• Proceedings of the KWS Conference
• /
• 2001.10a
• /
• pp.149-152
• /
• 2001

• Journal of the Korean Society of Propulsion Engineers
• /
• v.7 no.4
• /
• pp.73-79
• /
• 2003

The tensile strength test and the analysis for the section of brazing were performed in the cases of materials used for combustion chamber of regeneratively cooled liquid rocket engine. BNi-2 and BNi-7 based on nickel were used for brazing as filler metal. The properties of material and filler metal were analyzed by tensile strength test and metal microscope for 12 specimens. The tensile-strength of brazing for chrome-copper alloy and other kinds of alloy was higher than that of chrome-zirconium-copper alloy and other kinds of alloy The tensile strength in the case of BNi-2 as filler metal was higher than that of BNi-7 because the wetting property of BNi-2 was better than that of BNi-7.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.12
• /
• pp.1573-1579
• /
• 2013

To test the performance of nuclear fuels, coolant needs to be circulated through the test rig installed in the test loop. Because the pressure and temperature of the coolant is 15.5 MPa and $300^{\circ}C$ respectively, coolant sealing is one of the most important processes in fabricating a nuclear fuel test rig. In particular, 15 instrumentation cables installed in a test rig pass through the pressure boundary, and brazing is generally applied as a sealing method. In this study, an induction brazing system has been developed using a high frequency induction heater including a vacuum chamber. For application in the nuclear field, BNi2 should be used as a paste, and optimal process variables for Ni brazing have been found by several case studies. The performance and soundness of the brazed components has been verified by a tensile test, cross section test, and sealing performance test.

• Journal of Advanced Marine Engineering and Technology
• /
• v.19 no.3
• /
• pp.50-61
• /
• 1995

In recent years, many ceramic researchers have discoved various methods of joining ceramic to metal. However, most of these joining methods are perfomed under vacuum and pressured circumstances. So, when we join ceramic to metal,the proceedings are very complicated and require a very high cost. The purpose of this study is to develop a new joining method of an alumina ceramic to an aluminum metal in air atmosphere. The joining condition, such as copper metallizing, nickel plating, brazing, etc. was investigated through the shear strength test of the trial joint. The results obtained from the above experimenta are summarized as follows : 1) In the case of the $Al_2O_3$/$Al_2O_3$joint, the shear strength of the joint was affected by the various foctor such as kaolin content, copper metallizing thickness, firing temperature, firing time. 2) The better shear strength of the $Al_2O_3$/Al joint was obtained when Ni plating was conducted under higher current density than existing plating condition. 3) The shear strength of the $Al_2O_3$/Al joint increases with the Ni plating thickness is confined to the range of this paper. 4) The shear strength of the thermal-shocked specimen($Al_2O_3$/Al joint) was far more deteriorated than that of the as-bonded specimen.

• Transactions of Materials Processing
• /
• v.7 no.5
• /
• pp.465-473
• /
• 1998

The effect of alloying elements of Ag-Cu-Zr-X brazing alloy on the microstructure and the bond strength of $Al_2O_3/Ni-Cr$ brazed steel joint was investigated. The reaction layer, $ZrO_2$ (a=5.146 ${\AA}$ , b=5.213 ${\AA}$ , c=5.311 ${\AA}$ )was formed at the interface of $Al_2O_3/Ni-Cr$ steel joint by the redox reaction between alumina and Zr. The addition of An and Al to the Ag-Cu-Zr brazing alloy gave rise to changes in the thickness of the reaction product layer and the morphology of the brazement. Sn caused the segregation of Zr was decreased b Al the $ZrO_2$ layer formed at the Ag-Cu-Zr-Al alloy was thinner than that of $ZrO_2$ formed at the Ag-Cu-Zr-An alloy. The fracture shear strength was strongly dependent on the microstructure of the brazement. Brazing with Ag-Cu-Zr-Sn alloy resulted in a better bond strength than with Ag-Cu-Zr or Ag-Cu-Zr-Al alloy.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.266-268
• /
• 2006

The effects of the brazing temperature and homogenizing time for brazed specimens on the joint of Ni-based superalloys such as Haynes 250, Inconel 617 and Hastelloy-X were investigated. The brazing alloy is nickel base MBF 15. The foil had a thickness of $38{\mu}m$, which was used two sheets of that for the all experiments. The experimental brazing was carried out by a brazing process in a vacuum of approximately $2{\times}10^{-5}$ Torr, an applied pressure of about 0.74MPa and the three kinds of brazing temperatures were 1100, 1150, and $1190^{\circ}C$ for a holding time of 5 to 1440 minutes. Microstructural observations were made on the cross-sectional samples by using an optical microscope(OM), scanning electron microscope(SEM), and electron probe X-ray microanalyzer(EPMA). The tensile tests were performed at room temperature with a cross head speed 1.5 mm/min according to ASTM E8M. The results show that excellent joint tensile strengths of as high as 788MPa were obtained when processed at $1190^{\circ}C$ for 5 minutes.