• Journal of the Korean Orthopaedic Association
• /
• v.54 no.5
• /
• pp.435-439
• /
• 2019

Purpose: This study evaluated the efficacy of blood mixed cement for osteoporotic vertebral compression fractures in reducing the complications of percutaneous vertebroplasty using conventional cement. Materials and Methods: This study was performed retrospectively in 80 patients, from January 2016 to January 2017. Porous cement was formed by mixing 2, 4, and 6 ml of blood with 20 g of cement used previously. A tube with a diameter and length of 2.8 mm and 215 mm, respectively, was used and the polymerization temperature, setting time, and optimal passing-time were measured and compared with those using only conventional cement. Radiologically, the results were evaluated and compared. Results: The polymerization temperature was 70.3℃, 55.3℃, 52.7℃, and 45.5℃ in the conventional cement (R), 2 ml (B2), 4 ml (B4), and 6 ml (B6), respectively, and the corresponding setting time decreased from 960 seconds (R) to 558 seconds (B2), 533 seconds (B4), and 500 seconds (B6). The optimal passing-time was 45 seconds (B2), 60 seconds (B4), and 78 seconds (B6) at 73 seconds (R), respectively and as the amount of blood increased, it was similar to the cement passing-time. The radiological results showed that the height restoration rates and the vertebral subsidence rates similar among the groups. Two cases of adjacent vertebral compression fractures in the R group and one in the B2 and B4 groups were encountered, and the leakage rate of the cement was approximately two times higher than that in the conventional cement group. Conclusion: In conventional percutaneous vertebroplasty, the procedure of using autologous blood with cement decreased the polymerization temperature, reduced the setting time, and the incidence of cement leakage was low. These properties may contribute to more favorable mechanical properties that can reduce the complications compared to conventional cements alone.

• Economic and Environmental Geology
• /
• v.56 no.6
• /
• pp.899-909
• /
• 2023

In this study, the material scientific characteristics of Hobun pigments used as white inorganic pigment for traditional cultural heritage were identified according to the type of shell and calcination and evaluated the stability of the preservation environment. For the purpose of this, we collected 2 different types of Hobun pigments made by oyster and clam shell and its calcined products(at 1,150℃). Hobun pigments before calcined identified calcium carbonate such as calcite, aragonite but calcination derived changing main composition to portlandite and calcite. Results of FE-SEM showed characteristics microstructure for each shell but pigments after calcined observed porous structure. Porous granule highly caused oil adsorption according to increase specific surface area of pigments. In addition, the whiteness improved after calcined pigments compared to non-calcined pigments, and the color improvement rate of Hobun pigment (CS) which made of clam shell was higher. As a result of the accelerated weathering test, the Hobun pigment-colored specimen had a color difference value of less than 2 after the test, which was difficult to recognize with the naked eye. In particular, the color stability has improved as the color difference value of the Hobun pigment is smaller after calcined compared to before non-calcined pigment. However, it was confirmed that the stability of the painting layer was lower in the specimen after calcined pigment. For antifungal activity test, Aspergillus niger, Tyromyces palustris and Trametes versicolor were used as test fungi, and all pigments were found to have preventive and protective effects against fungi. Especially, the antifungal effect of the calcined pigment was excellent, which is due to the stronger basicity of the pigment.