• 한국농공학회논문집
• /
• 제49권5호
• /
• pp.23-30
• /
• 2007

This research was to evaluate the shrinkage and durability performance of latex modified repair mortar and to improve the service lift of the agricultural concrete structures. The shrinkage characteristics of the repair material creates the delamination of repair materials and existing concrete. It may reduce the service life of structures. Also the reduction of durability performance of the repair materials induces the destruction of the repaired concrete structures at early stage. In this research, plastic and drying shrinkage, thermal expansion coefficient for shrinkage properties, durability performance, permeability, repeated freezing and thawing, and resistance of chemical solution test were performed. Test results showed that the latex modified repair mortar indicated the shrinkage amount which the delamination does not happen, and the latex modified repair mortar appeared excellent long-term durability performance which can increase the service life.

• 한국농공학회논문집
• /
• 제49권3호
• /
• pp.43-50
• /
• 2007

The purpose of this study was to determine the optimum mix proportion of latex modified mortar for agricultural underwater concrete structures repair. The experimental variables included a latex and antiwashout admixture amount, binder-sand ratio, water-binder ratio. This study were evaluated a repair performance and environment effect of latex modified repair mortar for agricultural underwater concrete structures. The pH test was conducted to evaluated the environmental effect and the flow test was peformed to evaluated the workability. Also, compressive, flexural and bond tests were conducted. Test results show that the optimum mix proportion of latex modified repair mortar for agricultural underwater concrete structures, was achieved by 1:1.5 binder-sand ratio, 5% latex ratio (weight of binder), 1.3% antiwashout admixture ratio (weight of binder), 0.33 water-binder ratio and 10% silica lune replacement ratio (weight of cement). The environmental effect and repair performance of optimum mix proportion satisfied all target performance.

• 한국농공학회논문집
• /
• 제49권4호
• /
• pp.35-41
• /
• 2007

The most agricultural concrete structures for the irrigation and drainage are exposed to the underwater condition at the irrigation period and they take the influence on very severe cold in the winter. Therefore, it is impossible to use repair materials used to the general concrete structures. The research need the development of the repair material for a performance enhance of the agricultural underwater concrete structures. This research evaluated the mechanical and durability performance of the latex modified repair mortar for underwater concrete structures which peformed the repair in the underwater according to the characteristic of the agricultural concrete structure. The latex modified repair mortar is a material that minimize the effect of the ecosystem, environment and the segregation. In this research, the construction condition of the latex modified repair mortar for agricultural concrete structures was considered and the test specimens made in the underwater condition. Test results was then compared with target performance and commercial repair mortar. Experimental test results indicated that the mechanical and durability performance of latex modified repair mortar for agricultural underwater concrete structure satisfied all target performance. Also, the latex modified repair mortar resulted in better repair performance than the commercial repair mortar.

• 한국농공학회논문집
• /
• 제50권5호
• /
• pp.39-50
• /
• 2008

This study are decided the mix proportion method of latex modified concrete for agricultural concrete structures from the results of workability and strength test with mix proportion factor. For mix proportion factor, this study are selected the water-cement ratio, unit cement amount and latex content. Also, this study were performed the slump, compressive strength test and microstructure analysis using the scanning electron microscope(SEM). The strength and slump of LMC are dependent with unit cement amount, latex content, and water-cement ratio. Especially, the strength of LMC are not controlled by single mix proportion factor but effected by combined mix proportion factor. Microstructure investigation are showed the LMC are reduced the internal pore volume and enhanced the transition zone between cement paste and aggregate interface. This effect get by consist of latex films in the concrete. Also, this study were recommended the mix proportion method for LMC. These mix proportions method are estimated the mix design for satisfied the target performance which are applied the agricultural concrete structure.

• 콘크리트학회논문집
• /
• 제18권6호
• /
• pp.785-791
• /
• 2006

본 연구에서는 스틸렌(styrene)과 부틸아크릴레이트(butyl acrylate)를 모노머 비에 따라 합성 제조하고, 합성 제조 된 시멘트 혼화용 폴리머를 혼입한 폴리머 시멘트 모르타르의 물리적 성질과 내구성에 대한 특성을 보통 시멘트 모르타르와 기존에 생산되어 현장에 적용되고 있는 St/BA계 폴리머 시멘트 모르타르를 비교 분석하고자 하였다. 실험 결과, St/BA의 모노머 비가 50:50, 60:40일 경우에는 시멘트 혼화용으로 사용하기에 가장 적합하였으며, 세공용적의 분포나 강도 특성에서도 우수한 결과를 나타냈다. 또한 방수성능과 염화물 이온에 대한 침투 저항성도 St/BA의 모노머비가 증가할수록, 폴리머 시멘트 비가 증가할수록 증진 효과가 우수한 결과를 나타냈다. 따라서 본 연구를 통해 합성제조된 St/BA 라텍스를 시멘트 모르타르에 혼입할 경우 우수한 성능개선 효과를 얻을 수 있었다.

• 한국방재학회 논문집
• /
• 제10권2호
• /
• pp.47-53
• /
• 2010

초속경 LMC(Very-Early Strength Latex-Modified Concrete ; VES-LMC)는 작업성, 강도발현 및 장기 내구성 측면에서 콘크리트 타설 후 3시간 이내에 교통개방을 가능하게 할 목적으로 개발되었고, 교량바닥판 긴급보수 공사에 유용하게 사용되고 있다. 그러나 초속경 LMC에서 라텍스의 사용이 콘크리트의 내구성은 향상시키지만 다량의 갇힌 공기를 양산한다는 단점이 있다. 따라서 취약한 공극구조를 개선하기 위해서는 특별한 방법이 필요하며, 본 논문에서는 울트라파인 플라이 애시가 사용되었다. UFFA VES-LMC의 공기량은 재령 1일에 포졸란 반응의 대부분이 발생하여 재령 1일 공기량이 경화전 공기량보다 저하되었다. 또한 재령 28일 공기량은 재령 1일 공기량의 공극구조와 동일하게 나타나, 포졸란 반응에 의해 콘크리트의 전체 공기량이 감소함을 확인하였다. 수산화칼슘의 첨가는 200 ${\mu}m$이하 크기의 연행공기를 현저하게 증가시키고, UFFA를 15%이상 사용하면 간격계수를 200 ${\mu}m$ 이하까지 확보할 수 있어 VES-LMC의 공극구조 개선에 매우 효과적인 것으로 나타났다.

• 한국산학기술학회논문지
• /
• 제11권3호
• /
• pp.1040-1046
• /
• 2010

급속경화 콘크리트의 가장 큰 단점은 단시간 내에 발생하는 급격한 수화발열 반응으로 인해 초기팽창이나 수축이 매우 크게 일어나 균열이 발생할 가능성이 높다는 것이다. 그러나 플라이 애시가 사용되면 콘크리트의 수화열을 낮출 수 있으므로 초기팽창과 수축을 현저히 줄일 수 있어 균열발생 억제에 효과적일 수 있다. 초속경 라텍스개질 콘크리트(VES-LMC)는 우수한 재료특성에도 불구하고, 재료 자체의 높은 수화열로 인해 균열이 발생하는 사례가 보고되고 있다. 따라서 본 논문에서는 플라이 애시를 VES-LMC에 적용할 수 있는 방법을 고안하여, 균열에 대한 안정성을 확보하기 위한 연구를 수행하였다. 울트라파인 플라이 애시(Ultra-Fine Fly Ash ; UFFA)를 사용하여 조기강도 저하의 단점이 극복된 조건에서, 초기 수화열을 낮추고 수축을 저감하여 균열안정성을 확보할 수 있도록 하였다. 실험결과 조기 압축강도는 UFFA 혼입률이 증가함에 따라 다소 감소하지만, 재령 28일 강도는 통계학적으로 유사한 것으로 나타났다. 초기수축 실험결과 UFFA가 단위시멘트량대비 15%에서 20%까지 치환되면 최대수축을 43~47%까지 줄일 수 있어 초기수축 억제에 매우 효과적이므로 균열에 대한 안정성을 확보할 수 있는 것으로 나타났다.