• Journal of Welding and Joining
• /
• v.16 no.1
• /
• pp.125-133
• /
• 1998

The effect of volume fraction of Cr carbide phase (Cr CVF) on the low stress abrasion resistance in the chromium-carbide-type high Cr white iron hardfacing weld deposits has been investigated. In order to examine Cr CVF, a series of alloys with varying Cr CVF by changing chromium and carbon contents and the ratio of Cr/C were employed. The alloys were deposited once or twice on a mild steel plate using the self-shielding flux cored arc welding process. The low stress abrasion resistance of the alloys against sands was measured by the Dry Sand/Rubber Wheel Abrasion Test (RWAT). It was shown that hardness and abrasion resistance increased with increasing Cr CVF within the whole test range (Cr CVF : 0.23-0.64). Both primary Cr carbide and eutectic Cr carbide were particularly effective in resisting wear due to their high hardness.

• Journal of Korea Foundry Society
• /
• v.20 no.4
• /
• pp.260-268
• /
• 2000

응고 및 마모거동을 연구하기 위하여 Cr, V, Mo 및 W의 조성이 다른 3종류의 백주철을 주조하였다. 고주파유도용해로에서 장입시켜 1873K까지 승온시켜 장입원료들을 모두 용해시킨 후 1823K에서 Y블럭주형에 주입하였다. 얻어진 3종류의 백주철조성은 다음과 같다: Fe-3%C-10%Cr-5%Mo-5%W(합금1), Fe-3%C-10%V-5%Mo-5%W(합금2) 및 Fe-3%C-17%Cr-3%V(합금 3)응고과정을 추적하기 위하여 각 시편으로부터 50g을 채취한 후 알루미나도가니에 넣고 실리콘카바이드로를 사용하여 1723K의 알콘분위기하에서 재용해를 시켰다. 용금을 10K/분의 속도로 냉각시키면서 열분석을 행하였으며 도중 몇 차례 소입 실험을 병행하였다.합금1의 경우 초정오스테나이트, (오스테나이트+$M_7C_3$)공정, (오스테나이트+$M_6C$)공정, 합금2의 경우 초정 MC, 초정오스테나이트, (오스테나이트+MC)공정 , (오스테나이트+$M_2C$)공정, 합금3의 경우 초정 $M7C_3$와 (오스테나이트+$M_7C_3$)공정으로 구성되어 있었다. 주방상태, 균질화열처러상태, 공냉상태, 템퍼링상태에서 내마모시험을 행하였다. 먼저 주방상태시 편을 진공분위기하에서 1223K에서 5시간동안 균질화열처리를 행한후 로냉을 시켰다. 다시 이 시편을 1323K에서 2시간 유지후 강제공냉을 시켰으며 강제공냉된 시편을 573K에서 3시간동안 템퍼링처리를 하였다. 내마모시험은 120 mesh마모지에 10N의 하중을 가하여 실시하였다. 각 사이클마다 무게감소를 측정하였으며 8번 반복실험을 하였다. 마모량은 균질화열처리시편, 주방상태시편, 템퍼링시편, 공냉시편의 순으로 감소하였다. 합금2가 마모량이 가장 적었으며 합금3이 가장 많았다. 합금2의 마모량이 가장 적은 이유는 조직이 초정 MC, 공정 MC 및 공정 M2C로 구성되어 있기 때문으로 사료된다.주방상태에서 기지조직은 퍼얼라이트이었으나 열처리를 통하여 마르텐사이트, 템퍼드마르텐사이트, 잔류오스테나이트로 변태하였다. 이상의 결과를 종합해 보면 MC가 내마모성에 가장 기여하는 조직으로 판단되어진다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.2
• /
• pp.217-223
• /
• 1999

In this study, the effects of the content of $ZrO_{2}$ in $Si_{3}N_{4}$ on mechanical and wear properties were investigated. $Si_{3}N_{4}$ based composites containing 0~40 wt% $ZrO_{2}$ powders were fabricated using hot isostatic pressing (HIP), at $1750^{\circ}C$, 172 MPa for 1 hour in $N_{2}$ gas. Mechanical properties and wear properties of composites were examined. Mechanical properties (hardness, strength, and fracture toughness) of $Si_{3}N_{4}-ZrO_{2}$ composite were decreased with increasing the amount of $ZrO_{2}$, but relative density of composites were increased. Further, the increase in amount of $ZrO_{2}$, reduced wear rates in air. It was found that wear behaviors in air were related to microcracking.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.130-131
• /
• 2012

DC magnetron sputtering 장치를 이용하여 Al-Mg 합금 타겟의 조성비에 따른 박막의 미세구조를 관찰하였다. 그 결과 타겟의 조성비와 주요 공정변수 (인가전원밀도, 공정압력, 성장온도)에 따른 미세구조 형성거동을 알 수 있었으며, 내식성이 우수할 것이라 판단되는 평탄하고 매끄러운 표면구조와 치밀한 단면구조를 보이는 공정 조건을 도출하였다. 또한, 정변수에 따른 합금 박막의 내부응력 및 마모특성을 조사하였다.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1996.04a
• /
• pp.87-92
• /
• 1996

본 연구에서는 건조 마찰, 윤활제가 부족한 경우의 경계 윤활, 윤활제가 충분한 경우의 경계 윤활 상태에 대한 실험을 수행하여 각 윤활 상태에서의 요철표면의 성능을 알아 보고 요철 표면의 요철 표면의 성능에 영향을 주는 주된 요인을 알아보았다.

• Proceedings of the KWS Conference
• /
• 1999.10a
• /
• pp.132-135
• /
• 1999

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.311-311
• /
• 2005

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.52.1-52
• /
• 2002

• Journal of Power System Engineering
• /
• v.11 no.1
• /
• pp.121-126
• /
• 2007

This study aims at investigating the effect of heat treatment conditions on the dry sliding wear behavior of thermally sprayed Ni-based self-flux alloy coatings. Ni-based self-flux alloy powders were sprayed onto a carbon steel substrate and then heat-treated at 700, 800, 900 and $1000^{\circ}C$ for 30 minutes in a vacuum furnace. Dry sliding wear tests were performed using sliding speed of 0.4 m/s and applied load of 6 N. AISI 52100 ball(diameter 8 mm) was used as counterparts. Microstructure and wear behavior of both as-sprayed and heat-treated Ni-based self-flux alloy coatings were studied using a scanning electron microscope(SEM), energy dispersive X-ray spectroscopy(EDX), electron probe micro-analysis(EPMA) and X-ray diffraction(XRD). It was revealed that microstructure and wear behavior of thermally sprayed Ni-based self-flux alloy coatings were much influenced by heat treatment conditions.

• Tribology and Lubricants
• /
• v.30 no.6
• /
• pp.364-369
• /
• 2014

To assess the wear behavior of rails against subway rail car wheels, we investigate the sliding wear behavior of pins derived from two types of rails (normal rails and heat-treated rails) against a disc derived from a subway rail car wheel, using a pin-on-disc-type tribometer. We base the sliding wear test conditions on the sliding conditions for wheel flange-rail gauge corner contact. We demonstrate the remarkable transition in the wear behavior of the pins derived from the rails, from severe wear to mild wear, as a function of the sliding distance. The wear rate of the heat-treated rail material in the running-in wear region is much lower than that of the normal rail material. Furthermore, the wear rates of the pins in the running-in wear region decrease with increasing hardness and with decreasing sliding speed. However, there is little difference between the heat-treated rail pin and the normal rail pin in the wear rate in the steady-state wear region. Stricter controls on the decarburized layer beneath the surface of rails are required to reduce the wear rate in the running-in wear region.