• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.8
• /
• pp.1015-1021
• /
• 2010

In this study, the effect of the C/SiC composition ratio on the impact damage of a reaction sintered SiC (RS-SiC) plates was evaluated. An impact test was conducted by using an air gun. The impacter used was a steel ball with a diameter of 2 mm, and the impact velocities were 113, 122, and 180 m/s. The RS-SiC plates were $20\times20\times3$ mm with different C/SiC composition ratios. The ring crack diameters damaged by a steel ball were determined using SEM images. It was observed that the maximum diameter increased with increasing impact velocity, and it rapidly changed with increasing C/SiC composition ratio because of the effect of residual Si and the variation flexural strength. Cone cracks were formed in the case of C/SiC composition ratios of 0.4~0.5, this indicated that the impact damage changed from a ring crack to a cone crack in this critical range of C/SiC composition ratios. The C/SiC composition ratio of 0.3 was determined to be the optimal ratio for the RS-SiC manufacturing process.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.6
• /
• pp.1903-1912
• /
• 1996

A quantitative study of impact damage of a soda-lime glass was carried out. An initiation and a propagation of cracks by the impact of two inds of steel ball was investigated. The fron, side and rear view of cracks were observed by a stereo-microscope. And the lowering of the benidng strength due to the impact of steel balls was examined through the 4-point bending test. A transparent glass is very helpful to understand and analyze the impact damage behavior of another brittle matereial. A deagdram about crack patterns according to the threshold impact velocity was sketched. A ring crack and a cone crack were formed at the low impact velocity. And as the impact velocity was higher, initial lateral crack was generated on the slanting surface of cone crack, and radial cracks were generated from the outermost ring crack. When the impact velocity of steel balls exceed a critical velocity, the contact site of specimens were crushed. According to the propagation of a cone crack, a rapid strength degradation occurred. In the specimen having crushed region, a bending strength was converged to a constant value instead of strength degradation.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.7
• /
• pp.2196-2204
• /
• 1996

The damage mechanism by the impact of steel ball on the soda-lime glass having a different surface roughness was investigated. An initiation and a propagation behavior of cracks formed by each impact velocity were quantitatively studied. A 4-point bending test was carried out to evaluate the remaining bending strength of a scratched soda-lime glass which impacted by the steel ball. As the surface roughness was increased, the shape of cracks became more irregular rather than those of the smooth specimens. The phenomenon of turning up in the wing of cone cracks occurred even at the lower velocity than the critical velocity caused the crushing. The threshold velocity of cracks initiation generally became lower than those of smooth specimen. An initiation and a propagation behavior of radial cracks had no relation with the direction of scratch on the surface. The remaning benidng strength of the scratched specimen according to impact velocity had no big difference compared with those of the smooth specimen.

• Journal of Ocean Engineering and Technology
• /
• v.12 no.3 s.29
• /
• pp.49-59
• /
• 1998

The damage mechanism of $Cr_2O_3$ plasma coated soda-lime glass and uncoated glass by steel ball particle impact was analyzed in this study. And the shape variation of the cracks was investigated by stereo-microscope according to the impact velocity and steel ball diameter. In order to improve the damage reduction effect by $Cr_2O_3$ coating layer, crack size was measured and surface erosion state was observed for both of two kinds of specimen after impact experiment. And the results were compared with each other. The 4-point bending test was performed according to ASTM D790 testing method to evaluate the effect of coating layer for bending strength variation. As a result, it was found that the crack size of $Cr_2O_3$ coated specimen was smaller than that of uncoated one, because of the impact absorption by interior pores in the coating layer and the load dispersion by the structural characteristic of the coating layer. For the specimens subjected to the steel ball impact, the bending strength of coated specimen was higher than that of uncoated specimen.