• Tribology and Lubricants
• /
• v.34 no.6
• /
• pp.254-261
• /
• 2018

In order to reduce resistance torque and energy loss, minimizing friction between race surface and rolling elements of a bearing is necessary. Recently, to reduce friction in bearing element, solid lubricant coating for the bearing raceway surface has been receiving much attention. Considering the operating conditions of real bearings, verifying the effect of solid lubricant coatings under extreme conditions of high load that is more than 1 GPa is necessary. In this study, we evaluated the friction and wear characteristics of SUJ2 bearing steels deposited by carbon-based coatings (Si-DLC, ta-C), $MoS_2$ and graphite. In case of $MoS_2$ and graphite coatings, different surface treatments were applied to the coatings to verify the effect of surface treatment. A pin-on-disc type tribotester was used to evaluate the tribological characteristics of the coatings. It was possible to quantitatively estimate the friction and wear characteristics of solid lubricant under dry and lubrication conditions. The carbon-based coatings improved the friction and wear properties of SUJ2 bearing steels under the high load condition, but $MoS_2$ and graphite coatings were not suitable for high load conditions due to its low hardness. Different friction and wear behaviors were found for different substrate surface treatment method. Also, it was confirmed that solid lubricant coatings had a more positive effect than just applying the lubricant for improving the tribological characteristics.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.28 no.2
• /
• pp.261-270
• /
• 2001

This study was performed to evaluate wear characteristics of light-cured composites when opposed by human enamel. Seven light-cured restorative composites were selected and enamel cusps sectioned from premolars. All samples were stored in distilled water at $37^{\circ}C$ for 10 days. 68.6 N of weight was loaded during the test. The measurements of vertical loss of enamel cusps, weight loss and volume loss of composites, and SEM observations of the polished and abraded surfaces were made after 30,000 cycles. The results obtained were summarized as follows; 1. The highest hardness value of 70.4 was observed in the Spectrum group and the lowest value of 19.8 was observed in the Heliomolar group. Results of Tukey test showed that an overall significant difference was indicated except the Spectrum, Z100 and Clearfil AP-X groups(p<0.05). 2. Enamel showed the good abrasion resistance against the Heliomolar group of microfilled composite and the Palpique Toughwell group containing the submicron hybrid type spherical fillers. 3. The abrasive wear resistance of hybrid composites was improved with the decrease of mean particle size and hybrid of submicron particle fillers. 4. SEM observation of worn surfaces revealed the protrusion, attrition and missing of fillers, cracks developing and delamination in the matrix.