• Journal of Conservation Science
• /
• v.35 no.6
• /
• pp.573-587
• /
• 2019

In this study, reproducing specimens were made from mixing domestically produced magnetite, clay and non-plastic raw materials to reproduce the pigments used in the manufacture of traditional cheolhwa buncheong stoneware. In order to reveal the color fomation of glaze, 30 specimens with good color development were analyzed scientifically. Magnetite, which is the main raw material of the pigment, is a pigment capable of creating a dark black color in a reducing environment at 1,200℃. However, it reacts with the additionally added lime component and discolors to greenish yellow color in oxidizing environment at 1,230℃. Hematite is not significantly affected by the firing temperature and environment, but develops a dark black color when mixed with clay with iron content of more than 10%. The fluidity of the pigment is determined by R₂O₃/RO₂ value, which also affects the color development. In the microtexture observation, the color formation of the glaze layer and the iron oxide crystals identified some differences depending on the particle size of the pigment and the firing environment. Reproduced specimens made of magnetite are present in the form of aggregates of iron oxide in the interface between glaze layer and slip layer in the oxidizing environment at 1,200℃. However, in the reducing environment, aggregates of iron oxides do not exist in the reproduced specimens, and they are homogeneously distributed in the glaze layer and formed a dark black color. In contrast, hematite-based specimens form dendritic structures in the glaze layer in an oxidizing environment and develop black.

• Journal of Conservation Science
• /
• v.31 no.4
• /
• pp.403-409
• /
• 2015

Malachite and Azurite are the typical copper system pigments which used the mural paintings since ancient times. The mural painting is at risk for damages of the painting layer by atmosphere gas because it is exposed at external environment. In this study, it did experiment about an effect to Malachite and Azurite by environmental pollution gas($NO_2$, $CO_2$, $SO_2$) then analysis and estimate about test for pieces using mural painting colored that two pigments. As a result, Malachite and Azurite were changed on $NO_2$ but not changed $CO_2$ and $SO_2$. Especially as the concentration of $NO_2$ is increased, exfoliation of the pigment layer weave remarkably formed pores on the pigment particles on SEM, the phenomenon to be pieces were observed together with smaller particles. In the case of Malachite that were exposed to $NO_2$ gas, new compounds(Rouaite : dicopper (nitrate(V) trihydroxide, $Cu_2(NO_3)(OH)_3$)) was appeared by XRD analysis. Therefore, there had been able to verify the fact that the cause exfoliation and discoloration phenomena accompanied by chemical changes for Malachite and Azurite.

• Journal of Conservation Science
• /
• v.25 no.2
• /
• pp.179-196
• /
• 2009

The Gaetaesajiseokbulibsang (Treasure No. 219) consists of light gray and coarse to medium-grained granodiorite with feldspar phenocrysts in part. Magnetic susceptibility of the rock material was measured as 12.06(${\times}10^{-3}$ SI unit), being different from the granite($0.19{\times}10^{-3}$ SI unit) in the Mt. Cheonho. This indicates the raw material has been supplied from the outside. As a result of deterioration assessment, exfoliation of the Right Buddha, cement and dust of the Main Buddha were estimated as 35.2%, 21.1% and 25.0%. The ultrasonic velocity was measured as 2850.2m/s(Main Buddha), 2648.4m/s(Left Buddha) and 2644.5m/s(Right Buddha). The compressive strength calculated from the velocity showed low in the Right Buddha among three and the all pedestal parts which corresponds to the result of deterioration assessment. The indoor mean temperature and relative humidity of the shelter were $13.7^{\circ}C$ and 79.0%. It is evaluated that the indoor microclimate was stable and the shelter functioned to reduce climatic fluctuation of the outdoor. However, water condensation was occurred on the surface of the pedestal part during spring and summer, and freezing in winter season might also be done. These factors were probable to be a main cause of the surface exfoliation of the Triad Buddha Statues. Therefore, dehumidification and heating system in the shelter should be applied to prevent further deterioration.

• Journal of Conservation Science
• /
• v.33 no.3
• /
• pp.203-214
• /
• 2017

This study evaluated the degradation characteristics of FRP by ultraviolet (UV) rays and applied a UV-resistant coating to prevent the degradation of the surface of these sculptures. As a result of the degradation caused by UV rays, there were slight changes in the FRP surface and contact angle. The chromaticity sharply increased in the early phase of degradation. After applying the coating to the FRP, no significant surface changes were observed. However, it had lower changes in color as compared to the uncoated specimen, so it was verified that the control of discoloration could be possible. Some changes in the gloss and contact angle were observed depending on the extent of degradation, but the UV coating agent remained relatively stable. Analysis of the infrared light spectrum showed that there were almost no chemical changes, and it could be concluded that the coating treatment prevented degradation for a certain period. This study investigated the degradation of FRP used as materials in artwork exposed to UV rays, and it was found that there was a delay in the onset of degradation in the FRP with the UV-resistant coating when compared to the uncoated FRP.

• Journal of Conservation Science
• /
• v.26 no.2
• /
• pp.121-132
• /
• 2010

The Bukjiri Maaeyeoraejwasang (National Treasure No. 201) consists of two-mica granite in medium size, which was the simbol of power in the region of the Silla period. Magnetic susceptibility of the host rock was measured as 0.41(${\times}10^{-3}$ SI unit), which has the similar range with surrounding outcrop. The Buddha developed parallel discontinuous plane of NE to SW strike and damaged seriously by exfoliation, granular disintegration and brown discoloration as 41.5%, 16.7% and 40.0%, respectively. As a result of the ultrasonic velocity, which was relatively weak values as 1,629m/s (Buddha area) and 1,549m/s (surrounding outcrop), improved about 900m/s compared to last treatment. From the results of the evaluation for slope stability, identified the possibility of toppling failure in the Buddha, and planar and wedge failure in host rock. Therefore, we suggest for the safely conservation of the Buddha, continuance monitoring for understand behavior of discontinuity system of the surface, and necessitate foundation reinforcement method for the rock which has the danger of collapse.

• 보존과학연구
• /
• s.33
• /
• pp.125-148
• /
• 2012

The Octagonal nine storied pagoda of Woljeongsa Temple consists mainly of granite with the rockforming minerals quartz, plagioclase, microcline, and biotite. The surface of the stone stupa is light brown that has been discolored by the rust from the metal ornament and aids. The surface of the stylobate and roof stone is colonized by biological contaminants. Therefore, a comprehensive deterioration diagnosis was carried out in this study, and conservation treatment was conducted. It was proven that the $Fe^{2+}$ yield increases depending on the count of poultice used with oxalic acid, but the $Mg^{2+}$, $Al^{3+}$, and $Ca^{2+}$ yields were marginal following the preliminary test. Therefore, the use of poultice is an effective way of removing the rust, and only marginally influences the rock. The biological contaminants were removed through dry cleaning, and the soil located under the contaminants was removed through wet cleaning. Based on this, the dry and wet cleaning of all the biological contaminants, and the use of poultice with oxalic acid, were done to remove the rust. For the conservation treatment of the metal ornament, the rust was removed through physical cleaning, and anticorrosion treatment was performed on the iron ornament using Renaissance wax and copper ornament by BTA.