켄틸레버 형태로 제작하여 발전 평가하였을 때 저항이 470 $k{\Omega}$에서 969 ${\mu}W$ (4930 ${\mu}W/cm^3$)로 관찰되었다. PPZNN 후막 압전 세라믹은 향후 압전에너지 하베스터 소재로 다양한 응용분야에 사용될 것으로 예상된다.

• 한국분말재료학회지
• /
• 제17권2호
• /
• pp.130-135
• /
• 2010

Sm-16.7wt%Co alloy powders were prepared by high energy ball milling under the conditions of various milling time and the content of process control agent (PCA), and their microstructure and magnetic properties were investigated to establish optimum processing conditions. The initial powders employed showed irregular shape and had a size ranging from 5 to $110\;{\mu}m$. After milling for 5 h, the shape of powders changed to round shape and their mean powder size was approximately $5\;{\mu}m$, which consisted of the agglomerated nano-sized particles with 15 nm in diameter. The coercivity was reduced with increasing the milling time, whereas the saturation magnetization increased. As the content of PCA increased, the powder size minutely decreased to approximately $7\;{\mu}m$ at the PCA content of 10 wt%. The XRD patterns showed that the main diffraction peaks disappeared apparently after milling, indicating the formation of amorphous structure. The measured values of coercivity were almost unchanged with increasing the content of PCA.

• 한국분말재료학회지
• /
• 제19권4호
• /
• pp.310-316
• /
• 2012

Nanocrystalline $BaTiO_3$ powder could be synthesized by solid-state reaction using the mixture which was prepared by a high energy milling process in a bead mill for $BaCO_3$ and nanocrystalline $TiO_2$ powders mixture. Effect of the milling time on the powder characteristic of the synthesized $BaTiO_3$ powder was investigated. Nanocrystalline $BaTiO_3$ with a particle size of 50 nm was obtained at $800^{\circ}C$. High tetragonal $BaTiO_3$ powder with a tetragonality(=c/a) of 1.009 and a specific surface area of $7.6m^2/g$ was acquired after heat-treatment at $950^{\circ}C$ for 2 h. High energy ball milling was effective in decreasing the reaction temperature and increasing the tetragonality.

• 한국수소및신에너지학회논문집
• /
• 제13권3호
• /
• pp.242-248
• /
• 2002

SnCo alloy powder prepared by high energy ball milling is examined as an anode material for lithium-ion batteries. As the ball-milling time increased, the crystallinity of SnCo decreased. XRD and TEM SADP showed that nanocrystalline and amorphous phase coexisted after 16 h ball-milling. As the crystallinity decreased, the cycleability increased. At first cycle, there are 4 plateau potentials. The observation of voltage plateau at about 0.68 V confirms the formation of Sn-Li alloy and Co metal. It is considered that The plateau potentials below 0.68 V were reaction between Li and Sn. The change of chemical diffusion coefficient showed that the structure of SnCo alloy abruptly changed at first cycle, and maintained after 2nd cycle.

• 한국전기전자재료학회논문지
• /
• 제29권8호
• /
• pp.516-521
• /
• 2016

Mo-Cu alloys have been widely used for heat sink materials, vacuum technology, automobile, and many other applications due to their excellent physical and electric properties. Especially, Mo-Cu composites with 5 ~ 20 wt.% copper are widely used for the heavy duty service contacts due to their excellent properties like low coefficient of thermal expansion, wear resistance, high temperature strength, and prominent electrical and thermal conductivity. In most of the applications, highly-dense Mo-Cu materials with homogeneous microstructure are required for better performance. In this study, Mo-Cu alloys were prepared by PBM (planetary ball milling) and SPS (spark plasma sintering). The effect of Cu with contents of 5~20 wt.% on the microstructure and thermal properties of Mo-Cu alloys was investigated.

• 한국분말재료학회지
• /
• 제6권1호
• /
• pp.42-48
• /
• 1999

Three mixtures of elemental powders of Al-25at.%Ti, 48at.%Ti and 70at.%Ti were offered to ball milling process for the formation of intermetallic compounds of $Al_3Ti$, AlTi and $Ti_3Al$. Ballmilling or attrition process were carried out at the condition of rotaing speed of 110 or 350 rpm at $10^{-3}$ torr vacuum or argon atmospheres. $Al_3Ti$phases were fully obtained by heat treatment for 1 hors at $600^{\circ}C$ with Al-25at.%Ti composition mixtures milled by 100 hours. The amorphous phase was completely formed at the composition of Al-48at.%Ti mixed powders by milling 100hours at the 50 to 1 weight ratio of ball to powder, and AlTi compounds were obtained by heat treament. In the case of Al-70at%Ti mixed powders milled for 100 hours, $Ti_3Al$ and $Al_3Ti$intermetallic compounds were formed by heat treatment for 1 hour at $600^{\circ}C$. By attrition milling of 350rpm for 10 hours, $Ti_3Al$ phase was formed completley after heat treatment for 1 hour at $600^{\circ}C$.

• 한국결정성장학회지
• /
• 제27권3호
• /
• pp.135-142
• /
• 2017

본 연구에서는 국내 화력발전소에서 발생되는 바텀애쉬를 이용하여 질석 성형물을 제작하였으며, 이를 이용하여 흡음 건자재 제조를 위한 흡음성, 최고 휨파괴하중에 대하여 고찰하였다. 이러한 바텀애쉬와 질석의 성형물 제조를 위하여, 마이크로웨이브 건조방식의 공정를 사용하였다. 또한, 바텀애쉬의 볼밀링작업을 통하여 얻어진 $65{\mu}m$ 정도의 크기의 균일한 분말이 사용되었다. 5, 10 wt%의 바텀애쉬와 질석의 성형물을 제조하여, 최고 휨파괴하중 특성이 분석 되었다. 이러한 실험 결과들은 바텀애쉬의 재활용 기술에 필요한 기초적인 데이터를 제공한다.

• 한국분말재료학회지
• /
• 제3권3호
• /
• pp.181-187
• /
• 1996

Cobalt and VC powders were ball milled with M2 grade high speed steel powders under various ball to powder ratios. The powders milled under higher ball to powder ratio become finer, more irregular and have a broader size distribution, and thus possess a lower compressibility and a better sinterability regarding densification. Increasing the ball to powder ratio lowered the sintering temperature to obtain the density level necessary to isolate all the pores. Lowering the sintering temperature is very critical to maintain fine microstructure since grain and carbide coarsening are accelerated by higher sintering temperature due to more liquid phase formation. The powders obtained by ball milling at 20 to 1 ratio has the lowest compressibility but has the best sinterability, almost compatible to unmilled pure M2 powders. A sintered body over 97% theoretical density with fine microstructures having average grain size of ~10 microns was obtained from the powder by sintering at 1260 $^{\circ}C$ for 1 hour in vacuum. XRD results indicate that two types of carbides are mainly present in the sintered structure, MC and $M_{6}C$ type. The MC type carbides are more or less round shaped and mainly located at the grain boundaries whereas the $M_{6}C$ type are angular shaped and mainly located inside the grains.