• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.4
• /
• pp.182-189
• /
• 2021

Porous ceramics were manufactured using the foaming method for the development of inorganic insulating materials. Silica fume and SiO₂ were used as main raw materials, and bentonite was used as a rapid setting agent for uniform structure formation of porous ceramics. The porous ceramics were sintered at 1200℃, and porosity, density, compressive strength, microstructure and thermal conductivity were analyzed. As the content of silica fume to SiO₂ of the porous ceramics increased 70 to 90 %, the specific gravity increased from 0.63 to 0.69, and the compressive strength increased from 9.41 Mpa to 12.86 Mpa. But, the porosity showed a tendency to decrease from 72.07 % to 70.82 %, contrary to the specific gravity. As a result of measuring the thermal conductivity, the porous ceramic with a silica fume content of 70 % showed a thermal conductivity of 0.75 to 0.72 W/m·K at 25 to 800℃, respectively, and, another that a silica fume content of 90 % showed a 0.66~0.86 W/m·K. So the lower the silica f ume content, the lower the thermal conductivity, which was conf irmed to be consistent with porosity result. As a result of microstructure analysis using SEM (Scanning Electron Microscope), pores in the range of tens to hundreds ㎛ were observed inside and outside the porous ceramic, and it was confirmed that the pore distribution was relatively uniform.

• Journal of Bio-Environment Control
• /
• v.18 no.4
• /
• pp.332-340
• /
• 2009

In this study, the thermal insulation effectiveness of the greenhouse insulators by the installation methods was investigated to find the right installation way of the insulation materials. Physical properties of the insulators such as thickness, air transmissivity, apparent density, ultraviolet rays cutoff ratio, reflectance, thermal conductivity, moisture absorptivity were evaluated and the insulation ability of the insulators were measured by the module experiments. For the same insulator, the insulation ability of the case with the outward direction of the black colored face, i.e., with the inward direction of the white colored face, was better than that of vice versa. The case of the black colored both surfaces was better than the case of the white colored both surfaces. For aluminium reflection material, the case with the outward direction of the lustre face, i.e., with the inward direction of the non-lustre face, was better than that of vice versa. For the same material with the inner thin polyethylene foam (or polyester) and the chemical wool, the case with the outward direction of the inner thin polyethylene foam (or polyester), i.e., with the inward chemical wool, was better than that of vice versa. Addition of the inner thin polyethylene foam increased the insulation effect very much.