• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.34 no.1
• /
• pp.22-29
• /
• 2002

The coated paper was greatly affected by the basic physical properties of the binder as well as the amount of the coating formula. High glass transition temperature (Tg) of the styrene-butadiene (SB) latex, selected as the binder in our study, gave the high stiffness to the coated paper, but lowered the binding force and print gloss. The average particle size of the SB latex also greatly affected to the coated paper so that the smaller particle size improved the rheological property of the coating formula and increased the binding force and print gloss. Another property of the SBR latex, gel content, was important because when its value was small, the latex was easily deformed at the high temperature and increased air permeability to the coated paper. Therefore, the lower gel content consequently resulted in the higher blistering resistance, especially in the web paper. The larger portion of the SB latex in the coated formula improved the binding force and print gloss, but decreased the ink set-off and ink-trapping to the coated paper. The heavier coating improved optical properties such as opacity, paper gloss and paper smoothness, to the coated paper.

• Journal of the Korea Concrete Institute
• /
• v.15 no.1
• /
• pp.95-101
• /
• 2003

Drying shrinkage cracking which may be caused by the relatively large specific surface is a matter of grave concern for latex modified concrete(LMC) overlay and rapid-setting cement latex modified concrete(RSLMC) overlay. LMC and RSLMC were studied for field applications very actively in terms of strength and durability in Korea. However, there were no considerations in drying shrinkage. Therefore, the purpose of this dissertation was to study the drying shrinkage properties of LMC and RSLMC with the main experimental variables such as cement types(ordinary portland cement, rapid setting cement), latex contents(0, 5, 10, 15, 20%) and curing days at a same controlled environment of 60% of relative humidity and $20^{\circ}C$ of temperature. The drying shrinkage for specimens was measured with a digital dial gauge of Demec. The test results showed that the drying shrinkage of LMC and RSLMC were considerably lower than that of OPC and RSC, respectively. This might be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic, and colloidal properties of the latexes resulting in reduced water evaporation.

• Journal of the Korea Concrete Institute
• /
• v.17 no.5 s.89
• /
• pp.695-702
• /
• 2005

It is known that latex-modified concretes were increased their durability and permeability by added latex. The purpose of this study was to analysis the air void systems in latex-modified concretes using a reasonable and objective image analysis method with main experimental variables such as water-cement ratios, latex contents(0%, 15%) and cement types(ordinary portland cement, high-early strength cement and very-early strength cement). The results are analyzed spacing factor, air volume after hardened, air distribution and structure. Also, air void systems and permeability of latex-modified concretes were compared with correlation. The results are as follows; The same w/c ratio LMC showed better air entraining effect than OPC with AE water reducer. The VES-LMC showed that the number of entrained air below $100{\mu}m$ increased more than four times. In the HES-LMC, micro entraining air having range from 50 to $500{\mu}m$ increased above 7 times without antifoamer. Though spacing factor was measured low, latex-modified concretes were showed that permeability was good. It is considered that air void system does not have an effect on the property of latex-modified concretes but latex film is more influenced in the their durability.