• Journal of the Korea Concrete Institute
• /
• v.26 no.4
• /
• pp.517-524
• /
• 2014

Nitrite-Type hydrocalumite (calumite) is a material that can adsorb chloride ions ($Cl^-$) that cause corrosion of reinforce bars and liberate the nitrite ions ($NO_2{^-}$) that inhibit corrosion in reinforced concrete. In this study, polymer-modified mortars using two types of epoxy resin with calumite are prepared with various polymer binder-ratios of 0, 5, 10, 15, 20% and calumite contents of 0, 5%. The specimens are tested for chloride ion penetration, carbonation, drying shrinkage and corrosion inhibition. As a result, the chloride ion penetration and carbonation depth of PMM using epoxy resin somewhat increases with increasing calumite contents, but those remarkably decreases depending on the polymer-binder ratios. The 28-d drying shrinkage shows a tendency to decrease with increasing polymer-binder ratio and calumite content. Unmodified mortars with calumite content of 5% did not satisfy quality requirement by KS. However, it was satisfied with KS requirement by the modification of epoxy resin in cement mortar. On the whole, the carbonation and chloride ion penetration depth of epoxy-modified mortars with calumite is considerably improved with an increase in the polymer-binder ratio regardless of the calumite content, and is remarkably improved over unmodified mortar. And, the replacement of the portland cement with the calumite has a marked effect in the corrosion-inhibiting property of the epoxy-modified mortars.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.11
• /
• pp.7917-7924
• /
• 2015

In this study, based on CMA which is increasingly used for eco-friendly deicing materials, dehumidification MB made of sodium carbonate, $MgCl_2$/MgO (M/M), and SAP is to be produced. And its moisture absorption rate and dehumidification performance of the film are to be analyzed. And the data on the materials used for the dehumidification film are to be acquired. In case of the dehumidification MB, in which CMA and SAP are mixed, had poor film machinability due to foaming and moisture issues, but adding bentonite and calcium carbonate solved the problem. When a foaming agent was added to extend surface area between substances, CMA and M/M showed no remarkable difference, but SC showed large increase to 3.15 g/g. As the result of anti-corrosive test, CMA dehumidification film showed no corrosion while SC showed pitting corrosion and M/M showed corrosion.