• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.7
• /
• pp.723-730
• /
• 2012

During the cold wire-drawing process, the diameter of a wire is reduced and the length of the wire is increased as the wire passes through the die. The pressure and sliding motion at the interface between the wire and die cause elastic recovery of the workpiece and friction and wear on the die. In addition, wire deformation and frictional heating raise the temperature of the wire and die, resulting in difficulty in manufacturing the drawn products according to a designated inner diameter of the die, deviating from the designated dimension or the inner diameter of the die. In this study, considering the die temperature distribution, the effects of dimensional changes of the drawn products were analyzed quantitatively; these changes are caused by the elastic deformation of the die, the elastic recovery of the workpiece, and the thermal deformation of both the die and the workpiece. It was confirmed that the elastic recovery of the workpiece influenced these changes the most. The initial dies considering these factors could avoid deviation from the designated dimension, and the desired drawn products were obtained by using the designed initial drawing dies.

• 한국도로학회:학술대회논문집
• /
• 2005.11a
• /
• pp.337-343
• /
• 2005

• Proceedings of the Korean Nuclear Society Conference
• /
• 1995.05a
• /
• pp.729-734
• /
• 1995

원자력용 316L강에 질소를 첨가한 경우의 고온 인장성질을 조사하였다. 온도가 증가하면 인장강도는 감소하다가 온도범위가 30$0^{\circ}C$~50$0^{\circ}C$에서는 일정한 값을 나타낸 후 급격한 감소를 나타내었고 연신율은 감소하다가 40$0^{\circ}C$에서 최소값을 나타낸 후 다시 증가하는 경향을 나타내었다. 질소를 첨가하면 인장강도증가와 함께 연신율도 증가하였다. 동적변형시효 온도구간에서 변형속도변화에 따른 인장강도 및 연신율의 변화는 매우 작다. 동적변형시효를 위한 활성화에너지를 구해본 결과 동적변형시효를 일으키는 원소는 Cr이다. 질소를 첨가하면 동적변형시효가 발생되는 온도가 고온 쪽으로 이동되었는데 이것은 질소가 Cr과의 상호작용에 의해 Cr의 확산속도를 낮추기 때문이다. 가공경화지수는 동적변형시효와 회복의 영향으로 40$0^{\circ}C$에서 최대값을 나타내었으며 이 온도는 연신율이 최소값을 나타내는 온도와 인장강도가 일정하게되는 온도와 일치하므로 강도강화기구는 동적변형시효로 판명되었다.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.10 no.3
• /
• pp.292-297
• /
• 1986

Measurements of internal stress .sigma.$_{i}$, anelastic strain .epsilon.$_{A}$ and recovery rate .gamma. were made in steady state creep of 2024 Al alloys over a wide range of stresses at temperatures between 260.deg. C and 380.deg. C, for the purpose of investigating the relations among the three parameters. Values of .sigma.$_{i}$ were obtained by the method of strain transient dip test, and those of .epsilon.$_{A}$ and .gamma. were determined from the results of sudden stress removal or reduction tests. As a main result, it is thought that the anelastic behavior and recovery process are basically dependent on same deformation mechanisms.sms.sms.

• Korean Journal of Agricultural Science
• /
• v.14 no.2
• /
• pp.329-344
• /
• 1987

This paper described the behavior under repeated loading in triaxial compression test on clay. The experiment was conducted to investigate the influence of controlled various over-consolidation ratio and compaction energy, on the stress-strain behavior of clays. 1. The difference of deviator stress during repeated loading was greatly appeared at large strain. And pore water pressure was decreased at initial of unloading, but it was increased again before long. 2. The recoverable elastic strain (${{\Delta}{\varepsilon}e}$) and the slope of un-reloading were decreased with the increment of over-consolidation ratio (OCR). 3. The recoverable elastic strain (${{\Delta}{\varepsilon}e}$) was increased with the increment of strain rate but it was decreased with the increment of strain in strain rate tests. The slope of un-reloading (Eur) tends to increase with the increment of strain rate and it was decreased with the increment of strain. 4. The recoverable elastic strain was greatly increased with the increment of compaction energy and it slightly tends to decrease with the increment of strain on various compaction energy. The slope of un-reloading was not appeared markedly with increment of compaction energy but it tends to decrease with the increment of strain generally.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.103-104
• /
• 2009

This paper focuses on the characteristics on long-term deflection and creep recovery of reinforced concrete beams under a sustained load of 25kN. In order to investigate the residual strengthen of the RC beam, a static flexural experiment was conducted. The result of the RC beam preloaded was compared with that of a RC beam, which was not preloaded.

• 한국도로학회:학술대회논문집
• /
• 2009.11a
• /
• pp.199-206
• /
• 2009

• Proceedings of the Korean Vacuum Society Conference
• /
• 1992.07a
• /
• pp.75-76
• /
• 1992

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.40-40
• /
• 2003

최근 나노기술의 발달과 더불어 나노재료에 대한 특성평가 요구가 높아지고 있고, 따라서 나노스케일에서 재료의 기계적 거동을 분석할 수 있는 나노인덴테이션 기법이 심도있게 연구되고 있다. 본 연구에서는 나노인덴테이션, 주사탐침현미경(SPM), 투과전자현미경(TEM) 기법을 이용하여 여러가지 재료의 탄성 소성 변형 거동과 팝인/괍아웃 현상을 조사하고 해석하였다. 나노인덴테이션 기법으로는 50 마이크로뉴턴 (5 mg) 이하의 매우 작은 하중 하에서는 접촉 응력조건이라도 인장시험에서 관찰되는 영구변형이 제로인 완전탄성 변형 거동을 관찰할 수 있었다. 또한, 50-250 마이크로 뉴턴의 하중 범위에서 재료는 탄성변형 이후에 갑작스런 항복거동과 더불어 수십-수백 나노미터를 미끌어지듯 변형하는 팝인(pop-in), 또는 탈선(excursion) 현상을 관찰할 수 있었다. 이 현상은 하중을 가하는 동안에 여러 번 발생하였으며 재료의 표면상태와 전위밀도와 밀접한 상관관계를 보였다. 반복 압입 시험에서는 전형적인 가공경화 현상으로 항복점이 높아지고 새로운 항복점 이후에야 다시 팝인 발생함을 보였다. 한편, 하중을 가할 때 발생하는 팝인과는 달리 하중을 제거할 때 급격히 회복하는 팝아웃 현상 또한 관찰되었다.

• Analytical Science and Technology
• /
• v.9 no.2
• /
• pp.179-191
• /
• 1996

In order to understand the high temperature deformation behavior of superalloy 718, a rotating grade 718 alloy has been compression tested to about 0.7 upset ratio at $927{\sim}1066^{\circ}C$ temperature range and $5{\times}10^{-4}{\sim}5{\times}10^0sec^{-1}$ strain rate. The maximum flow stress was increased with increasing strain rate, and similar behavior was observed with decreasing temperature. At low temperature and high strain rates other than $5{\times}10^{-1}sec^{-1}$, strain softening was occurred mainly by dynamic recovery and deformation twinning processes, while at high temperature and low strain rates strain softening was offseted by dynamic recrystallization. At $5{\times}10^{-1}sec^{-1}$, strain hardening was occurred due to work hardening of the dynamic recrystallized grains. Strain rate sensitivity, m, was varied with strain rates. In the case of lower strain rate tests, m was measured as 0.3 and it was observed that the deformation was mainly controlled by dynamic recrystallization. At higher strain rate, m was lowered to 0.1 and the deformation was controlled by the dynamic recovery and the deformation twinning processes.