• Korean Journal of Materials Research
• /
• v.26 no.2
• /
• pp.61-66
• /
• 2016

In order to fabricate porous mullite ceramics with controlled pore structure and improved mechanical strength, a freeze casting route has been processed using camphene mixed with tertiary-butyl alcohol (TBA) and coal fly ash/alumina as the solvent and the ceramic material, respectively. After sintering, the solidification characteristics of camphene and TBA solvent were evident in the pore morphology, i.e., dendritic and straight pore channels formed along the solidification directions of camphene and TBA ice, respectively, after sublimation. Also, the presence of microcracks was observed in the bodies sintered at $1500^{\circ}C$, mainly due to the difference in solidification volume change between camphene and TBA. The compressive strength of the sintered bodies was found generally to be dependent, in an inverse manner, on the porosity, which was mainly determined by the processing conditions. After sintering at $1300{\sim}1500^{\circ}C$ with 30~50 wt% solid loading, the resulting mullite ceramics showed porosity and compressive strength values in ranges of 83.8~43.1% and 3.7~206.8 MPa, respectively.

• Resources Recycling
• /
• v.19 no.3
• /
• pp.16-23
• /
• 2010

Coal briquette use has dramatically increased because of high oil prices. Hence, it is necessary to develop an environment-friendly recycling technique of the coal briquette ash. The coal briquette ash contains a large amount of an unburned carbon content and a mullite with high thermal property, so it is considered to be used as raw materials of sintered eco-brick. This study aimed to investigate on how the unburned carbon affects properties of the sintered eco-brick. The eco-brick was mixed with the ratio of 50 wt% coal briquette ash having the unburned carbon 10.5 wt% and 50 wt% cullet, then being sintered at $950^{\circ}C$, which of the compressive strength was in line with the first class of the sintered clay brick standard(KS L 4201). In particular, the compressive strength of the sintered eco-brick was equal to the first class of the KS L 4201 despite the increase of mixing ratio for coal briquette ash with 1.0 wt% unburned carbon to 70 wt%.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.12
• /
• pp.762-767
• /
• 2017

Mullite ($3Al_2O_3{\cdot}2SiO_2$) has emerged as a promising candidate for high-temperature structural materials due to its erosion resistance, chemical and thermal stabilities, relatively low thermal expansion coefficient, excellent thermal shock and creep resistances, and low dielectric constant. However, since the pure mullite sintering temperature is as high as $1,600{\sim}1,700^{\circ}C$, there is an increasing need for a sintering additive capable of improving the strength characteristics while lowering the sintering temperature. Herein we have tried to obtain the optimal sintering additive composition by adding MgO, $Cr_2O_3$, and $Y_2O_3$ to mullite, followed by sintering at $1,325{\sim}1,550^{\circ}C$ for 2 h. With additives of 2 wt% of MgO, 2 wt% of $Cr_2O_3$, 4 wt% of $Y_2O_3$, A density of $3.23g/cm^3$ was obtained for the sintered body at $1,350^{\circ}C$ upon using 2 wt% MgO, 2 wt% $Cr_2O_3$, and 4 wt% $Y_2O_3$ as additives. The three-point flexural strength of that was 275 MPa and the coefficient of thermal expansion (CTE) was $4.15ppm/^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.43 no.4 s.287
• /
• pp.235-241
• /
• 2006

Mullite short fibers have been fabricated by adapting the Kneading-Drying-Calcination (KDC) process and characterized. The effect of the addition of foaming agent and calcination temperature on the formation of mullite fibers from coal fly ash, was examined. In the present work, ammonium alum $NH_4Al(SO_4)_2\;12H_2O$ synthesized trom coal fly ash and sodium phosphate $Na_2HPO_4\;2H_2O$ were used as foaming agents. After calcination at $1300^{\circ}C$ for 10 h and then etching with 20% HF solution at $50^{\circ}C$ for 5 h using a microwave heating source, the alumina-deficient $(AI_2O_3/SiO_2$ = 1.13, molar ratio) orthorhombic mullite fibers with a width of ${\sim}0.8mm$ (aspect ratio >30), were prepared from the coal fly ash with $AI_2O_3/SiO_2$ = 0.32, molar ratio by the addition of $NH_4AI(SO_4)_2\;12H_2O$, and with further addition of 2 wt% sodium phosphate. The excessive addition of sodium phosphate rather decreased the formation of mullite fibers, possibly due to the large amount of liquid phase prior to mullitization reaction.

• Journal of Conservation Science
• /
• v.28 no.1
• /
• pp.7-20
• /
• 2012

This study was to identify the material characteristics and provenance of the Joseon (the 15th to 17th century) potteries from Ssangyongdong Yongam site in Cheonan. The pottery samples of the kilns and the workshops (habitation) from the study area have grey or red color with similar matrix but various shapes and different hardness, according to firing temperature. All of the pottery and the workshop soils were very similar patterns with characteristics of occurrences, mineralogy and geochemical evolution trend. But soils from around the site does not correspond with them. So the workshop soil that the fine clay is raw clay for making pottery in Yongam site. Firing temperature of soft-type potteries were presumed to be formed around $900^{\circ}C$ based on phase transition of clay minerals and mica. Hard-type pottery, mullite was detected and plagioclase was not detected by X-ray diffraction analysis, which means that potteries had experienced firing between 1,000 to $1,100^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.12 no.7
• /
• pp.573-579
• /
• 2002

Stoichiometric mullite ($3Al_2$$O_3$. $2SiO_2$) precursor sol has been prepared by sol-gel method. The effects of the precursor pH and sintering temperature on the synthesizing behavior and morphology of mullite have been studied. Mullite precursor sol was prepared by dissolution of aluminum nitrate enneahydrate (Al($NO_3$)$_3$.9H$_2O) into the mixture of silica sol. Precursor pH of the sols was controlled to acidic condition ($PH\leq$ 1~1.5) and to basic condition ($pH\geq$8.5~9). The synthesized aluminosilicate sols were formed under 20 MPa pressure after drying at $150^{\circ}C$ for 24 hours, and then sintered for 3hours in the temperature range of $1100~1600^{\circ}C$. From TGA/DTA analysis, total weight loss in the aluminosilicate gel of the acidic sample was (equation omitted) 56% and that of the basic sample was (equation omitted) 85%, indicating that the synthesizing temperature of mullite phase for acidic and basic samples was above $1200^{\circ}C$ and $1300^{\circ}C$, respectively. The morphologies of the synthesized mullite were fine and needle-like (or rod-like) for acidic sample, and granular for basic sample that has been sintered above $1300^{\circ}C$. It was found that the morphology of mullite particle was predominantly governed by precursor pH and sintering temperature.

• Korean Journal of Materials Research
• /
• v.28 no.12
• /
• pp.719-724
• /
• 2018

Cordierite composed of an alumina-silica-magnesia compound has a low coefficient of thermal expansion(CTE) and excellent thermal shock resistance. It also has a low dielectric constant and high electrical insulation. However, due to low mechanical strength, it is limited for use in a ceramic heater. In this study, $ZrO_2$ is added to an 80 wt% cordierite-20 wt% mullite composition, and the effect of $ZrO_2$ addition on the mechanical strength and thermal shock resistance is investigated. With an increasing addition of $ZrO_2$, cordierite-mullite formed $ZrO_2$, $ZrSiO_4$ and spinel phases. With sintering conducted at $1400^{\circ}C$ with the addition of 5 wt% $ZrO_2$ to 80 wt% cordierite-20 wt% mullite, the most dense microstructure forms along with an excellent mechanical strength with a 3-point flexural strength of 238MPa. When this composition is quenched in water at ${\Delta}T=400^{\circ}C$, the 3-point flexural strength is maintained. Moreover, when this composition is cooled from $800^{\circ}C$ to air, the 3-point flexural strength is maintained even after 100 cycles. In addition, the CTE is measured as $3.00{\times}10^{-6}{\cdot}K^{-1}$ at $1000^{\circ}C$. Therefore, 80 wt% cordierite-20 wt% mullite with 5 wt% $ZrO_2$ is considered to be appropriate as material for a ceramic heater.

• Korean Journal of Materials Research
• /
• v.32 no.5
• /
• pp.258-263
• /
• 2022

Porous ceramics have the advantages of low density, low thermal conductivity, and excellent mechanical properties. Among porous ceramic manufacturing methods, the replica template method allows the easy manufacturing of porous filters with the highest porosity and pores of the desired size, but it also has the disadvantage that the resulting filters have low mechanical strength. To overcome this shortcoming, mullite (3Al₂O₃·2SiO₂) whiskers, which have excellent thermal stability and high mechanical strength, were introduced in porous ceramic structure. The mullite whiskers were synthesized using a composition of Al₂O₃, flyash and MoO₃. The morphologies and crystal structures of the mullite whiskers with MoO₃ contents were investigated in detail. When the porous ceramic with mullite whiskers was fabricated using 20 wt% MoO₃ catalyst the most uniform microstructure was obtained, and the mullite whiskers showed the highest aspect ratio of 47.03. The porosity and compressive strength of the fabricated porous ceramic were 82.12 % and 0.83 MPa, respectively.

• Resources Recycling
• /
• v.23 no.1
• /
• pp.40-47
• /
• 2014

Feasibility of utilizing unburned carbon residue in coal ash as a potential precursor for the production of activated carbon was assessed to seek for solution to recycle unburned carbon residue. The unburned carbon concentrate generated from the 4 stages of cleaner flotation has a grade of 87% carbon. The crystalline impurities in the concentrate included quartz and mullite. Unburned carbon had a low specific surface area of $10m^2/g$, which might be related to a high degree of coalification of domestic anthracite coal. Carbon particles were mostly porous and have a turbostratic structure. When 1g of carbon was activated with 6g of KOH powder, the highest specific surface area value of $670m^2/g$ was achieved. Low wettability of unburned carbon particles, which was resulted from high temperature combustion in a boiler, might cause poor pore formation when they were activated by KOH solution. The activated carbon produced in this study developed micropores, with an equivalent quality of general-purpose activated carbon made from coal. Hence, it is concluded that chemically treated unburned carbon can be used for water purification or an alternative to carbon black as it is.

• Composites Research
• /
• v.30 no.2
• /
• pp.84-93
• /
• 2017

This study investigates thermal and mechanical characterization of environmental barrier coating on the $SiC_f-SiC$ composites. The spherical environmental barrier coating (EBC) powders are prepared using a spray drying process for flowing easily during coating process. The powders consisting of mullite and 12 wt% of Ytterbium silicate are air plasma sprayed on the Si bondcoat on the LSI SiC fiber reinforced SiC composite substrate for protecting the composites from oxidation and water vapor reaction. We vary the process parameter of spray distance during air plasma spray of powders, 100, 120 and 140 mm. After that, we performed the thermal durability tests by thermal annealing test at $1100^{\circ}C$ for 100hr and thermal shock test from $1200^{\circ}C$ for 3000 cycles. As a result, the interface delamination of EBC never occur during thermal durability tests while stable cracks are prominent on the coating layer. The crack density and crack length depend on the spray distance during coating. The post indentation test indicates thermal tests influence on the indentation load-displacement mechanical behavior.