• Tribology and Lubricants
• /
• v.8 no.2
• /
• pp.20-25
• /
• 1992

Friction and wear behavior of hot isostatic pressed $Al_2O_3-TiC$ was experimentally examined. Pin-on-disk type friction and wear apparatus was designed and manufactured for the experiment. The experiments were conducted under unlubricated sliding motion in both low and high humidity for three kinds of sliding speed. $Al_2O_3-TiC$ and bearing steel were used as counterface materials. Friction coefficient, wear rate, and surface roughness were measured. Wear surface and wear debris were observed through optical microscope and SEM and analyzed by EDAX. The results showed that the counterface materials, the sliding speed, and the moisture at the sliding surface have significant influence on the friction coefficient and wear rate of $Al_2O_3-TiC$.

• Tribology and Lubricants
• /
• v.24 no.6
• /
• pp.386-392
• /
• 2008

Friction and wear behavior of hard coated and surface treated steel with candidate processing methods for low velocity high pressure application investigated. Wear tests were carried out under specific region considering the operation condition of construction equipments under lubricated and unlubricated condition. Different tribological behavior analyzed with comparing the wear rate of counter part, morphology and topography of worn surface and the worn volume of samples and counter parts.

• Tribology and Lubricants
• /
• v.25 no.3
• /
• pp.141-149
• /
• 2009

The effect of micro-cavities fabricated using laser surface texturing (LST) technique on polyoxymethylene (POM) surface was studied in terms of heat affected zone (HAZ), cavity geometry, surface roughness, deformation of cavity along with sliding cycles, and tribological characteristics. Cavity process parameters were lamp current, process time, and the stream of air used to minimize the flow of molten polymer into cavity. Especially, the deformation of cavity geometry was extensively studied to provide deep insight into morphological analysis of the cavities. Also, this paper presents the behavior of friction and wear of POM specimens as a function of sliding cycles.

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.5 s.98
• /
• pp.145-150
• /
• 1999

We have studied on the tribological characteristics of surface modification by Arc Ion Implantation(AIP) coating method. Coating materials were deposited by the Titanium carbide(TiC) and Titanium nitride(TiN). An experimental process was established to determine the tribological characteristics of friction and wear behaviour with the variation of applied load, temperature and the time by the Falex friction and wear test machine. The results, It can be improved that when the surface modification of hard coatings(TiC, TiN) was deposited steel, the tribological characteristics become better. It is argued that improved because of excellence of the anti-wear, the extreme pressure properties and the heat stability.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2003.11a
• /
• pp.105-111
• /
• 2003

The valve train system of engines has long been a sensitive area with respect to wear performance because of the high contact loads and surface sliding speeds encountered. In particular, wear problems of load-carrying components in relative motion, such as cam and tappet in valve train system have made troubles. To overcome these problems, combination of proper materials is important, as well as selecting of high wear performance materials. This paper presents the experimental result of friction and wear properties of ca/tappet materials. To investigate friction and wear properties for several combinations of materials, using commonplace tribometer(Plint 77, reciprocating type), we make a selection of a optimum material combination.

• Tribology and Lubricants
• /
• v.12 no.2
• /
• pp.32-40
• /
• 1996

The tribological role of copper alloy fine particles in an additive is not well known compared to solid lubricants such as $MoS_{2}$ and PTFE. In this experimental investigation, a series of friction and wear test was undertaken to gain a better understanding of an additive containing copper alloy fine particles and to identify the effectiveness of copper alloy particles in improving tribological performance of the lubricant. Friction and wear of specimens under lubricated contact condition were studied and the worn surfaces were characterized by AES (Auger Electron Spectroscopy), SEM (Scanning Electron Microscopy) and optical microscopy. It was revealed that a copper-contained layer was formed and this layer resulted in considerable reduction in both friction and wear due to its lubricity and anti-wear property. The analysis of worn surface revealed that copper of the fine alloy particles in the additive helps healing the worn surface by plating and filling wear pits.

• Tribology and Lubricants
• /
• v.5 no.1
• /
• pp.12-20
• /
• 1989

The friction and wear behavior of molybdenum disulfide filled polymer composites sliding against metal has been investigated using pin-on-disc machine and microscope. The observed wear rates were reduced by the addition of MoS$_2$ to nylon and this can be attributed to the homogenous transfer of MoS$_2$ to the counteddace thereby modifying sliding conditions. The friction of filled and unfilled nylon was increased with increasing sliding speed, and the catastropic wear rate was occurred at high normal load. This have been explained by thermal degradation. In the case of HDPE, however, the wear rate was not always reduced by the addition of MoS$_2$ and the influence of MoS$_2$ was mainly even the opposite. Filled and unfilled HDPE had lower values of friction and wear rate than those of nylon. Micrographs appeared that the delamination of the worn surface in nylon/MoS$_2$ composite occurred and revealed that the worn surface of HDPE presented a number of characteristic features as wear grooves, pulls, and smears and crescents.

• Tribology and Lubricants
• /
• v.15 no.2
• /
• pp.156-163
• /
• 1999

The mechanical characteristics of the high speed steel by Powder metallurgy Process (PM-HSS) has been reported to improve with several alloying constituents, such as high carbon, vanadium and cobalt. In this paper, sliding wear test has been conducted using a pin-on-disc machine for three PM-HSS which contains 0%, 5% and 12% cobalt respectively, in order to evaluate the effect of cobalt on wear properties of PM-HSS. The results of this study showed that the wear resistance of PM-HSS has been increased by the addition of cobalt on the range of experimental friction velocities. When compared with the effect of addition of cobalt, the wear resistance of PM-HSS with 5% cobalt has been found to be superior to that of PM-HSS with 12% cobalt.

• Tribology and Lubricants
• /
• v.15 no.4
• /
• pp.328-334
• /
• 1999

Acoustic emission (AE) sensor was used to evaluate the wear-life of CrN-coated steel disks with 1 $\mu\textrm{m}$ and 4 $\mu\textrm{m}$ coating thickness. The relationship between Af and friction signal from scratch test and sliding test was investigated. The first spatting of CrN film was detected by AR signals in the early stage of coating failures, and overall failures by friction signals. Therefore, the conservative design for coating-life should be done using the results of AE signals. Using the percent contact load, the ratio of sliding normal load to the critical scratch load and the number of cycles to failure was measured to predict the wear-life of CrN film. On the wear-life dia-gram the percent contact loads and the number of cycles to failure showed a good linear relationship on the log coordinate. As the load percentage was decreased, the diagram showed that the wear-limits, at which the coated steels survived more than 35,000 cycles, were about 4∼5% of the critical scratch loads.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.7 no.5
• /
• pp.213-220
• /
• 1999

The life data analysis of the system and component are useful to describe the result of reliability test in product life to satisfy customer's growing need and to change test specifications or design criteria by life data analysis. And vehicle durability tesr occurred market environment. In this study, a statistical analysis for the wear life of brake pad linings helped perform correlation procedure between vehicle durability test and market. B-life values of the brake pad wear life data from both vehicle durability test and marker usage were compared to determine acceleration of the test by the Weibull, normal and log-normal distribution. The acceleration coefficient of the vehicle durability test can access to evaluate design criteria of product and test specification.