• Journal of the Korean Wood Science and Technology
• /
• v.37 no.6
• /
• pp.546-555
• /
• 2009

To study an effective use of woods, three-ply hybrid laminated woods instead of crosslaminated woods which are composed of spruce in the face and three kinds of wood-based boards (MDF, PB, OSB) in the core were manufactured, and the effect of constitution elements for the core laminae on bending strength performances was investigated. Bending modulus of elasticity (MOE) of hybrid laminated woods had the highest values for the hybrid laminated wood types arranging OSB laminae in the core, and had the lowest values for those arranging MDF laminae in the core. These values were higher than those of various cross-laminated woods. The estimated bending MOEs of the hybrid laminated woods which were composed of perpendicular-direction lamina of spruce in the faces were similar to their measured values, regardless of wood-based boards in the core. However, those of the hybrid laminated woods which were composed of parallel-direction lamina of spruce in the faces had much higher values than those of their measured values, and it was necessary to revise the measured values. Bending modulus of rupture (MOR) of the hybird laminated woods had the highest value for those arranging OSB laminae in the core, and had the lowest values for those arranging PB laminae in the core unlike the bending MOE. By hybrid laminating, the anisotropy of bending strength performances was markedly decreased, and the differences of strength performances among wood-based boards were also considerably decreased.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.1
• /
• pp.48-56
• /
• 2016

In this study, to develop the lattice materials with a low environmental load for restoring the destroyed forest, 7 types of wood-concrete hybrid laminated materials were manufactured with domestic four softwoods, three hardwoods and concrete, and the effects of density of wood species on static bending strength performances were investigated. Bending MOEs of wood-concrete hybrid laminated materials increased with increasing density of wood species on the whole, and the values were higher than that of concrete by hybrid-laminating woods on the concrete. It was found that the measure values of bending MOEs were slightly lower than the calculated values calculated using equivalent cross-section method from MOE of each laminae of hybrid laminated materials and the difference between them was less than 10%. Bending proportional limit stresses of hybrid laminated materials showed 1.2-1.6 times higher than that of concrete by hybrid-laminating. Bending strength (MOR) of hybrid laminated materials increased with the density of wood species. By hybrid-laminating, the MOR of concrete was considerably increased. Therefore, it is considered that wood-concrete hybrid laminated materials can be applied as a materials with a low environmental load and durability for ecological restoration.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.1
• /
• pp.1-10
• /
• 2010

In this study, to study an effective use and improve strength performances of woods and wood-based materials, three-ply hybrid laminated woods which are composed of spruce in the face and three kinds of wood-based boards (MDF, PB, OSB) in the core were manufactured, and the effect of constitution elements used for the core laminae on bending creep performances was investigated. The shape of creep curves showed exponential function plots which the upper right side was increased, and differed among the kinds of wood-based boards used for the core laminae of hybrid laminated wood. The creep deformation perpendicular to the grain of faces of hybrid laminated woods was in order $C_{\perp}$(P) > $C_{\perp}$(M) > $C_{\perp}$(O) with PB, MDF and OSB in the core, respectively. It was found that the creep deformation arranged with OSB in the core had 2 times smaller than those arranged with MDF and PB in the core. By hybrid laminating, the creep deformation of spruce perpendicular to the grain was markedly decreased. On the other hand, the creep deformation parallel to the grain of the faces ($C_{\parallel}$ type) of hybrid laminated woods was in order $C_{\parallel}$(P) > $C_{\parallel}$(O) > $C_{\parallel}$(M) with PB, OSB and MDF in the core. The ratios among three hybrid laminated woods were considerably decreased, especially the difference between $C_{\parallel}$(P) and $C_{\parallel}$(O) hybrid laminated woods arranged with PB and OSB in the core was very small. These values showed 0.108~0.464 times smaller than creep deformation of three wood-based boards and it was found that creep deformation of three wood-based boards was considerably decreased by hybrid laminating. Creep anisotropy of hybrid laminated woods was greater in creep deformation than in initial deformation, whereas it was found that the values was much smaller than that of spruce parallel laminated woods.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.12
• /
• pp.1931-1936
• /
• 2010

In Korean tilting trains, honeycomb composite panels are used for high speed and light weight. The side wall of a tilting train consists of an aluminum honeycomb coated with carbon-fiber-reinforced epoxy skin and a nomex honeycomb panel as the main structure, with glass wool inserted between the panels. In this study, based on ASTM E2249-02, we measure the intensity sound transmission loss (TL) of the honeycomb composite panels. Using mass law deviation (MLD), we estimate the sound insulation performance of the honeycomb composite panels in terms of their weight and explore the feasibility of substituting a conventional corrugated steel panel. The transmission-loss data of the honeycomb composite panels obtained in the study will be used to establish noise-reduction measures for train compartments.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.1
• /
• pp.57-66
• /
• 2016

In order to develop materials with a low environmental load for restoring the destroyed forest, seven types of wood-concrete hybrid laminated materials were manufactured with four softwoods, three hardwoods and concrete, and the effect of wood density on bending creep property was investigated. The bending creep curves showed a shape to considerably increase at the upper right side, and the curves were found to show a linear behavior beyond about 30 min - 1 hour, as behaviors of solid woods and wood-based materials. The initial compliances of wood-concrete hybrid-laminated materials decreased with an increase in the wood density, and those values showed 0.9 - 1.2 times of the concrete one. The creep compliances of hybrid laminated materials showed very low values, which were 0.4 - 0.8 times of the concrete ones. The relative creep were very low with a range from 8.2% to 17.0% range, which were 0.3 - 0.7 times of the concrete ones. These results indicate that these materials can be applied for restoring the destroyed forest to reduce creep deformation of the conventional concrete materials by hybrid-laminating concrete and woods.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.5
• /
• pp.1611-1619
• /
• 1991

본 연구에서는 Hilton과 Sih의 경우를 확장 적용하여 Fig. 1(b)와 같이 탄성 층 내부에 존재하는 중앙균열선단의 응력확대계수 산출을 위하여 균열부위를 제외하고 는 섬유층과 레진층이 완전히 접착되었다고 가정한 모델을 다음과 같이 설정하였다. 중앙균열을 내재하고 있는 복합재료의 역학적 거동을 해석하기 위하여, 접착레진을 주 로하는 층(resin rich layer)을 중심으로 하여 상하 각1개의 섬유 (fiber)층과 균질한 특성을 갖는 복합재료의 층으로 단순화 하였으며, 이러한 단순화는 적층재에서의 균열 주위의 국부응력을 해석하기 위한 것으로서 복합재료는 레진층이나 섬유층에 비하여 매우 두꺼우므로 반무한체로 이상화 하였다. 선형탄성 이론에 의하여 혼합 경계조건 문제(mixed boundary value problem)로 부터 제2종 Fredholm적분방정식(fredholm int- egral equation of a second kind)을 유도하였으며 수치해석적인 방법에 의하여 응력 확대계수를 구하였다.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.05a
• /
• pp.76-76
• /
• 2004

하이브리드 복합재료 중에서 적충형태의 Al/GFRP는 단일재 알루미늄에 비해 피로특성, 비강도, 비강성 등이 매우 우수하여 Fig. 1과 같이 항공기 주익 구조에 주로 적용된다. 그러나 이러한 Al/GFRP 적층재 역시 장시간에 걸쳐 비행하중을 받게 되면 다양한 형태의 파손이 발생할 수 있다. 이 중 알루미늄층과 섬유층 사이에서 발생하는 층간분리는 Al/GFRP 적층재의 대표적인 피로파손 형태이며, 현재 이러한 파손은 다 방면으로 연구되고 있다.(중략)

• Journal of Korea Foundry Society
• /
• v.27 no.6
• /
• pp.255-257
• /
• 2007

최근에는 탄소섬유복합재료(CFRP)는 우주 및 민간 항공산업분야에 널리 활용이 되고 있는 실정이다. CFRP 복합재는 적층구성에 따라 기계물성치 및 강성에 크게 영향이 미치므로 가장 대표적인 직교이방성 적층재의 적층배향을 비파괴 탐상하는 것은 중요하다. 본 연구에서는 CFRP 적층재의 섬유배향에 가장 민감한 초음파 전단파를 활용하기 위해 2개의 종파 초음탐촉자를 이용하는 새로운 기법을 제안하였다. 또한 초음파 전단파를 발생하기 위해서는 탐촉자 밑면에 접촉매질인 태운꿀을 사용하는데 초음파시험하는 도중에 물성치중에 하나인 즉 점성이 상당히 변하게 된다. 이러한 문제를 해결하기 위해 2개의 종파용 초음파탐촉자를 이용해 전단파를 발생시킴으로써 접촉매질문제를 상당히 경감할 수 있는 것으로 나타났으며 여기에서 발생한 전단파가 CFRP 복합적층판의 섬유배향에 매우 민감함을 알 수 있었다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.3 s.258
• /
• pp.295-303
• /
• 2007

Degradation behaviors of filament-winded composites have been evaluated under the accelerated environmental test of high temperature, water immersion and thermal impact conditions. Two kinds of laminated composites coated by an urethane resin have been used: carbon-fiber reinforced epoxy(T700/Epon-826, CFRP) and glass-fiber reinforced phenolic (E-glass/phenolic, GFRP). For tensile strength of $0^{\circ}$ composites, CFRP showed little degradation while GFRP did high reduction by 25% under the influence of high temperature and water However for water-immersed $90^{\circ}$ composites tensile strength of both CFRP and GFRP showed high reduction. Bending strength and modulus of $90^{\circ}$ composites were largely reduced in water-immersion as well as high temperature environment. Urethane coating on the composite surface improved the bending properties by 20%, however hardly showed such improvement for water-immersed $90^{\circ}$ composites. In case of shear strength and modulus, both CFRP and GFRP showed high reduction by water-Immersion test but did a slight increase by high temperature and thermal impact conditions.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.2
• /
• pp.237-247
• /
• 1993

Carbon fiber reinforced plastics(CFRP) have gained increased application in aerospace structures because of their specific strength and stiffness, but are sensitive to impact-induced damage. An experimental investigation was carried out to evaluate the impact resistance of CFRP according to the ply angle. The specimens of angle ply laminate composites were employed with [0.deg. $_{6}$/ .deg.$_{10}$/0.deg.$_{6}$], in which 6 kinds of ply angle such as .deg.=15.deg., 30.deg., 45.deg., 60.deg., 75.deg. and 90.deg. were selected. The impact tests were conducted using the air gun type impact testing machine by steel balls of diameter of 5 mm and 10 mm, and impact-induced damages were evaluated under same impact speed of V=60m/s. The impact damaged zones were observed through a scanning acoustic microscope (SAM). The obtained results were summarized as follows: (1) Delaminations on the interfacial boundaries showed th directional characteristics to the fiber directions. The delamination area on the impact side (interface A) was considerably smaller compared to that of the opposite side (interface B). (2) Cracks corresponding to other delaminations than those mentioned in SAM photographs were also seen on the impact damaged zone. (3) The delamination patterns were affected by the ply-angle, the dimensions of the specimen, and the boundary conditions. (4) The impact damaged zone showed zone showed the delamination on the interfacial boundaries, transverse shear cracks of the surface layer, and bending cracks of the bottom layer.r.r.r.