• Korean Journal of Metals and Materials
• /
• v.46 no.8
• /
• pp.495-505
• /
• 2008

With the high proportion of zinc coated steels in body-in-white assembly, newly developed surface roughness textured galvannealed steel sheets have been introduced. In this study, zinc coated and surface roughness textured steel sheets were welded by resistance spot welding to investigate its weldability including electrode wear test. Based on the results of tensile-shear test, nugget diameter changes, and electrode tip growth test, it was clear that both surface roughness textured steels (GA-T and GA-E) showed good weldability. Also, there was no large difference in weldability and electrode wear behavior between GA-T and GA-E steels which have different surface roughness morphology. An analysis of electrode degradation showed Fe and Zn penetration through the electrode tip surface at 2400 welds reached $55{\sim}60{\mu}m$ and $75{\sim}80{\mu}m$, respectively. Therefore, there is no significant effect of surface roughness morphology on spot weldability of surface roughness textured galvannealed steel sheets. However, slight difference in thickness of alloying layers existing on electrode tip was found between GA-T and GA-E steels.

• Korean Journal of Metals and Materials
• /
• v.47 no.12
• /
• pp.834-841
• /
• 2009

A study on the welding of electrogalvanized TRIP (Transformation-Induced Plasticity) steels was done to compare the life of the electrode and the alloying phenomena on the electrode tip surface using singlephase AC and inverter-DC resistance welding processes. A longer life of the electrode (>200 welds) was achieved using the inverter-DC welding process. The tensile shear strength was higher in the electrode life test when welded with the inverter DC welding machine it maintained a higher value even when the welding nugget diameter was smaller than specified. When spot-welding was conducted using the single-phase AC welding process, a higher wear rate of the electrode was observed compared to that with the inverter-DC process. An alloying layer used to determine the rate of electrode growth showed differences in the metallurgical features of the surface alloying and Zn penetration depending on whether the single-phase AC process or the inverter-DC welding process was used. Moreover, changes in the dynamic resistance during the electrode life test were correlated with the electrode wear (or growth) rate.

• Transactions of Materials Processing
• /
• v.31 no.1
• /
• pp.17-22
• /
• 2022

Hot stamping is widely used to manufacture structural parts to satisfy requirements of eco-friendly vehicles. Recently, hot forming technology using uncoated steel sheet is being studied to reduce cost and solve patent problems. In particular, research is focused on process technology capable of suppressing the generation of an oxide layer. To evaluate the oxide layer in the hot stamping process, Gleeble testing machine can be used to evaluate the oxide layer by controlling the temperature history and the atmosphere condition. At this time, since cooling by gas injection is impossible to protect the oxide layer on the surface of a specimen, research on a method for securing a quenching speed through natural cooling is required. This paper proposes a specimen shape design method to secure a target quenching speed through natural cooling when evaluating the oxide layer of an un-coated boron steel sheet by Gleeble test. For the evaluation of the oxide layer of the un-coated steel sheet through the Gleeble test, dog-bone and rectangular type specimens were used. In consideration of the hot stamping process, the temperature control conditions for the Gleeble test were set and the quenching speed according to the specimen shape design was measured. Finally, the quenching speed sensitivity according to shape parameter was analyzed through regression analysis. A quenching speed prediction equation was then constructed according to the shape of the specimen. The constructed quenching speed prediction equation can be used as a specimen design guideline to secure a target quenching speed when evaluating the oxide layer of an un-coated boron steel sheet by the Gleeble test.

• Journal of the Korean institute of surface engineering
• /
• v.56 no.1
• /
• pp.69-76
• /
• 2023

The effects of hairline treatment on surface blackening and thermal diffusion behaviors of Zn-Al-Mg alloy coated steel sheet were evaluated by the three-dimensional surface profiler and laser-flash technique. The metallographic observation of coating damages by hairline treatments showed that several cracks were initiated and propagated along the interface between primary Zn/eutectic phases. As the hairline processing became more severe, the crack occurrence frequency in eutectic phase of coating layer and the surface roughness increased, which had a proportional relationship with the level of blackening on the coating surface. In addition, the higher interfacial areas of the blackened coating surface, caused by the hairline process, led to an increase in thermal diffusivity and conductivity of the coated steel sheet. On the other hand, when the coating damage by hairline treatment was excessive and the steel substrate was exposed, there was little difference between the thermal diffusivity/conductivity of the untreated sample though the blackening degree was higher than that of untreated sample. This work suggests that the increase in the surface areas of the coating layer without exposure to steel substrate through hairline treatment can be one of the effective technical strategies for the development of Zn-Al-Mg alloy coated steel sheets with higher blackening level and thermal diffusivity.

• Corrosion Science and Technology
• /
• v.22 no.2
• /
• pp.123-130
• /
• 2023

This study aimed to evaluate corrosion resistance of steel coated with GI and Zn-Al-Mg alloy using cyclic corrosion test (CCT) with electrochemical polarization and impedance measurements. Results showed that the Zn-Al-Mg alloy coated steel had a much higher corrosion rate than GI coated steel in early stages of corrosion. With prolonged immersion, however, the corrosion rate of the Zn-Al-Mg alloy coated steel greatly decreased, mainly owing to a significant decrease in the cathodic reduction reaction and an increase in polarization resistance at the surface. This was closely associated with the formation of protective corrosion products including Zn₅(OH)₈Cl₂·H₂O and Zn₆Al₂(OH)₁₆CO₃. Moreover, when the steel substrate was locally exposed due to mechanical damage, the kinetics of anodic dissolution from the coating layer and the formation of protective corrosion products on the surface of the Zn-Al-Mg alloy coated steel became much faster compared to the case of GI coated steel. This could provide a longer-lasting corrosion inhibition function for Zn-Al-Mg alloy coated steel used in plant farms.

• Journal of the Korean Society for Heat Treatment
• /
• v.37 no.1
• /
• pp.16-22
• /
• 2024

The conventional degreasing process involves removing oil and contaminants at temperatures above 80℃, resulting in excessive energy consumption, increased process costs, and environmental issues. In this study, we aimed to find the optimal degreasing conditions for the pre-treatment process of electro-galvanizing cold-rolled steel sheets, conducted efficiently at room temperature without the need for a separate heating device. To achieve this, we developed a room temperature degreasing solution and a brush-type degreasing tool, aiming to reduce energy consumption and normalize the decrease in degreasing efficiency caused by temperature reduction. Alkaline degreasing solution were prepared using KOH, SiO₂, NaOH, Na₂CO₃, and Sodium Lauryl Sulfate, with KOH and NaOH as the main components. To enhance the degreasing performance at room temperature, we manufactured additives including sodium oleate, sodium stearate, sodium palmitate, sodium lauryl sulfate, ammonium lauryl sulfate, silicone emulsion, and EDTA-Na. Room temperature additives were added to the alkaline degreasing solution in quantities ranging from 0.1 to 20 wt.%, and the uniformity of degreasing and the adhesion of the galvanized layer were evaluated through Dyne Test, T-bending Test, OM, SEM, and EDS analyses. The results indicated that the optimal degreasing solution composition consisted of NaOH (30 g/L), Na₂CO₃ (30 g/L), SLS (6 g/L), and room temperature additives (≤1 wt%).

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.95-95
• /
• 2018

강재의 방식법 중 도장은 부식을 억제하는데 효과적이고 편리한 방법으로 선박 및 해양 강 구조물의 방식법으로 사용되고 있다. 한편, 강 구조물의 효율적인 유지관리를 위해서는 방식 도장의 도막 열화도를 평가하고 잔존 수명을 예측하여 최적 시기에 보수도장 혹은 재도장하는 것이 필요하다. 일반적으로 선박 및 해양구조물에 적용되는 도막의 방식 성능 평가 방법으로 해수 침지 시험, 염수 분무 시험, 옥외 폭로 시험 등이 있다. 그러나 이러한 시험들은 그 시험 방법에 따라서 정량적인 평가에 한계가 있음은 물론 장기간 소요되는 등 곤란한 문제점이 있다. 그러므로 선박 및 해양구조물을 비롯하여 교량, 각종 강 구조물의 도장 방식에 사용되는 방식용 도료의 성능을 단기간에 적절하게 평가할 수 있는 가속시험법이 제시되며 연구-사용되고 있다. 그 중 도막 방식 성능을 보다 효율적, 비파괴적, 정량적으로 평가할 수 있는 임피던스 분광법(EIS)과 같은 전기화학적 방법은 상대적으로 시험 기간을 크게 단축시킬 수 있고, 대상 방식 도장의 미세한 성능 차이도 분별 가능하다는 장점이 있다[1]. 따라서 본 연구에서는 선박 및 해양구조물 등 가혹한 부식환경에서 강력한 내구성을 가질 수 있도록 다양한 종류의 표면처리 도장 시편을 제작하여 자외선 조사-염수분무-침지환경 등의 열악한 환경조건 하에서 부식-열화 촉진 시험을 실시하였다. 그리고 그 촉진 열화 과정에서 도막의 외관 상태를 관찰 분석함은 물론 전기화학적 임피던스 분광법을 병행 측정하며 그 표면막의 부식 및 도막 열화도를 비교-종합 평가하였다.본 연구에 사용된 시편은 Al 및 Zn 도금 강판에 에폭시, 에폭시-실리콘 우레탄, 에폭시-우레탄 도장 시편으로 Scribe, No Scribe 및 비교재 Al 및 Zn 도금 시편으로 분류하여 각각 실험을 진행하였다. 즉, 도막 열화 시험은 복합 노화 시험법으로 UV 조사 36 시간(ASTM G53), 염수분무 32 시간(ISO 7253), 수분 응축 10 시간을 1 Cycle로 100 Cycle(7800 시간) 동안 실험을 진행하였다. 이때 도막 열화도 평가는 전기화학적 임피던스 분광법을 이용하여 각 실험 조건별로 주파수에 따른 임피던스(Z) 값을 평가하였다. 즉, 상온 $25^{\circ}C$의 3.5% NaCl 100 ml 수용액에 작동 전극(Working Electrode)과 구리 도선을 통해 연결하였고, 노출 면적은 $1cm^2$로 일정하게 유지 하였으며, 상대 전극(Counter Electrode)은 탄소봉, 기준 전극(Reference Electrode)으로 포화카로멜전극(Saturated Calomel Electrode)을 사용하여 측정하였다. No Scribe 시편의 경우에는 Al 기판 에폭시-실리콘 우레탄 도장 시편이 우수한 도막 저항성을 나타내었으며, 에폭시-우레탄 도장시편은 23사이클 이후의 저항값이 가장 낮게 나타났다. Zn 기판의 경우는 에폭시, 에폭시-실리콘 우레탄, 에폭시-우레탄 도장 시편 모두 저항 값이 유사하였으며, Al 및 Zn 도금 시편은 도장 처리된 시편에 비해 훨씬 낮은 저항 값을 보였다. 또한 Scribe 시편의 경우에는 Al 기판 에폭시-실리콘 우레탄 도장 시편에서 높은 초기 저항 값을 보였으며, 23 사이클 후의 저항 값은 세 종류의 도막에서 약 1~0.1 Gohm 으로 나타났다. 그리고 Zn 기판 에폭시-실리콘 우레탄 도장 시편에서 가장 낮은 도막 저항 값이 나타났다. 이상의 실험을 통해서 본 연구 내용은 실내촉진시험으로 선박 및 해양 강 구조물에 사용되는 다양한 종류의 도막의 열화도를 평가하는 기초 설계 지침으로 응용될 수 있을 것으로 사료된다. 한편, 도막은 노출 환경에 따라 방식 성능이 다르므로 실제 도막의 사용환경을 고려하여 도장 사양별 적용 부위에 따른 적정 가속 실험 방법을 선정할 필요가 있다고 사료된다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.10
• /
• pp.1367-1375
• /
• 2010

In this study, optimization of the process parameters of the resistance spot welding of a sheet of aluminum-coated boron alloyed steel, 22MnB5, used in hot stamping has been performed by a Taguchi method to increase the strength of the weld joint. The process parameters selected were current, electrode force, and weld time. The heating temperature and heating time of 22MnB5 are considered to be noise factors. It was known that the variation in the thickness of the intermetallic compound layer between the aluminum-coated layer and the substrate, which influences on the formation of nugget, was generated due to the difference of diffusion reaction according to heating conditions. From the results of spot weld experiment, the optimum weld condition was determined to be when the current, electrode force, and weld time were 8kA, 4kN, and 18 cycles, respectively. The result of a test performed to verify the optimized weld condition showed that the tensile strength of the weld joint was over 32kN, which is considerably higher than the required strength, i.e., 23kN.