• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.4
• /
• pp.69-78
• /
• 2012

This paper study on the physical property of naturally vulcanizing waterproofing synthetic rubber sheet for the underground concrete wall. In order to finding the naturally vulcanizing time, the relation of vulcanizing time and tensile strength is analysed from non-vulcanizing to naturally vulcanizing time. Physical tests such as tensile strength, tear strength: etc., under the thermal environment temperature at $-20^{\circ}C$, $-10^{\circ}C$, $20^{\circ}C$, $60^{\circ}C$. The result of experiment show that the developed rubber sheet has the delay time about 85 days and the curing time about 35 days. The tensile strength increased by about 692% and coefficient of expansion decreased by about 10% which value can be sufficiently compensate the demerit of vulcanized rubber sheet. Also, all of the physical properties of the naturally rubber sheet satisfy the KS standard and compare to the vulcanized rubber sheet, the developed naturally rubber sheet have excellent durability.

• Elastomers and Composites
• /
• v.42 no.2
• /
• pp.107-111
• /
• 2007

Adhesion of NR and BR composites with different initial states of precured or uncured conditions was studied. Adhesion between the NR and BR sheets as well as adhesion between the same rubber sheets was investigated. Adhesion forces of the uncured/uncured specimens were larger than those of the cured/uncured and cured/cured ones. The cured/cured samples and uncured NR/cured BR specimen were fully peeled out by the peel test. When one sheet was broken during the peel test, the sheet having the higher crosslink density was broken irrespective of the rubber types. Adhesion forces of the same rubber sheets were higher than those of the different ones and adhesion force of the cured NR/uncured BR sample was higher than that of the uncured NR/cured BR one. The experimental results were explained with the crosslink density and interdiffusion of rubber chains.

• Elastomers and Composites
• /
• v.3 no.1
• /
• pp.62-74
• /
• 1968

천연(天然)고무 및 합성(合成) 고(高) cis 1 : 4 polyisoprene, 대표적(代表的)으로 'Natsyn 400'의 가공(加工), 배합(配合) 또는 가황체(加黃體)의 성질(性質)들의 차이점(差異點)들에 대(對)하여 설명(說明)하였다. 합성중합체(合成重合體)는 미리 소연(素鍊)함이 없이 충전제(充塡劑)를 첨가(添加)함으로서 가공(加工)이 용역(容易)하였으며 CV형(形) 천연(天然)고무에 있어서도 이점(利點)이 나타났다. 천연(天然)고무 배합물(配合物)은 점착성(粘着性)이 좋으며, 특(特)히 미가황물(未加黃物)의 강도(强度)가 현저(顯著)하게 우수(優秀)하다. 가황과정(加黃過程) 및 몇몇가황체(加黃體)의 성질(性質)에 있어서의 차이(差異)는 비(非)고무질(質)을 함유(含有)하지 않는 Natsyn으로 나타난다. 기타(其他)의 가황체성질(加黃體性質)의 차이(差異)는 천연(天然)고무에 있어서 그 가황체(加黃體)가 인장시(引張時)에 결정(結晶)하는 경향(傾向)을 크게 나타내고 있고 특(特)히 고온(高溫)에서 이들 차이(差異)가 현저(顯著)하다.

• Applied Chemistry for Engineering
• /
• v.10 no.3
• /
• pp.419-426
• /
• 1999

In this study, the reaction rate constant, activation energy, total crosslinking density, elastic constant, cure properties ($t_5,\;t_{90}$), modulus, and abrasion resistance of rubber compounds were investigated as a function of cure temperatures, cure systems and reinforcing filler loadings. Reaction rate constants showed strong dependence on thc carbon black loading, cure temperature and cure system, and increased sharply with increasing the reaction temperatures. The lowest activation energy was obtained in the efficient cure (EC) system which corresponds to the high level of sulfur to accelerator ratio, and the activation energy was decreased with decreasing the carbon black loadings. The change of carbon black loadings directly affects the modulus and abrasion resistance, but the change of cure system showed various effects on the rubber compounds. Increased carbon black loadings showed the high modulus, improved abrasion resistance and short scorch time but decrease in crosslinking density and elastic constant. Higher crosslinking density and elastic constant were shown in the EC cure system regardless of carbon black loadings, but scorch timc ($t_5$) was not affected by the change of the ratio of sulfur to accelerator. Rapid optimum cure time ($t_{90}$) were showen in the EC cure system. Also, the equivalent cure curve coefficient of rubber compound was 0.96 for conventional cure (CC) system, and 0.94 for semi-efficient cure (SEC) and EC system regardless carbon black loadings. As regarding the abrasion resistance, wear volume showed the logarithmic increase for the loaded weight.

• Applied Chemistry for Engineering
• /
• v.5 no.6
• /
• pp.943-948
• /
• 1994

The properties of uncured rubber compound and swelling behavior of cured rubber compound with carbon black(N33O grade) increment. Bound Rubber content(BRC) increased according to carbon black increment and ${\alpha}_f$, behavior of uncured rubber compound filled with carbon black, was 1.46. Carbon black added to rubber compound showed behavior of spherical particle by bound rubber. The $C_1$ values of cured rubber compounds, which measured by the stress-strain method of Mooney-Rivlin, increased with carbon black increment.

• Elastomers and Composites
• /
• v.41 no.2
• /
• pp.88-96
• /
• 2006

The self-sealing rubber material for a fuel cell which has self-sealing ability, in case of fuel leakage, was studied. Cure characteristics, density, swelling, and surface morphology of foamed natural rubber were investigated with carbon black and with processing oil within the range of $10{\sim}30phr$. The rheological properties indicated that the value of $ts_2$ and the value of $Tc_{90}$ were increased with increasing a content of processing oil, while carbon black did not show a similar trend. A difference in density by foaming was decreased to one fifth scale compared to the initial value. According to the swelling test of foamed natural rubber in fuel C, isooctane and toluene, all the self-sealing action was finished in two minutes. From the SEM image for the surface of rubber compounding, a foaming by sodium bicarbonate was found to be unequal and consecutive foaming cell.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 1998.04a
• /
• pp.34-34
• /
• 1998

일반 항공기 및 상용 복합 구조재의 경우에는 내부에 결함이 생길 경우 유지 및 보수가 용이하나 복합재 압력 용기의 경우에는 다양한 환경 변화를 겪게 되며 또한 유지 및 보수가 힘들다는 제약 조건이 있으므로 단열재로 사용되는 인슈레이션 고무와 FRP간의 접착, 가황 고무와 미가황 고무 사이의 접착 등 여러 가지 이종 재질들 간의 접착이 매우 중요한 변수가 될 뿐만 아니라 압력 용기의 전체적인 성능에도 상당한 영향을 미치게 된다. 이러한 시스템들은 제작 조건에 따라 결함이 발생하는 빈도가 차이가 나며 특히 가혹한 환경 조건하에서도 내구성을 보여야 하므로 본 실험에서는 다양한 환경 조건, 성형 조건을 가지는 FRP/고무, 고무/고무 접착 시스템의 계면 접착력을 측정한 후 이로부터 환경 노화에 저항성이 강한 최적의 접착제 및 접착 조건 등을 확립하고자 하였다.

• Elastomers and Composites
• /
• v.22 no.3
• /
• pp.204-212
• /
• 1987

The purpose of this study is to investigate the reinforced effect between MGF treated silane coupling agents and rubber matrix under the configuration chemical bonds, also the effect of triazine thiol compounds. For this study, vulcanizates were prepared with fifteen different compounding formulas. Their vulcanization characteristics, physical properties were examined by means of the ODR(Oscillating Dist Rheometer), the tensile tester, the benzene swelling test. The results of this study obtained are as follows: 1. In the ODR test, the MA vulcanizate was the fastest one in terms of having reached to optimum cure time($t_{90}$) and, with the same formula, when MGF vulcanizates, the shortest optimum cure times has appeared. 2. The SA, SC vulcanizates were the best the other in the physical properties such as 100%modulus, 200%modulus, 300%modulus, tensile strength. The SB vulcanizate, with higher density of crosslinking than other vulcanizates. The vulcanizates, which were filled with MGF treated with silane coupling agents we were the higher density of crosslinking than vulcanizates filled with MGF only. 3. In aging properties, the silica vulcanizates appeared to be better than the other vulcanizates. The aging Properties of treated MGF vulcanizates were similar to the silica vulcanizates. The(CR+APS+silica) and(CR+APS+MCF) were easily crosslinked by exposure to the air, and the physical properties have been improved.

• Elastomers and Composites
• /
• v.41 no.2
• /
• pp.79-87
• /
• 2006

This study are conducted for the purpose of developing rubber material with noise and crack resistance. Cure characteristics, physical properties, thermal resistance, fuel resistance, abrasion resistance, crack resistance and noise resistance of NBR compounds with the various amounts of oleamide and aramid chip were investigated. From the measurements of cure characteristics and Mooney viscosities, cure characteristics of uncured rubber showed that a torque was decreased as the amount of oleamide increased. Hardness, modulus and elongation of rubber specimens tended to be reduced gradually, however, tensile strength remained unchanged as the amount of the oleamide increased. As a testing results of heat resistance for 70 hours at $120^{\circ}C$ and oil resistance far 70 hours at $40^{\circ}C$, tensile strength and elongation were all reduced. From the TGA/DSC analysis, there was no such a change observed in thermal characteristics of rubber materials. As a result of testing basic physical properties, abrasion resistance, noise resistance and crack resistance, the optimum ratio of oleamide to NBR was found to be 3 phr, while that of aramid to NBR 227001 was 1 phr.

• Elastomers and Composites
• /
• v.38 no.1
• /
• pp.57-64
• /
• 2003

Metal oxide(MgO) was added to FKM rubber in order to develop automotive fuel hose which ran show elastic characteristics under extreme condition. Cure characteristics, physical properties, thermal resistance and fuel resistance of FKM compounded rubber with MgO were investigated. MgO was mixed to FKM rubber materials within the range of $0{\sim}20phr$. From the test results of rheological properties and Mooney viscosity, the $t_{s2}$, $T_{c90}$ values increased as the MgO contents increased in FKM rubber compounding. Hardness and 100% modulus of FKM compounded rubber slightly increased, but tensile strength and elongations at break slightly decreased. From the test results of thermal resistance of rubber specimens at 130, 150, and $170^{\circ}C$ for 70 hrs, the changing rate of physical properties was found to be relatively small. Fuel resistance tests were carried out for fuel A, B, C and D at $40^{\circ}C$ for 70hrs, and the results showed that the changing rate in physical properties was found to increase from Fuel A to D, Furthermore thermal properties of FKM compounded rubber containing MgO were also investigated by using TGA/DSC. The optimum mixing ratio of additive to FKM rubber to get the maximum effect on thermal resistance and fuel resistance, within the range of desirable specification for rubber material, was determined to be 6 phr for MgO.